초록 ▼

Cure and consolidation of a viscous thermoplastic resin, especially one that softens and melts at a high temperature, is improved by assisting autoclave pressurized momentum transport for compaction of the composite using high frequency, low amplitude acoustic vibration within the resin. The vibrati

Cure and consolidation of a viscous thermoplastic resin, especially one that softens and melts at a high temperature, is improved by assisting autoclave pressurized momentum transport for compaction of the composite using high frequency, low amplitude acoustic vibration within the resin. The vibration induces shear thinning in the resin which promotes resin flow, achieves filling or collapse of voids, and assists consolidation of the composite preform.

대표청구항 ▼

1. A method for curing a viscous thermoplastic resin preform having significant residual volatiles, comprising the steps of: a) preparing a fiber-reinforced resin perform; b) enclosing the preform in a pressure zone; c) applying a suction to reduce the pressure below one ambient atmosphere in t

1. A method for curing a viscous thermoplastic resin preform having significant residual volatiles, comprising the steps of: a) preparing a fiber-reinforced resin perform; b) enclosing the preform in a pressure zone; c) applying a suction to reduce the pressure below one ambient atmosphere in the pressure zone to extract residual volatiles and condensation by-products during curing; d) then, compacting the preform; e) then, heating the preform to a curing temperature of the resin while inputting acoustic vibration into the preform at a vibration frequency to assist momentum transport of the resin for adequate flow to fill voids and to assist in consolidating the preform as the resin melts and cures at the curing temperature to a composite. 2. The method of claim 1 wherein the heating step occurs in an autoclave and wherein the acoustic vibration is input into the preform using transducers that act through a layup mandrel which supports the preform. 3. The method of claim 1 wherein the acoustic vibration is input at a frequency of about 105Hz or greater with a displacement amplitude of about 10-6m. 4. The method of claim 3 wherein the vibration frequency induces Newtonian Theological behavior in a pseudoplastic fluid state of the resin as the resin melts and cures. 5. The method of claim 3 the melted resin has a viscosity greater than 106Pa-sec. 6. The method of claim 1 wherein step (e) results in the composite being substantially free of porosity and free from microcracking because the residual volatiles and the condensation by-products generated during curing escape from the preform. 7. The method of claim 1 further comprising the step of controlling displacement of the fibers in the resin preform to avoid distortion of the fibers in the composite. 8. The method of claim 1 wherein the resin is a thermoplastic that exhibits non-Newtonian rheological behavior. 9. The method of claim 8 wherein the resin is pseudoplastic so that the viscosity of the resin decreases with an increase in shear rate. 10. The method of claim 9 wherein step (e) results in the composite being substantially free of porosity and free from microcracking because the residual volatiles and the condensation by-products generated during curing escape from the preform.