초록 ▼

A method and apparatus for forming an improved pultruded and clinched Z-axis fiber reinforced composite laminate structure. The upper and lower skins and the core are pulled automatically through tooling where the skin material is wetted-out with resin and the entire composite laminate is preformed

A method and apparatus for forming an improved pultruded and clinched Z-axis fiber reinforced composite laminate structure. The upper and lower skins and the core are pulled automatically through tooling where the skin material is wetted-out with resin and the entire composite laminate is preformed in nearly its final thickness. The preformed composite laminate continues to be pulled into an automatic 3-dimensional Z-axis fiber deposition machine that deposits "groupings of fiber filaments" at multiple locations normal to the plane of the composite laminate structure and cuts each individual grouping such that an extension of each "grouping of fiber filaments" remains above the upper skin and below the lower skin. The preformed composite laminate then continues to be pulled into a secondary wet-out station. Next the preformed composite laminate travels into a pultrusion die where the extended "groupings of fiber filaments" are all bent over above the top skin and below the bottom skin producing a superior clinched Z-axis fiber reinforcement as a composite laminate continues to be pulled, catalyzed, and cured at the back section of the pultrusion die. The composite laminate continues to be pulled by grippers that then feed it into a gantry CNC machine that is synchronous with the pull speed of the grippers and where computerized machining, drilling, and cutting operations take place. This entire method is accomplished automatically without the need for human operators.

대표청구항 ▼

A method and apparatus for forming an improved pultruded and clinched Z-axis fiber reinforced composite laminate structure. The upper and lower skins and the core are pulled automatically through tooling where the skin material is wetted-out with resin and the entire composite laminate is preformed

A method and apparatus for forming an improved pultruded and clinched Z-axis fiber reinforced composite laminate structure. The upper and lower skins and the core are pulled automatically through tooling where the skin material is wetted-out with resin and the entire composite laminate is preformed in nearly its final thickness. The preformed composite laminate continues to be pulled into an automatic 3-dimensional Z-axis fiber deposition machine that deposits "groupings of fiber filaments" at multiple locations normal to the plane of the composite laminate structure and cuts each individual grouping such that an extension of each "grouping of fiber filaments" remains above the upper skin and below the lower skin. The preformed composite laminate then continues to be pulled into a secondary wet-out station. Next the preformed composite laminate travels into a pultrusion die where the extended "groupings of fiber filaments" are all bent over above the top skin and below the bottom skin producing a superior clinched Z-axis fiber reinforcement as a composite laminate continues to be pulled, catalyzed, and cured at the back section of the pultrusion die. The composite laminate continues to be pulled by grippers that then feed it into a gantry CNC machine that is synchronous with the pull speed of the grippers and where computerized machining, drilling, and cutting operations take place. This entire method is accomplished automatically without the need for human operators. s; and wherein in the volume particle size distribution, a total volume of particles that have particle sizes falling within a first particle size range is greater than a total volume of particles that have particle sizes falling within a second particle size range, where the first particle size range is defined by a particle size A representing the peak of the volume particle size distribution and a predetermined particle size B that is smaller than the particle size A, the second particle size range is defined by the particle size A and another predetermined particle size C that is larger than the particle size A, and the particle size C minus the particle size A is equal to the particle size A minus the particle size B. 2. The alloy powder according to claim 1, wherein the pulverized material alloy is a pulverized rapidly solidified alloy that was produced from a melt of a material alloy that was cooled at a cooling rate of about 102°C./sec to about 2×104°C./sec.