초록 ▼

A prepolymer composition for producing polyurethane insulating foams with fire-retardant properties from pressure tanks which consists of a prepolymer component with at least one PU prepolymer with a content of NCO groups of 4 to 20 wt % and usual additives, as well as a propellant component, wherei

A prepolymer composition for producing polyurethane insulating foams with fire-retardant properties from pressure tanks which consists of a prepolymer component with at least one PU prepolymer with a content of NCO groups of 4 to 20 wt % and usual additives, as well as a propellant component, wherein the prepolymer component is substantially halogenfree and has 5 to 40 wt %, based on the prepolymer component, of softening phosphates and/or phosphonates with the formulae O═P(OR3and O═P(OR)2R.

대표청구항 ▼

1. A prepolymer composition for producing polyurethane insulating foams with fire-retardant properties from aerosol cans, wherein said prepolymer composition comprises: a prepolymer component having at least one polyurethane (PU) prepolymer with a content of NCO groups of 4 to 20 wt % said prep

1. A prepolymer composition for producing polyurethane insulating foams with fire-retardant properties from aerosol cans, wherein said prepolymer composition comprises: a prepolymer component having at least one polyurethane (PU) prepolymer with a content of NCO groups of 4 to 20 wt % said prepolymer being prepared from aromatic polyisocyanates and polyester-polyols prepared from aromatic polycarboxylic acids and ethylene glycol or glycerol, said polyester polyols having a hydroxyl number between about 100 and 300 and a functionality of 2 to 4 and a propellant component selected from the group consisting of propane, butane, fluorocarbons and dimethyl ether, and combinations thereof, wherein said prepolymer component is halogen-free and has a content of 5 to 40 wt %, of softening phosphates, phosphonates or combinations thereof having the formulae O═P(OR) 3and O═P(OR)2R, wherein R is the same or different and selected from aralkyl, aryl, or alkylaryl groups having up to 10 carbon atoms, based on the prepolymer content.2. The prepolymer composition of claim 1, wherein the propellent is a fluorocarbon.3. The prepolymer composition of claim 2, wherein said prepolymer is prepared from monomers selected from the group consisting of tolylene diisocyanate, and diphenylmethane diisocyanate.4. The prepolymer composition of claim 3 wherein softening phosphates and phosphonates are used for setting polyurethane insulating foams to be flame-retardant, the propellant is a fluorocarbon, and the polyester-polyol is prepared from ethylene glycol. 5. The prepolymer composition of claim 1 wherein the polyester polyols are at least partly phosphorous-modified, and the polyester-polyol is prepared from ethylene glycol.6. The prepolymer composition of claim 1, wherein propellant content is 5 to 40 wt % of the prepolymer composition.7. The prepolymer composition of claim 1, wherein the propellant component is selected from the group consisting of propane and butane, and the polyester-polyol is prepared from ethylene glycol.8. The prepolymer composition of claim 1, wherein the propellant component contains fluorocarbon selected from the group consisting of C2HF5, C2H2F4(unsymmetrical), C2H3F3, C2H4F2(unsymmetrical) and mixtures thereof.9. The prepolymer composition of claim 1, wherein the prepolymer composition additionally contains a flame-retardant additive which is free from chlorine and bromine.10. The prepolymer composition of claim 9, wherein the flame-retardant additive is selected from the group consisting of melamine, melamine cyanurate, dimelamine phosphate, melamine phosphate, cyanodiamide, dicyanodiamide, aluminum trihydrate, ammonium polyphosphate and mixtures thereof.11. The prepolymer composition of claim 1, wherein the initial service viscosity of the polyurethane prepolymer at 20° C. is 5000 to 20000 mPa.s.12. The prepolymer composition of claim, 1 wherein the initial service viscosity of the polyurethane prepolymer is between 8000 to 15000 mPa.s. at 20° C.