Polymeric compositions from acrylic and unsaturated carboxyl monomers
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C08F-002/16
출원번호
US-0610686
(2000-07-07)
발명자
/ 주소
Robert V. Slone
출원인 / 주소
Rohm and Haas Company
대리인 / 주소
Ronald D. Bakule
인용정보
피인용 횟수 :
13인용 특허 :
6
초록▼
An aqueous composition suitable for use, when dry, as an improved elastomeric coating, caulk, sealant, or pressure sensitive adhesive is provided including a predominantly acrylic aqueous emulsion polymer, the polymer having a glass transition temperature (Tg) from -90.degree. C. to 20.degree. C., f
An aqueous composition suitable for use, when dry, as an improved elastomeric coating, caulk, sealant, or pressure sensitive adhesive is provided including a predominantly acrylic aqueous emulsion polymer, the polymer having a glass transition temperature (Tg) from -90.degree. C. to 20.degree. C., formed by the free radical polymerization of at least one ethylenically unsaturated nonionic acrylic monomer and 0.5-5%, by weight based on the total weight of said polymer, ethylenically unsaturated carboxylic acid monomer until 90-99.7% of said monomers by weight, based on the total weight of said polymer, has been converted to polymer and subsequently at least half of the remaining monomer is converted to polymer in the presence of 0.1-1.0 wt %, by weight based on the total weight of said polymer, t-amyl hydroperoxide. A method for preparing the emulsion polymer, a method for coating a substrate to provide an elastomeric coating on a substrate, a method for applying an aqueous caulk or sealant composition to a substrate, and a method for providing a pressure sensitive adhesive on a substrate are also provided.
대표청구항▼
1. An aqueous composition suitable for use when dry as an improved elastomeric coating, caulk, sealant or pressure sensitive adhesive comprising a predominantly acrylic aqueous emulsion polymer, said polymer having a glass transition temperature (Tg) from -90.degree. C. to 20.degree. C., formed by t
1. An aqueous composition suitable for use when dry as an improved elastomeric coating, caulk, sealant or pressure sensitive adhesive comprising a predominantly acrylic aqueous emulsion polymer, said polymer having a glass transition temperature (Tg) from -90.degree. C. to 20.degree. C., formed by the free radical polymerization of at least one ethylenically unsaturated nonionic acrylic monomer and 0.5-5%, by weight based on the total weight of said polymer, ethylenically unsaturated carboxylic acid monomer until 90-99.7% of said monomers by weight, based on the total weight of said polymer, has been converted to polymer and subsequently at least half of the remaining monomer is converted to polymer in the presence of 0.1-1.0 wt %, by weight based on the total weight of said polymer, t-amyl hydroperoxide.
Mudge Paul R. (Belle Mead NJ) Walker James L. (Whitehouse Station NJ) Pangrazi Ronald (Flemington NJ), Emulsion binders containing low residual formaldehyde and having improved tensile strength.
Demarest, Victoria Anne; Evans, Ann Elizabeth; Freeman, Adam Wade; Liss, Audrey Brenda, Plasticizer free caulks and sealants having improved aged wet adhesion.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.