초록

Rock fibres are made from a melt formed from a blend of low and high halogen waste materials. 80 to 98% are low halogen materials (containing less than 0.5 wt. % halogen) and 2 to 20% are high halogen materials (containing at least 1 wt. % halogen).

대표청구항 ▼

1. A process for forming rock fibres comprising melting mineral solids and forming a melt containing calcium, magnesium and iron in a combined amount of more than 15% by weight of oxides of which at least 1% is iron oxide and forming the fibres from the melt, wherein 80 to 98% by weight of the miner

1. A process for forming rock fibres comprising melting mineral solids and forming a melt containing calcium, magnesium and iron in a combined amount of more than 15% by weight of oxides of which at least 1% is iron oxide and forming the fibres from the melt, wherein 80 to 98% by weight of the mineral solids are low halogen mineral materials that each contain below 0.5% by weight halogen and 2 to 20% by weight of the mineral solids are high halogen mineral waste containing at least 1% by weight halogen and in which the melt comprise 0.05% to 2% fluorine. 2. A process according to claim 1 in which the melting of the high halogen mineral waste is accompanied by the formation of halogen-containing effluent gases, the gases are scrubbed before discharge to the atmosphere with a solid halide forming material and the resultant solid halide is added to the mineral solids as part of the high halogen waste. 3. A process according to claim 1 in which the low halogen mineral materials and the high halogen mineral waste are melted together in a furnace. 4. A process according to claim 1 in which a melt is formed of low halogen mineral material and the high halogen mineral waste is added as powder into the melt or immediately above the melt. 5. A process according to claim 1 in which the melt contains up to 5% halogen. 6. A process according to claim 1 in which the melt contains 0.3 to 2% fluorine. 7. A process according to claim 1 in which the melt contains at least 15% aluminium. 8. A process according to claim 1 in which the melt contains less than 10% alkali metal oxides. 9. A process according to claim 8 in which the amount of iron oxide is at least 3% by weight, the low halogen mineral materials contain below 0.2% by weight halogen, the high halogen mineral weight contain at least 3% by weight halogen and the halogen comprises fluorine. 10. A process according to claim 9 in which the amount of iron oxide is 5 to 12% by weight, the low halogen mineral contains 0.01-0.1% by weight halogen and the high halogen material contains 5-25% by weight halogen. 11. A process according to claim 1 in which the amount of high halogen mineral waste is at least 5% by weight. 12. A process according to claim 1 in which at least 50% of the halogen is fluorine. 13. A process according to claim 1 in which the melt contains a 30-51% silica, 14-35% alumina, 8-30% calcium oxide, 2-25% magnesium oxide, 2-15% iron oxide, a combined amount of iron and magnesium oxides of 10-30%, a combined amount of sodium and potassium oxides of not more than 10% by weight, a combined amount of calcium, sodium and potassium oxides of 10-30% by weight, an amount of titanium dioxide of not more than 6%, a combined amount of titanium dioxide and iron oxide of 4-18%, an amount of boron oxide up tp 5% by weight and an amount of phosphoerous oxide up to 8% by weight. 14. A process according to claim 1 in which the melt contains a 32-48% silica, 15-30% alumina, 10-25% calcium oxide, 2-20% magnesium oxide, 5-12% iron oxide, a combined amount of iron and magnesium oxides of 12-25%, a combined amount of sodium and potassium oxides of not more than 1-10% by weight, a combined amount of calcium, sodium and potassium oxides of 15-25% by weight, an amount of titanium dioxide of not more than 4%, a combined amount of titanium dioxide and iron oxide of 6-12%, an amount of boron oxide up to 3% by weight and an amount of phosphorous oxide up to 8% by weight.