초록 ▼

Silicon infiltration technology is used to produce ceramic bodies having utility as ballistic armor. In a first aspect of the invention, the ballistic armor includes a reaction-bonded silicon carbide body (RBSC). Good ballistic performance can be advanced by loading the permeable mass or preform to

Silicon infiltration technology is used to produce ceramic bodies having utility as ballistic armor. In a first aspect of the invention, the ballistic armor includes a reaction-bonded silicon carbide body (RBSC). Good ballistic performance can be advanced by loading the permeable mass or preform to be infiltrated to a high degree with one or more hard fillers, and by limiting the size of the largest particles making up the mass. In a second aspect, the silicon infiltration technology, e.g., siliconizing or reaction-bonding, is used to bond silicon carbide fibers to at least the back surface of a ceramic armor body, thereby enhancing ballistic stopping power. A third aspect of the invention pertains to the ability to engineer RBSC bodies such that there is little dimensional change during processing, thereby permitting high dimensional reproducibility in large-scale production.

대표청구항 ▼

1. A component of a ballistic armor, said component comprising at least one ceramic layer and at least one backing layer placed behind and bonded to said ceramic layer; said backing layer comprising at least one fiber-reinforced plastic material; said ceramic layer comprising at least one cerami

1. A component of a ballistic armor, said component comprising at least one ceramic layer and at least one backing layer placed behind and bonded to said ceramic layer; said backing layer comprising at least one fiber-reinforced plastic material; said ceramic layer comprising at least one ceramic composite body comprising (a) a matrix comprising silicon carbide; (b) at least one reinforcement material comprising a plurality of filler bodies dispersed throughout said matrix; and (c) no more than about 30 percent by volume of an infiltrant material comprising silicon dispersed throughout said matrix, wherein said ceramic composite body has a hardness of at least about 1100 kg/mm2as measured with a Vickers indenter using a 1 kg load, and further wherein said ceramic composite body is characterized by a fine-grained microstructure (i) exhibiting no more than a small or slight degree of interconnectivity of the bodies making up the filler material(s), and (ii) made up of morphological features, wherein no more than about 10 percent by volume of said morphological features are larger than about 100 microns in size. 2. The component of claim 1, wherein said ceramic composite body has a four-point flexural strength of at least about 280 MPa, and further wherein the armor has a ballistic stopping power of at least about 35.2 m3/kg/s when tested under the following conditions: 7.62 mm projectile unit layers of polymer composite backing material, each of said unit layers consisting of two tapes of unidirectional, extended-chain polyethylene fibers in a thermoplastic resin matrix, cross-plied at right angles to one another total areal density of about 23.25 kg/m2 outer tactical vest simulant comprising 28 plies of KM2 (600 denier) blanket comprising rip-stop nylon. 3. The component of claim 1, wherein said ceramic composite body comprises no more than about 20 percent by volume of said infiltrant phase. 4. The component of claim 1, wherein said ceramic composite body comprises reaction-bonded silicon carbide. 5. The component of claim 1, generally having a plate shape, and being curved in at least one dimension. 6. The component of claim 1, wherein said armor possesses a ballistic stopping power that is at least 90 percent that of a ballistic armor system consisting essentially of a backing layer bonded to a rear surface of a ceramic layer consisting essentially of hot pressed boron carbide. 7. The component of claim 1, wherein said fiber comprises at least one material selected from the group consisting of polyethylene, aramid and glass. 8. The component of claim 1, wherein said reinforcement material comprises silicon carbide. 9. The component of claim 1, wherein said filler bodies consist essentially of particulate. 10. The component of claim 9, wherein said filler bodies further consist essentially of silicon carbide, and further wherein said morphological features of said silicon carbide particulate include crystallites substantially all sizes of which are smaller than about 106 microns. 11. The component of claim 10, wherein said ceramic composite body comprises at least about 65 percent by volume of said silicon carbide particulate. 12. The component of claim 10, wherein said ceramic composite body comprises at least about 70 percent by volume of said silicon carbide particulate. 13. The component of claim 10, wherein at least 90 volume percent of said crystallites of said particulate are smaller than about 55 microns in size.