초록 ▼

The invention pertains to a process for preparing a sulfided hydrotreating catalyst in which a hydrotreating catalyst is subjected to a sulfidation step, wherein the hydrotreating catalyst comprises a carrier comprising at least 50 wt % of alumina, the catalyst comprising at least one hydrogenation

The invention pertains to a process for preparing a sulfided hydrotreating catalyst in which a hydrotreating catalyst is subjected to a sulfidation step, wherein the hydrotreating catalyst comprises a carrier comprising at least 50 wt % of alumina, the catalyst comprising at least one hydrogenation metal component and an organic compound comprising at least one covalently bonded nitrogen atom and at least one carbonyl moiety, the molar ratio between the organic compound and the total hydrogenation metal content being at least 0.01:1. The invention further pertains to the use of said hydrotreating catalyst in hydrotreating a hydrocarbon feed, in particular to achieve hydrodenitrogenation, (deep) hydrodesulfurization, or hydrodearomatization.

대표청구항 ▼

1. A process for preparing a sulfided hydrotreating catalyst comprising the steps of: a). compositing a catalyst carrier comprising at least 50 wt % of alumina with at least one hydrogenation metal component; b). combining the product of step a. with an organic compound comprising at least one c

1. A process for preparing a sulfided hydrotreating catalyst comprising the steps of: a). compositing a catalyst carrier comprising at least 50 wt % of alumina with at least one hydrogenation metal component; b). combining the product of step a. with an organic compound comprising at least one covalently bonded nitrogen atom and at least one carbonyl moiety, the molar ratio between the organic compound and the total hydrogenation metal content being at least 0.01:1, and c). sulfiding the product of step b. 2. The process of claim 1 wherein the organic compound comprises at least two nitrogen atoms and at least two carbonyl moieties. 3. The process of claim 1 wherein at least one carbonyl moiety is present in a carboxyl group. 4. The process of claim 1 wherein at least one nitrogen atom is covalently bonded to at least two carbon atoms. 5. The process of claim 1 wherein the organic compound is of formula (I) (R1R2)N--R3--N(R1'R2') (I) wherein R1, R2, R1' and R2' are independently selected from alkyl, alkenyl, and allyl with up to 10 carbon atoms optionally substituted with one or more groups selected from carbonyl, carboxyl, ester, ether, amino, or amido, and R3 is an alkylene group with up to 10 carbon atoms which may be interrupted by --O-- or --NR4-, R4 being selected from the same group as indicated above for R1, which R3 alkylene group may be substituted with one or more groups selected from carbonyl, carboxyl, ester, ether, amino, or amido, with the proviso that the organic compound of formula (I) comprises at least one carbonyl moiety. 6. The process of claim 5 wherein at least two of R1, R2, R1' and R2' have the formula --R5--COOX, wherein R5 is an alkylene group having 1-4 carbon atoms, and X is hydrogen or another cation, where if X is a multivalent cation, one X can adhere to two or more --R5--COO groups. 7. The process of claimed 1 wherein the sulfidation is carried out ex-situ. 8. The process of claim 1 wherein the sulfidation is carried out in-situ with an optionally spiked hydrocarbon feed. 9. The process of claim 1 wherein the carrier comprising the hydrogenation metal component and the organic compound is dried at a temperature sufficiently low to maintain a ratio of the organic compound to the total hydrogenation metal content of at least 0.01:1. 10. The process of claim 1 wherein the alumina comprises a transition alumina. 11. A process for hydrotreating a hydrocarbon feed wherein a hydrocarbon feed is contacted under hydrotreating conditions with a catalyst obtained by the process of claim 1. 12. The process of claim 11 wherein the hydrocarbon feed contains at least 0.2 wt % of sulfur, calculated as S. 13. The process of claim 1 wherein the molar ratio between the organic compound and the total hydrogenation metal content is between 0.01:1 and 0.55:1. 14. The process of claim 1 wherein the composite of step a. is calcined prior to step b. 15. The process of claim 14 wherein the calcination step is carried out at a temperature of from about 400 to about 850° C. 16. The process of claim 1 wherein hydrogenation metal components comprise at least one hydrogenation metal component of Group VI and nickel.