초록 ▼

A novel clay pigment, the manufacture thereof and the use of the pigment in the coating of lightweight groundwood paper are disclosed. The kaolin clay particles initially have a shape factor between less than 10 and a particle size distribution where between 30 to 60% by weight is less than 2 micron

A novel clay pigment, the manufacture thereof and the use of the pigment in the coating of lightweight groundwood paper are disclosed. The kaolin clay particles initially have a shape factor between less than 10 and a particle size distribution where between 30 to 60% by weight is less than 2 microns and 20% by weight is less than 0.25 micron e.s.d. This clay is subjected to attrition grinding to produce clay particles having a shape factor between 13 and 18 and then classified to produce a particle size distribution where 80 to 90% by weight are less than 2 microns and 20% by weight are less than 0.25 micron. These pigments have a G.E. brightness ranging from 88 to 92; are deficient in ultra-fine particles; are fluid at a high solids concentration greater than 70%, and have a low shear Brookfield viscosity below 500 cps and a high shear Hercules viscosity of 18 dyne-cm above 200 rpm when using an "A" bob.

대표청구항 ▼

1. A method of providing a high brightness kaolin pigment product, comprising: (a) selecting a base kaolin clay crude to be processed, the selected base kaolin clay being hydrated kaolin clay having a particle size distribution wherein from about 30 to about 60% by weight of the particles have a

1. A method of providing a high brightness kaolin pigment product, comprising: (a) selecting a base kaolin clay crude to be processed, the selected base kaolin clay being hydrated kaolin clay having a particle size distribution wherein from about 30 to about 60% by weight of the particles have a particle size less than 2 microns and about 20% by weight is less than 0.25 micron; (b) forming an aqueous kaolin suspension of said kaolin clay crude; (c) subjecting said aqueous kaolin suspension of said clay crude to a grinding step where the kaolin particles are ground to a shape factor ranging from about 10 to about 30; and (d) classifying said ground particles to a particle size distribution characterized in that about 80% to about 90% by weight of the particles are less than 2 microns, and about 20% by weight is less than 0.25 micron. 2. A method of claim 1 including grinding said particles of said kaolin of step (c) to a shape factor ranging from 13 to 18. 3. A method of claim 1 further including prior to the grinding and classifying said particles, subjecting said aqueous kaolin suspension to a magnetic separation process to remove a substantial, portion of iron impurities from said kaolin clay. 4. A method of claim 1 further including after classifying said ground particles of step (d), dewatering said aqueous kaolin to a solids level of about 70% by weight. 5. A method of claim 2 including subjecting said particles of step (d) to a defining process if more than 20% by weight of said particles is greater than 0.25 microns. 6. A method of making light weight coating applications for groundwood paper products comprising adding to said light weight coating applications for groundwood paper products, a high brightness kaolin pigment product made according to the method of claim 1. 7. A high brightness kaolin pigment product produced in accordance with claim 1, said pigment having a G.E. brightness ranging between 88 and 92. 8. A high brightness kaolin pigment product of claim 7, said pigment having a particle size distribution wherein less than 99% by weight of the kaolin particles have a particle size less than 2 microns and about less than 20% by weight of the kaolin particles have a particle size less than 0.25 micron. 9. A high brightness kaolin pigment product of claim 6 formed into an aqueous slurry having a solids level of about 70% by weight, a low shear Brookfield viscosity below 550 cps, and a high shear Hercules viscosity of about 18 dyne-cm at above 190 rpm, using an "A" bob. 10. A process for preparing a kaolin clay composition for use in lightweight coating applications for groundwood paper products, comprising: delaminating the kaolin clay crude; and controlling the degree of the delaminating process of the kaolin clay by measuring the shape factor of the kaolin clay. 11. A process of claim 10 wherein said measuring step is done simultaneously during the delaminating stop. 12. A process of claim 10 wherein the delaminating step is discontinued when the shape factor of the kaolin clay ranges from 13 to 18.