초록 ▼

A method of providing a protective barrier between a plastic casing and a rubber layer molded over the plastic casing. The protective barrier is applied to the plastic casing and then the rubber layer molded onto the plastic casing over the protective barrier. The protective barrier prevents the rub

A method of providing a protective barrier between a plastic casing and a rubber layer molded over the plastic casing. The protective barrier is applied to the plastic casing and then the rubber layer molded onto the plastic casing over the protective barrier. The protective barrier prevents the rubber layer from reacting with the underlying plastic casing. In one embodiment, the plastic casing comprises a polycarbonate resin and the protective barrier comprises a polyurethane coating.

대표청구항 ▼

1. A method of forming a rubber-overmolded plastic casing, the method comprising: providing a plastic piece comprising a polycarbonate resin, the plastic piece being a part of a casing applying a protective barrier as a liquid solution directly to at least a part of the plastic piece; curing

1. A method of forming a rubber-overmolded plastic casing, the method comprising: providing a plastic piece comprising a polycarbonate resin, the plastic piece being a part of a casing applying a protective barrier as a liquid solution directly to at least a part of the plastic piece; curing the liquid solution to form a protective barrier directly on at least the part of the plastic piece; and molding a rubber layer directly onto the protective barrier over the plastic piece. 2. The method as described in claim 1, further comprising, before applying the protective barrier, cleaning at least the part of the plastic piece over which the protective barrier will be applied.3. The method as described in claim 2 further comprising, after cleaning the part of the plastic piece and before applying the protective barrier, drying the plastic piece.4. The method as described in claim 1, wherein the plastic piece is translucent.5. The method as described in claim 1, wherein the casing is a computer casing.6. The method as described in claim 1, wherein the casing is for a computer peripheral.7. The method as described in claim 1, wherein the protective coating is applied under ambient conditions.8. The method as described in claim 1, wherein the protective barrier is thick enough to prevent the rubber layer from attacking the plastic piece.9. The method as described in claim 1, wherein the protective barrier is clear.10. The method as described in claim 1, further comprising, before molding the rubber layer over the protective barrier, curing the protective barrier.11. The method as described in claim 1, wherein the rubber layer is translucent.12. A method of protecting a plastic piece from reacting with a rubber layer molded over at least a part of the plastic piece, the method comprising: providing the plastic piece comprising a polycarbonate resin; cleaning at least the part of the plastic piece; drying the plastic piece; after cleaning and drying the plastic piece, applying a liquid solution to at least the part of the plastic piece; curing the liquid solution to form a polyurethane coating directly on at least the part of the plastic piece; and molding the rubber layer directly onto the polyurethane coating. 13. The method as described in claim 12 wherein at least the part of the plastic piece is cleaned using a solvent.14. The method as described in claim 13 wherein the solvent is selected from the group consisting of: isopropyl alcohol, ethanol, and methanol.15. The method as described in claim 12 wherein at least the part of the plastic piece is cleaned using a cleaner.16. The method as described in claim 12 wherein the plastic piece is dried using compressed air.17. The method as described in claim 12 wherein the plastic piece is dried in an oven.18. The method as described in claim 12 wherein the plastic piece is translucent.19. The method as described in claim 12 wherein the plastic piece is a part of a computer casing.20. The method as described in claim 12 wherein the plastic piece is a part of a casing for a computer peripheral.21. The method as described in claim 12 wherein the liquid solution comprises an isocyanate component and a polyol component.22. The method as described in claim 21 wherein the liquid solution comprises approximately equal parts of the isocyanate component and the polyol component.23. The method as described in claim 21 wherein the isocyanate component and the polyol component are present in the liquid solution in a ratio of between about 45:55 and about 55:45.24. The method as described in claim 12 wherein the liquid solution is applied under ambient conditions.25. The method as described in claim 12 wherein the liquid solution is applied at a temperature between about 20° and about 30° C.26. The method as described in claim 12 wherein the liquid solution is applied under less than about 80% relative humidity.27. The method as described in claim 12 wherein the polyurethan e coating has a thickness of between about 0.01 and about 0.03 mm.28. The method as described in claim 12 wherein the polyurethane coating has a thickness of 0.02±0.005 mm.29. The method as described in claim 12 wherein the polyurethane coating is clear.30. The method as described in claim 12 wherein the liquid solution is cured at an elevated temperature.31. The method as described in claim 12 wherein the liquid solution is cured at a temperature between about 70° and about 90° C.32. The method as described in claim 12 wherein the liquid solution is cured at an elevated temperature for between about 20 and about 60 minutes.33. The method as described in claim 12 wherein the rubber layer is translucent.