초록 ▼

A self-leveling finishing composition capable of providing chemically resistant low profile coatings is described. The finishing composition comprises thermoplastic resin solids and thermosetting resin solids in a weight ratio of about 0.5:1 to about 11:1 and a solvent composition comprising a solve

A self-leveling finishing composition capable of providing chemically resistant low profile coatings is described. The finishing composition comprises thermoplastic resin solids and thermosetting resin solids in a weight ratio of about 0.5:1 to about 11:1 and a solvent composition comprising a solvent capable of dissolving the thermoplastic resin solids component and a solvent miscible co-solvent capable of dissolving the thermosetting resin solids. The finishing composition is applied and dried to a dry-to-touch surface which is thereafter subjected to conditions capable of initiating polymerization of the component thermosetting resin solids. The finishing composition can be used as a substitute for more expensive or more labor intensive coating compositions in existing surface finishing protocols without compromise of surface quality and chemical resistance.

대표청구항 ▼

1. A self-leveling finishing composition for providing durable low profile coatings, said composition comprising: about 10 to about 65% by weight of resin solids comprising about 15% to about 65% by weight non-thermosetting thermoplastic resin solids, and about 5 to about 50% by weight of therm

1. A self-leveling finishing composition for providing durable low profile coatings, said composition comprising: about 10 to about 65% by weight of resin solids comprising about 15% to about 65% by weight non-thermosetting thermoplastic resin solids, and about 5 to about 50% by weight of thermosetting resin solids wherein the weight ratio of thermosetting resin solids to non-thermosetting thermoplastic resin solids is about 0.5:1 to about 11:1; and about 35% to about 90% by weight of a solvent composition comprising a solvent capable of dissolving the non-thermosetting thermoplastic resin solids and a solvent miscible co-solvent capable of dissolving the thermosetting resin solids wherein the solvent and the co-solvent are selected so that the composition, when applied to a surface by a conventional coating method, is capable of flash drying to a dry-to-touch surface coating within less than one hour at ambient temperature. 2. The composition of claim 1 wherein the thermoplastic component is selected from the group consisting of nitrocellulose, cellulose acetate-butyrate, alkyd resin, polyester resin, urethane resin, acrylic resin and epoxy resin. 3. The composition of claim 2 further comprising an effective amount of a flow additive. 4. The composition of claim 1 wherein the thermosetting resin solids are thermally-curable. 5. The composition of claim 1 wherein the thermosetting resin solids are curable by a free radical mechanism. 6. The composition of claim 5 wherein the thermosetting resin component is selected from UV curable monomers, oligomers and polymers, each having up to 6 reactive olefin functional groups. 7. The composition of claim 1, 2, 3, 4 or 5 wherein at least one of the solvent or co-solvent is hydroxy functional. 8. The composition of claim 1, 2, 3, 4 or 5 wherein at least one of the solvent or co-solvent is ketone-functional. 9. The composition of claim 8 further comprising a hydroxy functional compatibilizing solvent. 10. The composition of claim 1 wherein the ratio of thermoplastic to thermosetting resin solids, and the solvent and the co-solvent are selected so that the composition, when applied to a surface by a conventional coating method, is capable of flash drying to a dry-to-touch surface coating within less than 30 minutes at ambient temperature. 11. The composition of claim 1 wherein the weight ratio of thermoplastic to thermosetting resin solids is about 1:1 to about 6:1. 12. The composition of claim 1 wherein the dry-to-touch coating presents a clear, low profile surface. 13. A method for producing a low-profile, mar resistant coating on a surface, said method comprising the steps of applying a composition of claim 1 to coat said surface; drying said applied composition until dry-to-the-touch; subjecting the dried composition to conditions capable of initiating polymerization of the thermosetting resin solids in said composition. 14. The method of claim 13 wherein the thermosetting resin solids are curable by a free radical mechanism and the dried composition is subjected to incident actinic radiation. 15. The method of claim 13 wherein the thermosetting resin solids are thermally curable and the dried composition is subjected to heating to a temperature effective to cure the thermosetting resin solids.