초록 ▼

A molding process that uses a textured interfacial layer to isolate the surface of a mold from the surface of a composite article produced with the mold. A solution is deposited on the mold surface to form the interfacial layer, whose surface opposite the mold is textured. The texture of the interfa

A molding process that uses a textured interfacial layer to isolate the surface of a mold from the surface of a composite article produced with the mold. A solution is deposited on the mold surface to form the interfacial layer, whose surface opposite the mold is textured. The texture of the interfacial layer is then transferred to the surface of the composite article produced with the mold. After demolding, the interfacial layer adheres to the article as a protective coating, but can be readily removed from the article to expose an underlying textured surface of the article.

대표청구항 ▼

1. An open tool molding process for producing a composite article with a textured surface, the method comprising the steps of: depositing a mold release composition on an untextured mold surface of an open tool mold, the mold surface being defined by a polymeric material; spraying a polymeric so

1. An open tool molding process for producing a composite article with a textured surface, the method comprising the steps of: depositing a mold release composition on an untextured mold surface of an open tool mold, the mold surface being defined by a polymeric material; spraying a polymeric solution on the mold surface so that the polymeric solution forms a textured interfacial layer having a thickness of about 0.10 to about 0.18 mm on the mold sureface, the solution being an aqueous polymeric solution chosen from the group consisting of polyvinyl acetate solutions and acrylic latex emulsions; depositing a gel coat layer on the textured interfacial layer so that the gel coat layer has a surface textured by the textured interfacial layer; depositing on the gel coat layer a polymeric material containing a dispersion of fiber material; curing the textured interfacial layer, the gel coat layer and the polymeric material so that the cured polymeric material with the fiber material dispersed therein forms a fiber-reinforced composite article having a textured surface defined by the cured gel coat layer, the textured interfacial layer overlying the textured surface; removing the composite article from the mold so that the textured interfacial layer remains as a protective film on the textured surface of the composite article; and then removing the textured interfacial layer from the composite article to reveal the textured surface of the composite article. 2. The open tool molding process according to claim 1, wherein the textured interfacial layer is removed from the composite article after the composite article has been transported to a site remote from the mold. 3. The open tool molding process according to claim 1, wherein the polymeric solution is deposited using an airless spray gun. 4. The open tool molding process according to claim 3, wherein the interfacial layer is deposited by spraying the polymic solution through a first orifice to form a first sublayer of the textured interfacial layer, and then spraying the polymeric solution through a second orifice to form a second sublayer of the textured interfacial layer, the second being smaller than the first oriface such that second sublayer is finer textured than the first sublayer. 5. The open tool molding process according to claim 1, wherein the gel coat layer is formed of a composition comprising the polymeric material. 6. The open tool molding process according to claim 1, wherein the polymeric solution is dried prior to depositing the gel coat layer, and the gel coat layer is partially cured prior to depositing the polymeric material containing the dispertion of fiber material. 7. The open tool molding process according to claim 1, further comprising the step of depositing a mold release composition on the textured interfacial layer prior to depositing the gel coat layer.