초록 ▼

A porous ceramic fiber insulating material and method of making a material having a combination of silica (SiO2) and alumina (Al2O3) fibers, and boron-containing powders is the topic of the new invention. The insulative material is composed of about 60 wt % to about 80 wt % silica fibers, about 20 w

A porous ceramic fiber insulating material and method of making a material having a combination of silica (SiO2) and alumina (Al2O3) fibers, and boron-containing powders is the topic of the new invention. The insulative material is composed of about 60 wt % to about 80 wt % silica fibers, about 20 wt % to about 40 wt % alumina fibers, and about 0.1 wt % to about 1.0 wt % boron-containing powders. A specific boron-containing powder used for this invention is boron carbide powder which provide boron-containing by-products, which aid in fusion and sintering of the silica and alumina fibers. The material is produced by forming an aqueous slurry, blending and chopping the fibers via a shear mixer, orienting the fibers in the in-plane direction, draining water from the fibers, pressing the fibers into a billet, heating the fibers to remove residual water, and firing the billet to fuse the fibers of the material. After sintering, bulk density of the new insulation material ranges from 6 to 20 lb/ft3.

대표청구항 ▼

A porous ceramic fiber insulating material and method of making a material having a combination of silica (SiO2) and alumina (Al2O3) fibers, and boron-containing powders is the topic of the new invention. The insulative material is composed of about 60 wt % to about 80 wt % silica fibers, about 20 w

A porous ceramic fiber insulating material and method of making a material having a combination of silica (SiO2) and alumina (Al2O3) fibers, and boron-containing powders is the topic of the new invention. The insulative material is composed of about 60 wt % to about 80 wt % silica fibers, about 20 wt % to about 40 wt % alumina fibers, and about 0.1 wt % to about 1.0 wt % boron-containing powders. A specific boron-containing powder used for this invention is boron carbide powder which provide boron-containing by-products, which aid in fusion and sintering of the silica and alumina fibers. The material is produced by forming an aqueous slurry, blending and chopping the fibers via a shear mixer, orienting the fibers in the in-plane direction, draining water from the fibers, pressing the fibers into a billet, heating the fibers to remove residual water, and firing the billet to fuse the fibers of the material. After sintering, bulk density of the new insulation material ranges from 6 to 20 lb/ft3. otton and polyester fibers. 14. The fabric of claim 13 wherein said fabric is range-dyed in a thermosol process. 15. The fabric of claim 10 wherein said fabric is comprised of yarns selected from the group consisting of natural fibers, synthetic fibers, and any blends thereof. 16. The fabric of claim 15 wherein said fabric is comprised of a blend of natural and synthetic fibers. 17. The fabric of claim 16 wherein said fabric is comprised of a blend of cotton and polyester fibers. 18. The fabric of claim 17 wherein said fabric is range-dyed in a thermosol process. 19. A comprising a plurality of nicked individual fibers and exhibits a hand that is softer than that exhibited by the same fabric without any nicked individual fibers, at least a portion of which is range-dyed and mechanically finished, wherein said range-dyed and mechanically finished fabric portion is non-directional, wherein said individual fibers are not pulled during said mechanical finishing such that a napped surface is not produced thereby.