초록 ▼

A process for forming a retroreflective layer on a powder coated substrate is provided. The substrate is powder coated and the powder coating is subsequently partially cured. Reflective elements are then partially embedded in the semi-cured powder. The powder is then fully cured to permanently bond

A process for forming a retroreflective layer on a powder coated substrate is provided. The substrate is powder coated and the powder coating is subsequently partially cured. Reflective elements are then partially embedded in the semi-cured powder. The powder is then fully cured to permanently bond the reflective elements with the powder coating. The resultant retroreflective assembly can be used in any application requiring high detectability in poor visibility conditions, such as road signs and the like.

대표청구항 ▼

1. A process for forming a retroreflective surface on a substrate consisting of: providing a powder coating material; pretreating the substrate; applying the powder coating material to an outer surface of the substrate; partially curing the powder coating such that it becomes tacky or gelled;

1. A process for forming a retroreflective surface on a substrate consisting of: providing a powder coating material; pretreating the substrate; applying the powder coating material to an outer surface of the substrate; partially curing the powder coating such that it becomes tacky or gelled; providing a reflective material; applying a retroreflective layer on the surface of the powder coating by at least partially embedding the reflective material in the partially cured powder coating; and finish curing the powder coating. 2. The process according to claim 1, wherein the step of providing a powder coating is performed by providing a thermoset or thermoplastic polymer. 3. The process according to claim 1, wherein the step of providing a reflective material is performed by providing a plurality of ceramic optical elements. 4. The process according to claim 3, wherein the ceramic optical elements are microspheres. 5. The process according to claim 4, wherein the microspheres are barium titanate glass beads. 6. The process according to claim 4, wherein the microspheres have a refractive index of at least about 1.5. 7. The process according to claim 6, wherein the refractive index is about 1.9. 8. The process according to claim 3, wherein the ceramic optical elements have a particle size of from about 50 to about 1000 micrometers in diameter. 9. The process according to claim 1, wherein the step of applying the powder coating material to an outer surface of the substrate is performed by electrostatically spray coating the powder coating material on the substrate. 10. The process according to claim 1, wherein the step of applying the powder coating material to an outer surface of the substrate is performed by positioning the substrate in a fluidized bed of the powder coating material. 11. The process according to claim 1, wherein the pretreating the substrate step is performed by the steps of cleaning the substrate and conversion coating the substrate prior to applying the powder coating to the outer surface of the substrate. 12. The process according to claim 1, wherein the steps of partially curing the powder coating and finish curing the powder coating are performed by heating the powder coating using a convection heating system. 13. The process according to claim 1, wherein the steps of partially curing the powder coating and finish curing the powder coating are performed by heating the powder coating using infrared or ultraviolet radiation. 14. The process according to claim 1, wherein the step of partially curing the powder coating comprises curing the powder to the gel point of the powder. 15. A process for forming a retroreflective surface on a substrate, the process consisting of: providing a thermoset powder coating material; pretreating the substrate by cleaning and conversion coating the substrate; applying the thermoset powder coating material to the substrate by electrostatic spray or fluidized bed coating; partially curing the thermoset powder to the gel point of the powder; applying reflective ceramic optical elements to the partially cured thermoset powder coating; finish curing the thermoset powder coating to form a retroreflective surface on the substrate; and applying a clear coat to the retroreflective surface. 16. The process according to claim 15, wherein the ceramic optical elements are barium titanate glass microspheres. 17. The process according to claim 15, wherein the ceramic optical elements have a refractive index of from about 1.5 to about 2.6.