초록 ▼

A method whereby a composite clad metal ingot can be produced for onward processing at higher temperatures which are sufficient to allow the properties of the substrate material to be adequately controlled to meet specific requirements. These higher temperatures are required to avoid the undue level

A method whereby a composite clad metal ingot can be produced for onward processing at higher temperatures which are sufficient to allow the properties of the substrate material to be adequately controlled to meet specific requirements. These higher temperatures are required to avoid the undue levels of work hardening which occurs at the lower temperatures previously employed because of the need to avoid the formation of deleterious intermetallics at the bonded clad substrate interface. Such intermetallics are formed at temperatures above approximately 850° C. and should they be present, will weaken or destroy the bond. The ingot, consisting of a steel or stainless steel substrate which is clad with a corrosion resistant metal, preferably of titanium, zirconium or their alloys, and containing an interlayer of high melting point metal of tantalum, niobium (columbium) or their alloys, is processed at temperatures above 900° C. The tantalum or niobium interlayer prevents the formation of the deleterious brittle intermetallics which would otherwise be formed at these temperatures. Consequently, these higher temperatures can be used to control the steel properties by the conventional and prescribed methods of the art and without regard to the effects that they would otherwise have upon the bond.

대표청구항 ▼

1. A method of producing a composite material, including a layer of metal cladder material and a metal substrate material, wherein an interlayer of metal material is interposed between said metal cladder material and said metal substrate, which comprises bonding said metal interlayer material to sai

1. A method of producing a composite material, including a layer of metal cladder material and a metal substrate material, wherein an interlayer of metal material is interposed between said metal cladder material and said metal substrate, which comprises bonding said metal interlayer material to said metal cladder material and to said metal substrate material, and thereafter hot forming said composite material, said metal interlayer material being such that upon hot forming at a temperature above 900° C. to provide the said metal substrate material with required mechanical and metallurgical properties, the bonds between said metal cladder material and said metal interlayer material and between said metal substrate material and said interlayer material are not adversely affected and the formation of intermetallics and depletion of the bond between the metal substrate material and metal cladder material at such temperature are prevented. 2. A method as in claim 1 in which the metal interlayer material has a melting point higher than the metal cladder material and the metal substrate material. 3. A method as in the preceding claim 1 in which the metal interlayer material is explosively bonded to the layer of metal cladder material and to the metal substrate material. 4. A method as in the preceding claim 1 in which the metal substrate material is carbon or stainless steel and the metal cladder material is a corrosion resistant metal. 5. A method as in the preceding claim 1 in which the corrosion resistant metal cladder material is titanium or an alloy of titanium. 6. A method as in the preceding claim 1 in which the corrosion resistant metal cladder material is zirconium or an alloy of zirconium. 7. A method as in the preceding claim 1 in which the metal interlayer material is niobium, also known as columbium, or an alloy of niobium (colombium). 8. A method as in the preceding claim 1 in which the metal interlayer material is tantalum or an alloy of tantalum. 9. A method as in the preceding claim 1 in which the several layers of metal substrate, metal cladder and metal interlay materials are in substantially flat plate or sheet form to provide a composite flat ingot suitable for hot rolling into final sheet or plate form. 10. A method as in the preceding claim 1 in which the several layers of metal substrate, metal cladder and metal interlayer materials are of substantially cylindrical form to provide a composite cylindrical billet suitable for hot extrusion into tubular or pipe form.