초록 ▼

A process for making MD (machine direction) oriented polyethylene film is disclosed. The process comprises blending a high-molecular weight, medium-density polyethylene (HMW MDPE) and a linear low-density polyethylene (LLDPE), converting the blend into a thick film, and orienting the thick film into

A process for making MD (machine direction) oriented polyethylene film is disclosed. The process comprises blending a high-molecular weight, medium-density polyethylene (HMW MDPE) and a linear low-density polyethylene (LLDPE), converting the blend into a thick film, and orienting the thick film into a thinner film in the machine direction. The resulting film has high modulus, high gloss, low haze, and relatively high MD tear and dart impact.

대표청구항 ▼

1. A process for preparing a film, said process comprising: (a) blending (i) from about 20 wt % to about 80 wt % of a high-molecular weight, medium density polyethlene that has a density within the range of about 0.92 to about 0.94 g/cc, an MI2within the range of about 0.01 to about 0.5 dg/min,

1. A process for preparing a film, said process comprising: (a) blending (i) from about 20 wt % to about 80 wt % of a high-molecular weight, medium density polyethlene that has a density within the range of about 0.92 to about 0.94 g/cc, an MI2within the range of about 0.01 to about 0.5 dg/min, an MFR within the range of about 50 to about 300, and a multimodal molecular weight distribution comprising a low-molecular weight component and a high-molecular weight component wherein the low molecular weight component has an MI2from about 50 to about 600 dg/min and a density from about 0.94 to about 0.97 g/cc; and (ii) from about 20 wt % to about 80 wt % of a linear low-density polyethylene that has a density within the range of about 0.90 to about 0.93 cc/g and an MI2within the range of about 0.5 to about 50 dg/min; (b) converting product of step (a) into a film; and (c) orienting the film of step (b) uniaxially in the machine direction. 2. The process of claim 1 wherein the film produced in step (c) has a draw-down ratio greater than about 3. 3. The process of claim 1 wherein the film produced in step (c) has a draw-down ratio greater than about 4. 4. The process of claim 1 wherein the linear low-density polyethylene is a copolymer of ethylene with an α-olefin selected from the group consisting of propylene, 1-butene, 1-pentene, 1-hexene, 1-octene, 4-methyl-1-pentene, and mixtures thereof. 5. The process of claim 1 wherein the linear low-density polyethylene is a copolymer of ethylene with 1-hexene. 6. The process of claim 1 wherein the high-molecular weight, medium-density polyethylene has a density within the range of about 0.93 to about 0.94 g/cc. 7. The process of claim 1 wherein the high-molecular weight, medium-density polyethylene has an MI2within the range of about 0.01 to about 0.3 dg/min. 8. A film produced by the process of claim 1.