초록 ▼

A method for forming dendritic metal powders, comprising the steps of: (1) heating a powder comprising non-dendritic particles, under conditions suitable for initial stage sintering, to form a lightly sintered material; and (2) breaking the lightly sintered material to form a powder comprising dendr

A method for forming dendritic metal powders, comprising the steps of: (1) heating a powder comprising non-dendritic particles, under conditions suitable for initial stage sintering, to form a lightly sintered material; and (2) breaking the lightly sintered material to form a powder comprising dendritic particles. In one embodiment, the lightly sintered material is broken by brushing the material through a screen. Another aspect of the present invention comprises the dendritic particles that are produced by the method described above. These particles can comprise any suitable metal, such as transition metals, rare earth metals, main group metals or metalloids or an alloy of two or more such metals. The particles can also comprise a ceramic material, such as a metal oxide. These particles are characterized by a dendritic, highly anisotropic, morphology arising from the fusion of substantially non-dendritic particles, and by a low apparent density relative to the substantially non-dendritic starting material. The present dendritic particles can be of high purity, and substantially free of carbon contamination.

대표청구항 ▼

1. A powder comprising anisotropic titanium-containing particles, wherein said powder is produced by a method comprising: (a) heating a starting titanium-containing powder comprising non-dendritic particles under conditions suitable for initial stage sintering, thereby forming a lightly sintered

1. A powder comprising anisotropic titanium-containing particles, wherein said powder is produced by a method comprising: (a) heating a starting titanium-containing powder comprising non-dendritic particles under conditions suitable for initial stage sintering, thereby forming a lightly sintered material; and (b) breaking the lightly sintered material, thereby forming a powder comprising anisotropic titanium-containing particles having irregular morphology, said particles comprising aggregated and fused non-dendritic titanium-containing particles and having an air-laid density which is lower than the air-laid density of said starting titanium-containing powder, and wherein the starting titanium-containing powder comprises an alloy of titanium. 2. A powder comprising anisotropic titanium-containing particles, wherein said powder is produced by a method comprising: (a) heating a starting titanium-containing powder comprising non-dendritic particles under conditions suitable for initial stage sintering, thereby forming a lightly sintered material; and (b) breaking the lightly sintered material, thereby forming a powder comprising anisotropic titanium-containing particles having irregular morphology, said particles comprising aggregated and fired non-dendritic titanium-containing particles and having an air-laid density which is lower than the air-laid density of said starting titanium-containing powder, and where the starting titanium-containing powder consists essentially of titanium. 3. A metal powder comprising anisotropic titanium-containing particles having irregular morphology, said particles comprising aggregated and lightly sintered non-dendritic titanium-containing particles, wherein the titanium-containing particles comprise an alloy of titanium.