초록

Process for preparing rigid and flexible polyurethane foams by reacting a polyisocyanate, polyols and water in the presence of a catalyst and a fire retardant which is a combination of expandable graphite and phosphorous-containing compound.

대표청구항 ▼

1. Process for preparing a rigid foam by reacting a polyisocyanate (1), an isocyanate-reactive compound (2), said compound (2) having an average equivalent weight of at most 374 and an average number of isocyanate-reactive hydrogen atoms of from 2 to 8, an isocyanate-reactive compound (3), said comp

1. Process for preparing a rigid foam by reacting a polyisocyanate (1), an isocyanate-reactive compound (2), said compound (2) having an average equivalent weight of at most 374 and an average number of isocyanate-reactive hydrogen atoms of from 2 to 8, an isocyanate-reactive compound (3), said compound (3) having an average equivalent weight of more than 374 and an average number of isocyanate-reactive hydrogen atoms of from 2 to 6 and water in the presence of a catalyst and in the presence of a fire retardant wherein the fire retardant is a combination of 1) expandable graphite and 2) phosphorous-containing compounds of formula:wherein X, Y and Z are independently selected from the groups —R and —OR′ wherein R is an alkyl, aryl or aralkyl group having 1-12 and preferably 1-10 carbon atoms, and R′ is an aryl or aralkyl group having 6-12 and preferably 6-10 carbon atoms and wherein the phosphorous-containing compounds are selected from triphenylphosphine oxide, triphenylphosphate, triphenylphosphonate and compounds having one or more, and preferably one, alkyl group(s) having 1-6 carbon atoms, attached to one or more of the aromatic rings of these triphenylphosphate, -phosphonate and -phosphine oxide. 2. The process according to claim 1, wherein the weight ratio of phosphorous-containing compounds to expandable graphite is from about 1/9 to about 4/1. 3. The process according to claim 1, wherein the combined weight of phosphorous-containing compounds and expandable graphite is 5-30%, most preferably 6-20%, by weight calculated on the total formulation. 4. Process for preparing a flexible foam by crushing the rigid foam prepared according to the process according to claim 1. 5. Isocyanate-reactive composition comprising an isocyanate-reactive compound (2), said compound (2) having an average equivalent weight of at most 374 and an average number of isocyanate-reactive hydrogen atoms of from 2 to 8, and an isocyanate-reactive compound (3), said compound (3) having an average equivalent weight of more than 374 and an average number of isocyanate-reactive hydrogen atoms of from 2 to 6, and a fire retardant wherein the fire retardant is a combination of 1) expandable graphite and 2)) phosphorous-containing compounds of formula:wherein X, Y and Z are independently selected from the groups —R and —OR′ wherein R is an alkyl, aryl or aralkyl group having 1-12 and preferably 1-10 carbon atoms, and R′ is an aryl or aralkyl group having 6-12 and preferably 6-10 carbon atoms and wherein the phosphorous-containing compounds are selected from triphenylphosphine oxide, triphenylphosphate, triphenylphosphonate and compounds having one or more, and preferably one, alkyl group(s) having 1-6 carbon atoms, attached to one or more of the aromatic rings of these triphenylphosphate, -phosphonate and -phosphine oxide.