초록 ▼

The invention is to perform operations from sealing of a honeycomb core with a thermosetting sealing material having an adhesive property to its hardening in one step, prevent a resin from flowing into cells of the honeycomb core during resin impregnating operation, and thereby mold low-cost honeyco

The invention is to perform operations from sealing of a honeycomb core with a thermosetting sealing material having an adhesive property to its hardening in one step, prevent a resin from flowing into cells of the honeycomb core during resin impregnating operation, and thereby mold low-cost honeycomb sandwich components by using RTM technique which is adopted in molding solid materials, for instance. Dry fabric sheets are stacked on both sides of a honeycomb core with thermosetting sealing members having an adhesive property placed in between, and the sealing members and the dry fabric sheets are heated at the curing temperature of the sealing members to cause initial hardening of the sealing members and to dry the dry fabric sheets. Then, the dry fabric sheets are impregnated with a thermosetting resin and the resin impregnated into the dry fabric sheets is hardened by hot-pressing an entire assembly thus prepared under specific conditions.

대표청구항 ▼

1. A method of forming a honeycomb sandwich composite panel by a resin transfer molding process consisting of:stacking a thermosetting sealing material on at least one side of a honeycomb core, said thermosetting sealing material having an adhesive property and consisting of resin film and glass mic

1. A method of forming a honeycomb sandwich composite panel by a resin transfer molding process consisting of:stacking a thermosetting sealing material on at least one side of a honeycomb core, said thermosetting sealing material having an adhesive property and consisting of resin film and glass microspheres;stacking a dry fabric on said thermosetting sealing material;hardening said sealing material by heating said sealing material and said dry fabric up to the curing temperature of said sealing material at a rate of 1° C. per minute or less and maintaining this temperature for a specified curing time period of said sealing material;impregnating said dry fabric with a thermosetting resin while varying the temperature of said sealing material and said dry fabric to a resin impregnating temperature and maintaining this temperature for a specified period of time; andhardening the resin impregnated into said dry fabric by heating said sealing material and said dry fabric to the curing temperature of said thermosetting resin and hot-pressing them for a specified period of time. 2. The method of forming a honeycomb sandwich composite panel according to claim 1, wherein:said curing temperature of said sealing material is about 120±5° C., and said specified curing time period is about 130±10 minutes. 3. The method of forming a honeycomb sandwich composite panel according to claim 1, wherein:said sealing material is laminated by a plurality of said thermosetting resin films. 4. A method of forming a honeycomb sandwich composite panel by a resin transfer molding process comprising:stacking a thermosetting sealing material having an adhesive property on at least one side of a honeycomb core, said thermosetting sealing material consisting of a plurality of epoxy resin adhesive films and a carrier material used as an adhesive film placed between said epoxy resin films;stacking a dry fabric on said thermosetting sealing material;hardening said sealing material by heating said sealing material and said dry fabric to the curing temperature of said sealing material at a rate of 1° C. per minute or less and maintaining this temperature for a specified curing time period of said sealing material;impregnating said dry fabric with a thermosetting resin while varying the temperature of said sealing material and said dry fabric to a resin impregnating temperature and maintaining this temperature for a specified period of time; andhardening the resin impregnated into said dry fabric by heating said sealing material and said dry fabric to the curing temperature of said thermosetting resin and hot-pressing them for a specified period of time. 5. The method of forming a honeycomb sandwich composite panel according to claim 4, wherein:said curing temperature of said sealing material is about 120±5° C. and said specified curing time period is about 130±10 minutes. 6. A method of forming a honeycomb sandwich composite panel by a resin transfer molding process comprising:stacking a thermosetting sealing material having an adhesive property on at least one side of a honeycomb core, said thermosetting sealing material consisting of epoxy resin adhesive films and an epoxy resin film placed between said epoxy resin films;stacking a dry fabric on said thermosetting sealing material;hardening said sealing material by heating said sealing material and said dry fabric up to the curing temperature of said sealing material at a rate of 1° C. per minute or less and maintaining this temperature for a specified curing time period of said sealing material;impregnating said dry fabric with a thermosetting resin while varying the temperature of said sealing material and said dry fabric to a resin impregnating temperature and maintaining this temperature for a specified period of time; andhardening the resin impregnated into said dry fabric by heating said sealing material and said dry fabric to the curing temperature of said th ermosetting resin and hot-pressing them for a specified period of time. 7. The method of forming a honeycomb sandwich composite panel according to claim 6, wherein:said curing temperature of said sealing material is about 120±5° C. and said specified curing time period is about 130±10 minutes. 8. A method of forming a honeycomb sandwich composite panel by a resin transfer molding process comprising:stacking a thermosetting sealing material having an adhesive property on at least one side of a honeycomb core, said thermosetting sealing material consisting of three epoxy resin adhesive films;stacking a dry fabric on said thermosetting sealing material;hardening said sealing material by heating said sealing material and said dry fabric up to the curing temperature of said sealing material at a rate of 1° C. per minute or less and maintaining this temperature for a specified curing time period of said sealing material;impregnating said dry fabric with a thermosetting resin while varying the temperature of said sealing material and said dry fabric to a resin impregnating temperature and maintaining this temperature for a specified period of time; andhardening the resin impregnated into said dry fabric by heating said sealing material and said dry fabric to the curing temperature of said thermosetting resin and hot-pressing them for a specified period of time. 9. The method of forming a honeycomb sandwich composite panel according to claim 8, wherein:said curing temperature of said sealing material is about 120±5° C. and said specified curing time period is about 130±10 minutes.