초록 ▼

A process is described for the manufacture of flexible tubular elements, particularly stents for the medical field, the process comprising the steps of: a) providing a hollow metal tube (or metal coated tube) with an open pattern of a chemical-etch-resistant coating layer; b) supporting the holl

A process is described for the manufacture of flexible tubular elements, particularly stents for the medical field, the process comprising the steps of: a) providing a hollow metal tube (or metal coated tube) with an open pattern of a chemical-etch-resistant coating layer; b) supporting the hollow metal tube with a coating thereon onto a chemical etch resistant support element; c) contacting the open pattern with a solution capable of etching the metal of the hollow metal tube so that said metal is etched away from physically exposed surfaces of the metal tube and openings in the metal tube corresponding to the open pattern of the coating layer are created in the metal tube element without etching the chemical etch resistant support element; and d) removing the metal tube from the chemical etch resistant support element.

대표청구항 ▼

1. A process for the manufacture of flexible cylindrical stents comprising: a) providing a hollow metal tube with an open pattern of a chemical-etch-resistant coating layer; b) applying a fine particulate slurry using mild agitation to said open pattern of said tube so as to ensure that each phy

1. A process for the manufacture of flexible cylindrical stents comprising: a) providing a hollow metal tube with an open pattern of a chemical-etch-resistant coating layer; b) applying a fine particulate slurry using mild agitation to said open pattern of said tube so as to ensure that each physically exposed surface of said open pattern is substantially uniform; c) supporting said hollow metal tube with a coating thereon on a chemical etch resistant support element; d) contacting the open pattern with a solution capable of etching the metal of the hollow metal tube so that said metal is etched away from physically exposed surfaces of the metal tube and openings in the metal tube corresponding to the open pattern of the coating layer are created in the metal tube element without etching said chemical etch resistant support element; and e) removing said metal tube from said chemical etch resistant support element. 2. The process of claim 1 wherein said contacting of the open pattern with said solution is effected by having the metal tube both rotate and revolve, and by having a spray which repeatedly alters its angle of spray towards said metal tube. 3. The process of claim 1 wherein more than one metal tube is supported on a movable support, and said movable support is passed through an area where chemical etch solution is applied by spraying. 4. The process of claim 3 wherein said spraying of said etchant solution is performed while the supported cylindrical element both rotates on a longitudinal axis and is revolved with at least some movement in a direction perpendicular to said longitudinal axis, while said solution capable of etching the metal of the metal tubular element is sprayed at a temperature between 20 and 65° C. 5. The process of claim 4 wherein said etchant solution comprises a ferric chloride solution with a Baume between 48 and 55 degrees at a temperature between 110 and 140° F. 6. The process of claim 3 wherein said etchant solution comprises a ferric chloride solution with a Baume between 48 and 55 degrees at a temperature between 110 and 140° F. 7. The process of claim 1 wherein said solution, capable of etching the metal of the hollow metal tube, contacts said metal of the hollow metal tube at a solution temperature above 40° C. 8. The process of claim 7 wherein said solution comprises ferric chloride solution with a Baume' above 47.5°. 9. The process of claim 1 wherein more than one tubular element is on the same support or said tubular element and the open pattern defines more than one tubular medical element on each tubular element. 10. The process of claim 1 wherein said open pattern is formed by wash development of a resist layer and wash development of said resist layer is performed with a developer which will develop a pattern of resist layer and contact between the resist layer and the developer is effected by spraying said developer onto a surface of said resist layer while said hollow metal tube element is rotating and with said spray being emitted from nozzles which vary their relative angle with respect to the hollow metal tube repeatedly while spraying.