초록 ▼

A method is disclosed for partly reinforcing a workpiece which is capable of reinforcing the reinforcement requiring part of the workpiece on which stress is liable to be concentrated upon use of the workpiece. A workpiece1made of metal having a reinforcement requiring part10and a forming die3are pr

A method is disclosed for partly reinforcing a workpiece which is capable of reinforcing the reinforcement requiring part of the workpiece on which stress is liable to be concentrated upon use of the workpiece. A workpiece1made of metal having a reinforcement requiring part10and a forming die3are provided. The reinforcement requiring part10of the workpiece1is heated up to a higher temperature than the other part18. The reinforcement-requiring part10is quenched and reinforced as compared to the other part18by bringing the forming surface area of the forming die3into direct contact with at least the reinforcement-requiring part10of the workpiece1which is then strongly pressed.

대표청구항 ▼

1. A method for partly reinforcing a workpiece comprising the steps of: providing a forming die; providing a workpiece that is made up of a metal substrate having a reinforcement requiring part; applying heating means for forming a first heating atmosphere having a high temperature and a sec

1. A method for partly reinforcing a workpiece comprising the steps of: providing a forming die; providing a workpiece that is made up of a metal substrate having a reinforcement requiring part; applying heating means for forming a first heating atmosphere having a high temperature and a second heating atmosphere having a relatively lower temperature than the first heating atmosphere; placing the reinforcement requiring part in the first heating atmosphere and the other part of the workpiece in the second heating atmosphere, respectively, thereby heating up the reinforcement requiring part to a higher temperature than the other part; partly reinforcing the workpiece by bringing a forming surface area of the die into contact with at least the reinforcement requiring part followed by strongly pressing to quench-reinforce the reinforcement requiring part as compared to the other part of the workpiece; wherein said means comprises a furnace room and one or more partition walls disposed within said furnace room said one or more partition walls defining said first and second heating atmospheres that are disposed at a first and second temperature, respectively, the first temperature being higher than said second temperature. 2. The method of claim 1, wherein press-forming of the reinforcement requiring part is also carried out in the partly reinforcing step concurrently with the quench-reinforcing of the reinforcement requiring part.3. The method of claim 1, wherein the first heating atmosphere is heated up to the first temperature by induction heating using an electric conductor.4. The method of claim 1, wherein the forming surface area of the forming die for forming the reinforcement requiring part has a higher workpiece-cooling power than the other part of the die.5. The method of claim 1, wherein the reinforcement requiring part is at least a part of a hole's peripheral area of the workpiece.6. The method of claim 1, wherein the reinforcement requiring part is at least a part of a hole's peripheral area of the workpiece, and in the partly reinforcing step, the peripheral area of the hole is brought into contact with the forming surface area of the die to form a wall-shaped or cylindrically formed part by press-forming concurrently with quench-reinforcing of the formed part more than the other part.7. The method of claim 1, wherein the reinforcement requiring part is at least a part of the outer peripheral area of the workpiece.8. The method of claim 1, wherein a forming part of the die for forming the reinforcement requiring part is equipped with cooling means for forcibly cooling the forming part.9. The method of claim 1, wherein the forming part of the die for forming the reinforcement requiring part is made of material or designed so as to have a higher thermal conductivity than the other part of the forming die.10. The method of claim 1, wherein the workpiece is made of an iron-based material, and the reinforcement requiring part is heated up to at least A1 transformation temperature.