초록 ▼

A phase of aluminum trihydroxide and supports and catalysts made therefrom. This invention also relates to methods of producing this phase of aluminum trihydroxide and catalysts made therefrom, and to a method for improving the activity of and for regenerating catalysts having a silica-alumina suppo

A phase of aluminum trihydroxide and supports and catalysts made therefrom. This invention also relates to methods of producing this phase of aluminum trihydroxide and catalysts made therefrom, and to a method for improving the activity of and for regenerating catalysts having a silica-alumina support.

대표청구항 ▼

1. A composition comprising an aluminum trihydroxide phase having measurable X-ray diffraction peaks between about 2θ=18.15° and about 2θ=18.50°, between about 2θ=36.1° and about 2θ=36.85°, between about 2θ=39.45° and about 2θ=40.30°, and between about 2θ=51.48° and about 2θ=52.59°. 2. The compositi

1. A composition comprising an aluminum trihydroxide phase having measurable X-ray diffraction peaks between about 2θ=18.15° and about 2θ=18.50°, between about 2θ=36.1° and about 2θ=36.85°, between about 2θ=39.45° and about 2θ=40.30°, and between about 2θ=51.48° and about 2θ=52.59°. 2. The composition of claim 1 further characterized in that the aluminum trihydroxide phase has measurable X-ray diffraction peaks between about 2θ=27.35° and about 2θ=27.90°, between about 2θ=34.75° and about 2θ=35.48°, and between about 2θ=62.40° and about 2θ=63.80°. 3. The composition of claim 1 further characterized in that the aluminum trihydroxide phase does not have measurable X-ray diffraction peaks between about 2θ=20.15° and about 2θ=20.65°. 4. The composition of claim 1 further characterized in that the aluminum trihydroxide phase does not have measurable X-ray diffraction peaks between about 2θ=20.15° and about 2θ=20.65° and between about 2θ=37.35° and about 2θ=37.75°. 5. The composition of claim 1 further characterized in that the aluminum trihydroxide phase does not have measurable X-ray diffraction peaks between about 2θ=18.70° and about 2θ=18.90°, between about 2θ=20.30° and about 2θ=20.50°, and between about 2θ=40.30° and about 2θ=40.70°. 6. The composition of claim 1 further characterized in that the aluminum trihydroxide phase has measurable X-ray diffraction peaks between about 2θ=27.35° and about 2θ=27.90°, between about 2θ=34.75° and about 2θ=35.48°, and between about 2θ=62.40° and about 2θ=63.80°; and does not have measurable peaks between about 2θ=18.70° and about 2θ=18.90°, between about 2θ=20.15° and about 2θ=20.65°, between about 2θ=37.35° and about and between about 2θ=40.30° and about 2θ=40.70°. 7. A process for making a composition comprising an aluminum trihydroxide phase having measurable X-ray diffraction peaks between about 2θ=18.15° and about 2θ=18.50°, between about 2θ=36.1° and about 2θ=36.85°, between about 2θ=39.45° and about 2θ=40.30°, and between about 2θ=51.48° and about 2θ=52.59°, comprising: (a) wetting a starting material comprising silica coated amorphous alumina comprising between about 4 wt. % and about 8 wt. % silica, wherein at least about 20 wt. % of said alumina is amorphous, by contact with a chelating agent in a carrier liquid and a metallic compound; (b) aging the so-wetted starting material while wet; (c) drying the so-aged starting material at a temperature between about 100° C. and about 230° C. and under conditions to substantially volatilize the carrier liquid; and (d) calcining the so-dried material.