초록 ▼

A heat treatable coated article including an infrared (IR) reflecting layer (e.g., of or including Ag), the coated article being able to attain a &Dgr;E* (glass side) no greater than about 3.5, more preferably no greater than 3.0, and even more preferably no greater than 2.6, following or due to hea

A heat treatable coated article including an infrared (IR) reflecting layer (e.g., of or including Ag), the coated article being able to attain a &Dgr;E* (glass side) no greater than about 3.5, more preferably no greater than 3.0, and even more preferably no greater than 2.6, following or due to heat treatment (e.g., thermal tempering). Accordingly, low-E (i.e., low emissivity) coated articles of certain embodiments of this invention appear from the glass side thereof visually similar to the naked eye both before and after heat treatment. Good matchability characteristics (i.e., low &Dgr;E* values) combined with good durability can be achieved by controlling to what extent barrier layer(s) in contact with the IR reflecting layer are nitrided and to what thickness(es) they are sputtered. Optionally, certain embodiments of this invention relate to coated articles that also have high visible transmission and/or good durability. Coated articles herein may be used in the context of insulating glass (IG) window units, vehicle windows, or any other suitable applications. In certain embodiments of this invention, an exemplary layer stack includes: glass/Si3N4/NiCrNx/Ag/NiCrNx/Si3N4. Other materials may instead be used without departing from the scope and/or spirit of the instant invention which is a low-E matchable and/or durable product.

대표청구항 ▼

1. A method of making a coated article, the method comprising: depositing a layer system on a glass substrate, the layer system including an infrared (IR) reflecting metal layer located between and in contact with first and second barrier layers that are at least partially nitrided, controlling

1. A method of making a coated article, the method comprising: depositing a layer system on a glass substrate, the layer system including an infrared (IR) reflecting metal layer located between and in contact with first and second barrier layers that are at least partially nitrided, controlling nitrogen gas flow during sputtering of at least one of the barrier layers so that the nitrogen gas flow is from 0-16 sccm/kW, and heat treating the substrate with the layer system thereon so that due to said heat treating the resulting substrate with the layer system thereon has a &Dgr;E* value (glass side) no greater than 3.5. 2. The method of claim 1, wherein the nitrogen gas flow is from 4-12 sccm/kW.3. The method of claim 2, wherein the nitrogen gas flow is from 6-10 sccm/kW.4. A method of making a coated article, the method comprising: depositing a layer system on a glass substrate, a layer system including at least one infrared reflecting layer located between and in contact with first and second barrier layers; controlling nitrogen gas flow during sputtering of at least one of the barrier layers so that the nitrogen gas flows from 0-16 sccm/kW; and heat treating the substrate with the layer system thereon so that the resulting substrate with the layer system thereon has a &Dgr;E* value (glass side reflective) no greater than 3.5. 5. The method of claim 4, wherein the nitrogen gas flow is from 4-12 sccm/kW.