초록 ▼

A method for producing small spherical particles that are especially useful as catalysts and catalyst supports employed in chemical processes is disclosed. According to some embodiments, the method includes impregnating a porous support with a metal or metal oxide and dissolving the support to relea

A method for producing small spherical particles that are especially useful as catalysts and catalyst supports employed in chemical processes is disclosed. According to some embodiments, the method includes impregnating a porous support with a metal or metal oxide and dissolving the support to release spherical particles. In certain embodiments the support that is employed in the method comprises a number of spherical voids which determine the size of the spherical particles, and preferably have micrometer range diameters. One embodiment of an attrition resistant Fischer-Tropsch catalyst comprises a plurality of micrometer size spherical metal and/or metal oxide particles that are prepared according to the above-described method.

대표청구항 ▼

1. A method of making at least one spherical particle comprising: loading a support with at least one metal and/or metal oxide, said support comprising a material that is capable of being dissolved away from said metal or metal oxide; and dissolving said support material. 2. The method of clai

1. A method of making at least one spherical particle comprising: loading a support with at least one metal and/or metal oxide, said support comprising a material that is capable of being dissolved away from said metal or metal oxide; and dissolving said support material. 2. The method of claim 1 further comprising selecting a support comprising at least one substantially spherical void. 3. The method of claim 2 wherein said at least one void has a diameter in the range of about 0.1 to 10 microns. 4. The method of claim 3 wherein said diameter is about 2 microns. 5. The method of claim 1 further comprising selecting a support having a structure chosen from the group consisting of particulates and monoliths. 6. The method of claim 1 further comprising selecting a support comprising an acid- or alkali-labile material. 7. The method of claim 6 wherein said dissolving comprises treating said loaded support with an alkali. 8. The method of claim 7 wherein said alkali comprises NaOH or KOH. 9. The method of claim 6 wherein said dissolving comprises treating said metal and/or metal oxide loaded support with an acid. 10. The method of claim 9 wherein said acid comprises HF. 11. The method of claim 1 comprising: impregnating said support with a solution comprising at least one decomposable metal salt, to yield a supported metal or metal oxide precursor, said support containing a plurality of spherical voids; calcining said precursor such that a metal and/or metal oxide loaded support is obtained; optionally, reimpregnating said loaded support with a second solution comprising at least one decomposable metal salt to provide a reimpregnated loaded support and calcining said reimpregnated loaded support; dissolving said support such chat a plurality of spherical metal and/or metal oxide particles are released from said support; and harvesting said particles. 12. The method of claim 11 wherein at least 10% of said particles are spherical. 13. The method of claim 1 wherein said support comprises silica. 14. A spherical particle prepared according to the method of claim 1 having a micrometer range diameter. 15. The particle of claim 14 wherein said diameter is in the range of about 0.1 to 10 microns. 16. The particle of claim 15 wherein said diameter is about 2 microns.