The active brazing solder for brazing ceramic parts of alumina, particularly of high-purity alumina, contains a maximum of 12 wt. % Ti, a maximum of 8 wt. % Be, and less than 16.5 wt. % Fe, the remainder being Zr and any impurities that may be present. The active brazing solder has the following beh

The active brazing solder for brazing ceramic parts of alumina, particularly of high-purity alumina, contains a maximum of 12 wt. % Ti, a maximum of 8 wt. % Be, and less than 16.5 wt. % Fe, the remainder being Zr and any impurities that may be present. The active brazing solder has the following behaviour/features: Brazing temperature: lower than 1,000.degree. C.; the brazed joint is high-vacuum-tight over a long period of time; the coefficient of thermal expansion of the active brazing alloy is substantially identical to that of the alumina ceramic in the entire temperature range covered during the brazing process; the strength of the brazed joint between the two ceramic parts is so high that under tensile loading, fracture will result not at the joint, but in the adjacent ceramic; the pressure resistance of the active brazing solder is greater than 2 GPa; the active brazing solder is very good processable into powders having particle sizes on the order of 10 .mu.m.

대표청구항 ▼

1. A method of forming a brazed joint between a first alumina-ceramic part and a second alumina-ceramic part, comprising the steps of:applying to a joint formed by said first alumina-ceramic part and said second alumina-ceramic part an active brazing solder consisting essentially of 8.6 wt. % to 12

1. A method of forming a brazed joint between a first alumina-ceramic part and a second alumina-ceramic part, comprising the steps of:applying to a joint formed by said first alumina-ceramic part and said second alumina-ceramic part an active brazing solder consisting essentially of 8.6 wt. % to 12 wt. % titanium, 1 wt. % to 8 wt. % beryllium, 0 wt. % to 16.5 wt. % iron, 63.5 wt. % to 90.4 wt. % zirconium, and a remainder being any impurities; heating said active brazing solder applied to said joint to a brazing temperature in order to melt said active brazing solder and wet said first alumina-ceramic part and said second alumina-ceramic part with said active brazing solder; and cooling said active brazing solder after said heating step to an ambient temperature to form said brazed joint between said first alumina-ceramic part and said second alumina-ceramic part.