초록 ▼

Glass is produced in a glassmelting furnace by combusting fuel and oxidant having an oxygen content greater than 80 vol. % oxygen in a melting zone to form molten glass, wherein the surface of the molten glass is exposed to the gaseous atmosphere in the melting zone and the water vapor content of th

Glass is produced in a glassmelting furnace by combusting fuel and oxidant having an oxygen content greater than 80 vol. % oxygen in a melting zone to form molten glass, wherein the surface of the molten glass is exposed to the gaseous atmosphere in the melting zone and the water vapor content of the atmosphere at the surface of the molten glass is greater than 35 vol. %, and oxidant having an oxygen content greater than 80 vol. % is injected into the refining zone of the furnace under conditions to minimize mixing of said oxidant with gases above said oxidant and sweep water vapor at the surface of the molten glass into the melting zone to lower the water vapor content of the atmosphere at the surface of the molten glass.

대표청구항 ▼

1. A method of producing glass, comprising providing a glassmelting furnace having a melting zone equipped with burners for combusting fuel and oxidant and an unfired refining zone, feeding glassmaking materials into the melting zone, feeding fuel and oxidant having an oxygen content greater tha

1. A method of producing glass, comprising providing a glassmelting furnace having a melting zone equipped with burners for combusting fuel and oxidant and an unfired refining zone, feeding glassmaking materials into the melting zone, feeding fuel and oxidant having an oxygen content greater than 80 vol. % oxygen to said burners and combusting said fuel and said oxidant in the melting zone to generate heat to melt the glassmaking materials in the melting zone to form molten glass, wherein the surface of the molten glass is exposed to the gaseous atmosphere in the melting zone and the water vapor content of the atmosphere at the surface of the molten glass in the melting zone is greater than 35 vol. %, passing the molten glass into said refining zone, cooling the molten glass in the refining zone without combusting fuel and oxidant in the refining zone, and injecting oxidant having an oxygen content greater than 80 vol. % into the refining zone at a sufficiently low velocity below 50 feet per second to minimize mixing of said oxidant with gases above said oxidant to displace water vapor at the surface of the molten glass in the refining zone into the melting zone and lower the water vapor content of the atmosphere at the surface of the molten glass in the refining zone to less than 25 vol. %, wherein the amount of oxidant injected into the refining zone and the amount of oxidant fed to said burners together equals from 85% to 120% of the stoichiometric amount required for complete combustion of said fuel. 2. A method according to claim 1 wherein the total amount of oxidant injected into the refining zone is 15% to 80% of the stoichiometric amount of oxidant needed for complete combustion of said fuel fed to said furnace. 3. A method according to claim 1 wherein the total amount of oxidant injected into the refining zone is 30% to 50% of the stoichiometric amount of oxidant needed for complete combustion of said fuel fed to said furnace. 4. A method according to claim 1 wherein the oxidant injected into the refining zone blankets the entire upper surface of the molten glass in the refining zone. 5. A method according to claim 1 wherein the oxidant fed to said melting zone and injected into said refining zone comprises at least 90 vol. % oxygen. 6. A method according to claim 5 wherein the total amount of oxidant injected into the refining zone is 15% to 80% of the stoichiometric amount of oxidant needed for complete combustion of said fuel fed to said furnace. 7. A method according to claim 5 wherein the total amount of oxidant injected into the refining zone is 30% to 50% of the stoichiometric amount of oxidant needed for complete combustion of said fuel fed to said furnace. 8. A method according to claim 5 wherein the oxidant injected into the refining zone blankets the entire upper surface of the molten glass in the refining zone.