초록 ▼

Laminates are prepared from resin-impregnated flexible graphite sheets. Impregnated sheets are calendered and layers of the calendered sheets, which may also be coated with a resin adhesive, are stacked into structures which optionally contains layers of metals or plastics. After curing at elevated

Laminates are prepared from resin-impregnated flexible graphite sheets. Impregnated sheets are calendered and layers of the calendered sheets, which may also be coated with a resin adhesive, are stacked into structures which optionally contains layers of metals or plastics. After curing at elevated temperature and pressure, 2500 psi and 150° C., the laminates form dense machinable structures suitable for uses such as electronic thermal management (ETM) devices.

대표청구항 ▼

1. A resin/graphite laminate comprising multiple sheets of resin impregnated flexible graphite cured at an elevated temperature and a pressure of from 1000 psi to 5000 psi. 2. The laminate of claim 1 wherein the resin is an epoxy. 3. The laminate of claim 1 wherein the sheets of resin impregnated gr

1. A resin/graphite laminate comprising multiple sheets of resin impregnated flexible graphite cured at an elevated temperature and a pressure of from 1000 psi to 5000 psi. 2. The laminate of claim 1 wherein the resin is an epoxy. 3. The laminate of claim 1 wherein the sheets of resin impregnated graphite are glued together with a phenolic-based adhesive prior to being pressure cured at an elevated temperature. 4. The laminate of claim 1 wherein the multiple sheets are pressure cured at a temperature of from 90° C. to 200° C. 5. The laminate of claim 1 wherein the density of the cured laminate is greater than about 1.85 g/cm 3 . 6. A resin/graphite laminate comprising layers of resin impregnated flexible graphite sheets together with layers of a non-graphite material, wherein the laminate is cured at an elevated temperature, and a pressure of from 1000 psi to 5000 psi. 7. The laminate of claim 6 wherein the resin is epoxy. 8. The laminate of claim 6 wherein the non-graphite material is selected from the group consisting of copper, aluminum and plastics. 9. The laminate of claim 6 wherein the laminate is cured at a temperature of below about 200° C. 10. An electronic thermal management device comprising a lamellar structure comprising sheets of resin impregnated flexible graphite cured at an elevated temperature and a pressure of from 1000 psi to 5000 psi. 11. The device of claim 10 wherein the lamellar structure is cured at a temperature of from 90° C. to 200° C. 12. The device of claim 10, wherein the device exhibits a thermal conductivity which is anisotropic in nature and is greater than 100 W/mC in at least one plane. 13. The device of claim 12 wherein the anisotropic thermal conductivity varies by a factor of at least 15 as between a plane with a higher thermal conductivity and a plane with lower thermal conductivity. 14. The device of claim 10 wherein the pressure cured lamellar structure has a density greater than about 1.85 g/cm 3 . 15. The electronic thermal management device of claim 10 wherein the sheets of flexible graphite have a resin content of at least about 3% by weight. 16. An anisotropic electronic thermal management device having a thermal conductivity of greater than about 300 W/mC in an in plane direction and a thermal conductivity of less than about 10 W/mC in an out of plane direction and comprising resin impregnated sheets of flexible cured at a pressure of from 1000 psi to 5000 psi. 17. The electronic thermal management device of claim 16 wherein the resin is epoxy. 18. The electronic thermal management device of claim 16 wherein the resin impregnated sheets form a lamellar structure having a density of at least 1.85 g/cm 3 . 19. The electronic thermal management device of claim 16 wherein the resin impregnated sheets of flexible graphite have been cured at an elevated temperature and pressure to form a lamellar structure. 20. The resin/graphite laminate of claim 1 wherein said resin content comprises no more than 20% by weight. 21. The resin/graphite laminate of claim 1 wherein said resin content comprises no more than 25% by weight. 22. The resin/graphite laminate of claim 1 wherein the sheets of flexible graphite have a resin content of from about 5% to about 35% by weight. 23. A resin/graphite laminate comprising multiple sheets of resin impregnated flexible graphite cured at an elevated temperature and a pressure of at least about 1000 psi. 24. The laminate of claim 23 wherein the resin is an epoxy. 25. The laminate of claim 23 wherein the sheets of resin impregnated graphite are glued together with a phenolic-based adhesive prior to being cured. 26. The laminate of claim 23 wherein the multiple sheets are pressure cured at a temperature of at least about 90° C. 27. The laminate of claim 23 wherein the density of the cured laminate is greater than about 1.85 g/cm 3 .