초록 ▼

A process for forming a polyurea coating on a wood composite substrate comprises the steps of applying an isocyanate to an edge of the wood substrate to form a pretreated edge and applying a polymer latex to the pretreated edge to form the polyurea coating. This polyurea coating provides excellent p

A process for forming a polyurea coating on a wood composite substrate comprises the steps of applying an isocyanate to an edge of the wood substrate to form a pretreated edge and applying a polymer latex to the pretreated edge to form the polyurea coating. This polyurea coating provides excellent protection against the penetration of water through the edges and into the interior of the wood composite material and wood composite materials having this polyurea coating have significantly less edge swelling and adsorb considerably less water than wood composites that have no such protective coatings.

대표청구항 ▼

1. A process for forming a polyurea coating on a wood composite substrate comprising: (a) applying an isocyanate, at a concentration of from about 1 g/m to about 20 g/m, to an edge of the wood substrate to form a pretreated edge; and (b) applying a polymer latex to the pretreated edge. 2. The

1. A process for forming a polyurea coating on a wood composite substrate comprising: (a) applying an isocyanate, at a concentration of from about 1 g/m to about 20 g/m, to an edge of the wood substrate to form a pretreated edge; and (b) applying a polymer latex to the pretreated edge. 2. The process according to claim 1, wherein the isocyanate comprises a diphenylmethane-p,p'-diisocyanate polymer. 3. The process according to claim 2, wherein the isocyanate further comprises an emulsifier. 4. The process according to claim 3, wherein the emulsifier is selected from the group consisting of tung oil and linseed oil. 5. The process according to claim 1, wherein the isocyanate comprises a diphenylmethane-p,p'-diisocyanate polymer and drying oils in a ratio of from about 20:1 to 1:20. 6. The process according to claim 1, wherein the polymer latex comprises a polymer selected from the group consisting of acrylics and polyvinyl acetates. 7. The process according to claim 1, wherein the polymer latex comprises a wax emulsion. 8. The process according to claim 1, wherein the polymer latex comprises a polyurea catalyst. 9. The process according to claim 1, wherein the wood substrate is selected from the group consisting of plywood, particleboard, flakeboard, and oriented strand board. 10. A process for preparing a polyurea coating for a wood substrate comprising: providing an isocyanate; and reacting in-situ on an edge of the wood substrate the isocyanate with a polymer selected from the group consisting of acrylics and polyvinyl acetates to form the polyurea coating. 11. The process according to claim 10, wherein a urethane bond is formed between isocyanate and a radical on the wood substrate, the radical being selected from the group consisting of a hydroxyl group, and a carboxyl group. 12. The process according to claim 10, wherein the polyurea coating is present in liquid form and whereby carbon dioxide gas is produced as a by-product of the reaction between the isocyanate and the polymer such that a foam is produced, the foam comprising a carbon dioxide gas dispersed phase and a polyurea liquid continuous phase. 13. A wood composite having a polyurea coating formed by: (a) applying an isocyanate, at a concentration of from about 1 g/m to about 20 g/m, to an edge of the wood composite to form a pretreated edge; and (b) applying a polymer latex to the pretreated edge to form the polyurea coating. 14. The process according to claim 1, wherein the edge is profiled.