초록 ▼

In order to make weather seals from closed cell elastomer foam material, molten plastic is extruded over a substrate of the foam material. Surface reactions during extrusion are avoided by continuously pulling the substrate through an oven chamber to degas (and remove moisture from) the material at

In order to make weather seals from closed cell elastomer foam material, molten plastic is extruded over a substrate of the foam material. Surface reactions during extrusion are avoided by continuously pulling the substrate through an oven chamber to degas (and remove moisture from) the material at least on its outside to a limiting thickness of the order of 10-30 mil to form a skin or crust. The extrusion of the over-coating is carried out to form a sleeve while the substrate is still hot. Since the skin is a degassed region on the outside of the foam substrate, reactions which may cause blistering and prevent the extrusion of a smooth and firmly adhering skin are avoided. The substrate material is preferably a thermosetting EPDM rubber closed cell foam, and the over coating material is a thermoplastic elastomer (TPE).

대표청구항 ▼

1. In a method of making a weather seal having a flexible foam substrate over which a coating of plastic material is extruded while the plastic coating material is molten to provide a skin over the substrate, the improvement comprising the step of heating the substrate prior to extrusion of said mol

1. In a method of making a weather seal having a flexible foam substrate over which a coating of plastic material is extruded while the plastic coating material is molten to provide a skin over the substrate, the improvement comprising the step of heating the substrate prior to extrusion of said molten material to form a layer which is essentially unreactive with said molten skin during extrusion. 2. The method according to claim 1, wherein said heating step is carried out to provide a crust on the surface of said substrate which is essentially pore-free. 3. The method according to claim 2, wherein said crust is about 30 mil thick. 4. The method according to claim 1, wherein said heating step is carried out for sufficient time and at sufficient temperature to precure said layer of said foam on the surface thereof. 5. The method according to claim 1, wherein said foam is of thermosetting material. 6. The method according to claim 1, wherein said foam is EPDM. 7. The method according to claim 1, wherein said foam is a closed-cell elastomeric material of cylindrical shape having an outside diameter of from about 50 to 600 mils. 8. The method according to claim 7, wherein said cylinder is a tube having a wall thickness inwardly from said outside diameter from about 25 to about 300 mils. 9. The method according to claim 1, wherein said heating step is carried out to substantially outgas said foam at least in the thickness of said layer. 10. The method according to claim 9, wherein said extrusion step is carried out while said foam is still hot from the heating thereof. 11. The method according to claim 12, wherein said foam is about 200° F. during extrusion of said coating thereon. 12. The method according to claim 1, wherein said heating step is carried out by the steps comprising feeding said substrate through an extruder where said coating is applied thereto from a supply of said molten material, locating an oven upstream of said extruder, through which said substrate moves along a path over which said substrate travels to said extruder during said feeding step. 13. The method according to claim 12, wherein said heating step is carried out by the further step of forcing heated air through said oven to contact said substrate therein. 14. The method according to claim 13, wherein said heating step is carried out by the further step of maintaining a plurality of turns of said substrate lengthwise in said oven while continuously reeling said substrate through said oven. 15. The method according to claim 13, wherein said heating step further comprises providing a sufficient volume of moving heated air in said oven passing over and in contact with said substrate by blowing pressurized air from at least one manifold, said manifold and said oven having corresponding lengths, communicating said air from said manifold to said oven via a plurality of heated passageways which raise the temperature of said air to provide heated air to said oven, and permitting said air to flow continuously through said oven. 16. The method according to claim 14, wherein said reeling step is carried out by winding said plurality of turns of said substrate around pulleys at opposite ends of said oven, and driving said pulleys to reels that turn at such rate to provide sufficient dwell time in said oven for said substrate to form said crust, and further comprising the step of tensioning said substrate between one of said pulleys from which said substrate travels to said extruder and said extruder. 17. A method of making a weather seal having a substrate of closed pore elastomer foam, said substrate having a coating of thermoplastic material extruded over the substrate, which method comprises the steps of applying heat to the external surface of said substrate prior to extrusion of said coating to form a layer which is essentially unreactive on the surface of said substrate, said heating step being carried out without affecting the closed pore foam charact eristic of said substrate under said layer. 18. The method according to claim 17 wherein said thermosetting closed pore foam material is precured before said heating step is carried out.