초록

The present invention involves coatings deposited on a substrate including a layer having a selected resistivity. The resistive layer can serve as a heat source in a variety of applications and can be fabricated using an arc plasma spraying procedure.

대표청구항 ▼

1. A heater comprising at least one thermally sprayed resistive heating layer, wherein said thermally sprayed resistive heating layer comprises a mixture of a first material, a second material, and a third material, wherein said first material is an electrically conducting material, said second mate

1. A heater comprising at least one thermally sprayed resistive heating layer, wherein said thermally sprayed resistive heating layer comprises a mixture of a first material, a second material, and a third material, wherein said first material is an electrically conducting material, said second material is an electrically insulating material, and said third material alters thermal expansion of said resistive heating layer. 2. The heater of claim 1, further comprising a substrate on which said resistive healing layer is coated. 3. The heater of claim 2, wherein said substrate comprises a conductor, a metal, a ceramic, a plastic, graphite, or a carbon fiber element. 4. The heater of claim 2, wherein said substrate is a pipe, nozzle, impellor, or sparkless ignition device, or is employed in a rapid thermal processing apparatus. 5. The heater of claim 1, further comprising a voltage source coupled to said resistive heating layer. 6. The heater of claim 1, wherein said first material, said second material, or said third material is a ceramic. 7. The heater of claim 6, wherein said first material is a ceramic selected from the group consisting of silicon carbide, molybdenum disilicide, lanthanum chromato, zirconium diborido, titanium diboride, boron carbide, tungsten disilicide, and tin oxide. 8. The heater of claim 6, wherein said second material is a ceramic selected from the group consisting of aluminum oxide, aluminum nitride, and mullite. 9. The heater of claim 6, wherein said third material is a ceramic selected from the group consisting of silicon carbide, molybdenum disilicide, lanthanum chromave, zirconium diboride, titanium diboride, boron carbide, tungsten disilicide, tin oxide, aluminum oxide, aluminum nitride, mullite, silica, yttrium oxide, magnesium zirconate, chromium-doped aluminum oxide, chromium boride, and ceramic fibers. 10. The heater of claim 6, wherein said heater is operable up to 1200° C. in air. 11. The heater of claim 1, wherein said third material is selected from the group consisting of molybdenum, a metal, polystyrene, and platinum. 12. The heater of claim 1, wherein said first material has a positive temperature coefficient of resistivity and said third material has a negative temperature coefficient of resistivity. 13. The heater of claim 12, wherein said first material is titanium diboride and said third material is silicon carbide. 14. The heater of claim 12, wherein said first material is molybdenum disilicide and said third material is lanthanum chromate. 15. The heater of claim 1, wherein said resistive heating layer comprises a plurality of thermally sprayed layers. 16. The heater of claim 1, wherein said thermally sprayed resistive heating layer is a plasma sprayed resistive heating layer. 17. The heater of claim 1, further comprising a thermal barrier layer. 18. The heater of claim 17, wherein said thermal barrier layer comprises zirconium oxide. 19. The heater of claim 1, further comprising a thermal barrier layer disposed between said substrate and said resistive heating layer. 20. The heater of claim 1, furthur comprising a thermal barrier layer, wherein said resistive heating layer is disposed between said thermal barrier layer and said substrate. 21. A method of fabricating at least one resistive heating layer, said method comprising the steps of:a) mixing a first material, a second material, and a third material, wherein said first material is an electrically conducting material, said second material is an electrically insulating material, and said third material alters thermal expansion of said resistive heating layer; andb) thermally spraying the mixture of step (a) onto a subsfrate, thereby fabricating a resistive heating layer. 22. The method of claim 21, further comprising step (c) removing said resistive heating layer from said substrate. 23. The method of claim 21, further comprising step (c) connecting a voltage source to said resistive heating layer, thereby producing a h eater. 24. The method of claim 21, wherein said substrate is a pipe, nozzle, impellor, or sparkless ignition device or is employed in a rapid thermal processing apparatus. 25. The method of claim 21, further comprising the step, before step (b), of forming a bonding layer between said substrate and said resistive heating layer. 26. The method of claim 21, further comprising the step, before step b), of forming an electrically insulating layer between said substrate and said resistive heating layers. 27. The method of claim 21, further comprising step (c) coating said resistive heating layer with a thermal barrier layer, an electrically insulating layer, a thermally emissive layer, or a thermally conductive layer. 28. The method of claim 21, wherein said substrate in step b) is coated with a thermal barrier layer. 29. The method of claim 21, wherein said thermal spraying is plasma spraying. 30. A heater comprising a thermally sprayed resistive heating layer that comprises a mixture of titanium diboride and aluminum oxide. 31. A heater comprising a thermally sprayed resistive heating layer that comprises a mixture of molybdenum silicide and mullite. 32. A heater comprising a thermally sprayed resistive heating layer that comprises a mixture of zirconium diboride and aluminum oxide. 33. A heater comprising a thermally sprayed resistive heating layer that comprises a mixture of a first material, a second material, and a third material, wherein said first material is an electrically conducting material, said second material is an electrically insulating material, and said third material alters a property of said resistive heating layer, wherein said first material has a positive temperature coefficient of resistivity and said third material has a negative temperature coefficient of resistivity. 34. The heater of claim 33, wherein said first material is titanium diboride and said third material is silicon carbide. 35. The heater of claim 33, wherein said first material is molybdenum disilicide and said third material is lanthanum chromate. 36. The heater of claim 33, wherein said property is selected from the group consisting of thermal conductivity, resistivity, thermal emissivity, bonding, hardness, ductility, thermal expansion, porosity, chemical resistance, oxidation resistance, reduction resistance, molten metal resistance, temperature coefficient of resistivity, self-regulating heating, decorative finish, catalytic activity, sintering, reflecflvity, abrasion resistance, strength, sensing capabilities, and filtering properties; and wherein said heater further comprises a thermal barrier layer disposed between said substrate and said resistive heating layer. 37. The heater of claim 33, wherein said property is selected from the group consisting of thermal conductivity, resistivity, thermal emissivity, bonding, hardness, ductility, thermal expansion, porosity, chemical resistance, oxidation resistance, reduction resistance, molten metal resistance, temperature coefficient of resistivity, self-regulating heating, decorative finish, catalytic activity, sintering, reflectivity, abrasion resistance, strength, sensing capabilities, and filtering properties; and wherein said heater further comprises a thermal barrier layer, wherein said resistive heating layer is disposed between said thermal baiter layer and said substrate. 38. A method of fabricating a resistive heating layer, said method comprising the steps of:a) mixing a first material, a second material, and a third material, wherein said first material is an electrically conducting material, said second material is an electrically insulating material, and said third material alters a property of said resistive heating layer;b) thermally spraying the mixture of step (a) onto a substrate, thereby fabricating a resistive heating layer; andc) removing said resistive heating layer from said substrate.