초록 ▼

A layered catalyst composition is disclosed where the composition is prepared by bonding an outer layer comprising a bound zeolite (e.g. zeolite beta) to an inner core material (e.g. cordierite). The use of an organic bonding agent in the catalyst preparation procedure provides a composition that is

A layered catalyst composition is disclosed where the composition is prepared by bonding an outer layer comprising a bound zeolite (e.g. zeolite beta) to an inner core material (e.g. cordierite). The use of an organic bonding agent in the catalyst preparation procedure provides a composition that is sufficiently resistant to mechanical attrition to be used commercially in aromatic alkylation processes (e.g. benzene alkylation to ethylbenzene). Advantages associated with the use of layered compositions include a significant reduction in the amount of zeolite used for a given reactor loading and improved selectivity to desired alkylated aromatic products. Further benefits are realized when the layered composition is formed into shapes having a sufficiently high void volume to reduce pressure drop across the alkylation catalyst bed. This is especially relevant for operation involving high recycle rates and consequently low alkylating agent concentrations in the reaction zone. Such conditions are known to promote reduced byproduct formation.

대표청구항 ▼

1. A process for preparing a layered catalyst composition comprising an inner core, an outer layer bonded to the inner core, the outer layer bonded to the inner core such that the attrition loss is less than 25% of the weight of the outer layer, and the outer layer comprising a zeolite and a binder,

1. A process for preparing a layered catalyst composition comprising an inner core, an outer layer bonded to the inner core, the outer layer bonded to the inner core such that the attrition loss is less than 25% of the weight of the outer layer, and the outer layer comprising a zeolite and a binder, the process comprising: a) coating the inner core with a slurry comprising the zeolite, a sol of the binder, and an organic bonding agent to yield a coated core having the outer layer; b) drying the coated core at a temperature from about 50° C. to about 300° C. to yield a dried coated core; and, c) calcining the dried coated core at a temperature from about 400° C. to about 900° C. for a time sufficient to bond the outer layer to the inner core and provide the layered catalyst composition. 2. The process of claim 1 where the zeolite is selected from the group consisting of beta, zeolite Y, zeolite X, zeolite L, ferrierite, MFI, mordenite, and erionite. 3. The process of claim 1 where the binder is an inorganic metal oxide selected from the group consisting of alumina, silica, magnesia, titania, and zirconia. 4. The process of claim 1 where the inner core is coated with the slurry by rolling or dipping. 5. The process of claim 1 where the inner core is coated with the slurry by spraying the slurry onto a fixed fluidized bed of core particles. 6. The process of claim 1 where the bonding agent is selected from the group consisting of polyvinyl alcohol, hydroxy propyl cellulose, methyl cellulose, and carboxy methyl cellulose. 7. The process of claim 1 where the sol of the binder is a sol of a metal selected from the group consisting of aluminum, silicon, magnesium, titanium, and zirconium. 8. The process of claim 1 where the inner core is selected from the group consisting of cordierite, alpha alumina, theta alumina, magnesia, silicon carbide, metals, zirconia, titania, and mixtures thereof. 9. The process of claim 8 where the inner core is cordierite. 10. The process of claim 1 where the inner core has an effective diameter from about 0.05 mm to about 5 mm. 11. The process of claim 1 where the outer layer has a thickness from about 10 to about 400 microns. 12. The product of the process of claim 1.