초록 ▼

Reactive foils and their uses are provided as localized heat sources useful, for example, in ignition, joining and propulsion. An improved reactive foil is preferably a freestanding multilayered foil structure made up of alternating layers selected from materials that will react with one another in

Reactive foils and their uses are provided as localized heat sources useful, for example, in ignition, joining and propulsion. An improved reactive foil is preferably a freestanding multilayered foil structure made up of alternating layers selected from materials that will react with one another in an exothermic and self-propagating reaction. Upon reacting, this foil supplies highly localized heat energy that may be applied, for example, to joining layers, or directly to bulk materials that are to be joined. This foil heat-source allows rapid bonding to occur at room temperature in virtually any environment (e.g., air, vacuum, water, etc.). If a joining material is used, the foil reaction will supply enough heat to melt the joining materials, which upon cooling will form a strong bond, joining two or more bulk materials.

대표청구항 ▼

1. A method of making a freestanding reactive multilayer foil composed of a plurality of alternating layers that can react exothermically, comprising the steps of: providing a substrate; vapor depositing the alternating layers on the substrate to form a reactive multilayer foil having a thickne

1. A method of making a freestanding reactive multilayer foil composed of a plurality of alternating layers that can react exothermically, comprising the steps of: providing a substrate; vapor depositing the alternating layers on the substrate to form a reactive multilayer foil having a thickness in the range of about 10 micrometers to about 1 cm, the vapor deposition conditions chosen for low stress so that the product of stress in the film and the film thickness is kept below 1000 N/m; and separating the multilayer foil from the substrate to provide the freestanding reactive multilayer foil. 2. The method of claim 1 wherein the substrate has sufficient adherence to the deposited layers to retain the layers during deposition but insufficient adherence to prevent removal of the multilayer foil after deposition.3. The method of claim 1 wherein the layers comprise one or more layers of aluminum, and at least one of the layers of aluminum is deposited in contact with the substrate.4. The method of claim 3 wherein the substrate comprises silicon.5. The method of claim 1 wherein the substrate comprises a coating of a release material or a coating of an adhesion material.6. The method of claim 1 wherein the substrate comprises a removable sacrificial layer.7. The method of claim 1 wherein the vapor depositing is under conditions chosen to minimize stress in the deposited layers.8. The method of claim 1 wherein the vapor depositing comprises physical vapor deposition.9. The method of claim 8 wherein the vapor depositing comprises magnetron sputtering or electron beam evaporation.10. The method of claim 1 wherein the substrate is cooled during the vapor depositing.11. The method of claim 1 wherein the layers are deposited to form a multilayer foil having a thickness in the range 50 &mgr;m-1 cm.12. The method of claim 1 wherein vapor depositing the alternating layers comprises vapor depositing alternating layers selected from the group consisting of Rh/Si, Ni/Si, and Zr/Si.13. The method of claim 1 wherein vapor depositing the alternating layers comprises vapor depositing alternating layers selected from the group consisting of Ni/Al, Ti/Al, Monel/Al, and Zr/Al.14. The method of claim 1 wherein vapor depositing the alternating layers comprises vapor depositing alternating layers selected from the group consisting of Al/Fe2O3and Al/Cu2O.15. The method of claim 1 wherein vapor depositing the alternating layers comprises vapor depositing a layer comprising boron or carbon.16. The method of claim 1 wherein vapor depositing the alternating layers comprises vapor depositing a layer comprising a transition metal.17. The method of claim 1 including the further step of forming openings in the foil.18. The method of claim 1 including the further step of forming a periodic pattern of openings in the foil.19. The method of claim 1 including the further steps of forming a plurality of openings in the foil, the openings having effective diameters in the range 10-10,000 micrometers.20. The method of claim 1 further comprising the step of depositing an intermediate layer between the alternating layers.21. A method of making a freestanding reactive multilayer foil composed of a plurality of alternating layers that can react exothermally, comprising the steps of: providing a substrate comprising a removable sacrificial layer of copper, brass or photoresist; vapor depositing the alternating layers on the substrate to form the reactive multilayer foil; and separating the multilayer foil from the substrate.