초록 ▼

Process for the preparation of heat-stable, antimony-free polyesters of neutral color and the products which can be prepared by this processA process for the preparation of heat-stable, antimony-free polyesters of neutral color by esterification of aromatic dicarboxylic acids or transesterification

Process for the preparation of heat-stable, antimony-free polyesters of neutral color and the products which can be prepared by this processA process for the preparation of heat-stable, antimony-free polyesters of neutral color by esterification of aromatic dicarboxylic acids or transesterification of lower aliphatic esters of aromatic dicarboxylic acids with aliphatic diols and subsequent polycondensation in which a possible transesterification is carried out in the presence of 20 to 120 ppm, based on the catalyst metal, of a transesterification catalyst, after the esterification or transesterification has ended, phosphoric acid, phosphorous acid and/or phosphonic acids or a derivative thereof are added to the esterification or transesterification batch as a completing agent in an amount which is 100% of the amount equivalent to the transesterification catalyst employed and up to 99% of the amount equivalent to the cobalt to be employed, up to 80 ppm of cobalt in the form of a cobalt compound are then added to the batch, and the polycondensation is carried out without the addition of antimony, in the presence of 1 to 10 ppm of titanium, which is added in the form of a titanium compound, and if appropriate in the presence of up to 1000 ppm of organic compounds which donate crosslinking structural groups (pentaerythritol) and if appropriate up to 50 ppm of an optical brightener, is described.The polyester obtainable by this process is furthermore described.

대표청구항 ▼

1. A process for the preparation of a heat-stable antimony free polyester of neutral color comprising the esterification of an aromatic dicarboxylic acid or transesterification of a lower alkyl ester of an aromatic dicarboxylic acid with an aliphatic diol in the presence of 20 to 120 ppm of a transe

1. A process for the preparation of a heat-stable antimony free polyester of neutral color comprising the esterification of an aromatic dicarboxylic acid or transesterification of a lower alkyl ester of an aromatic dicarboxylic acid with an aliphatic diol in the presence of 20 to 120 ppm of a transesterification metal catalyst, which is added in the form of a metal compound, and subsequent polycondensation, wherein after the esterification or transesterification has ended, a complexing agent selected from the group consisting of phosphoric acid, phosphorous acid, phosphonic acid and the esters of such acids is added in an amount which is 100% of the amount equivalent to the transesterification catalyst employed and up to 99% of the amount equivalent to cobalt to be employed, and wherein between 1 and 80 ppm of the cobalt in the form of a cobalt compound is added, and the polycondensation is carried out without the addition of antimony, in the presence of 1 to 10 ppm of titanium, which is added in the form of a titanium compound. 2. The process as claimed in claim 1, wherein, the complexing agent is added to the esterification or transesterification batch in an amount of 100% of the amount equivalent to the transesterification catalyst employed and 90 to 99% of the amount equivalent to the cobalt to be employed. 3. The process as claimed in claim 1, wherein a melt is formed during the polycondensation which is carried out in the presence of 1 to 10 ppm of titanium up to an intrinsic viscosity, measured in dichloroacetic acid at 25° C., of 0.4 to 0.9 dl/g and up to a carboxyl group concentration of 10 to 50 mmol/kg in the melt, and then wherein the polycondensation is continued up to the desired end viscosity in the solid phase. 4. The process as claimed in claim 1, wherein 20 to 40 ppm of cobalt in the form of a cobalt compound is added to the batch. 5. The process as claimed in claim 1, wherein the polycondensation is carried out in the presence of 2-8 ppm of titanium. 6. The process claimed in claim 1, wherein the polycondensation is carried out in the presence of 100 to 500 ppm of organic crosslinking agents. 7. The process as claimed in claim 1, wherein the polycondensation is carried out in the presence of up to 25 ppm of an optical brightener. 8. A heat-stable, antimony-free polyester of neutral color based on an aromatic dicarboxylic acid and an aliphatic diol, prepared by the process as claimed in claim 1, in which, in the non-matted state, its color number components area* in the range from −3 to +3,b* in the range from −6 to +6 andL* in the range from 55 to 75. 9. A heat-stable, antimony-free polyester of neutral color based on an aromatic dicarboxylic acid and an aliphatic diol as claimed in claim 8, which comprises 1 to 10 ppm of titanium, 20 to 120 ppm of a transesterification catalyst metal in the form of catalytically inactive complexes with a complexing agent selected from the group consisting of phosphoric acid, phosphorous acid, phosphonic acid and the esters of such acids, and 0 to 80 ppm of cobalt, which is partly present in the form of catalytically inactive complexes with a complexing agent selected from the group consisting of phosphoric acid, phosphorous acid, phosphonic acid and derivatives thereof. 10. A heat-stable, antimony-free polyester of neutral color as claimed in claim 8, which comprises 2 to 8 ppm of titanium, 50 to 90 ppm of manganese in the form of catalytically inactive complexes with a complexing agent selected from the group consisting of phosphoric acid, phosphorous acid, phosphonic acid and the esters of such acids, and 20 to 40 ppm of cobalt, which is partly present in the form of catalytically inactive complexes with a complexing agent selected from the group consisting of phosphoric acid, phosphorous acid, phosphonic acid and derivatives thereof. 11. A heat-stabled, antimony-free polyester of neutral color as claimed in claim 8, in which, in the non-matted state, its color number components area* in the range from −2 to +2,b* in the range from −3.5 to +3.5 andL* in the range from 60 to 70. 12. A heat-stable, antimony-free polyester of neutral color as claimed in claim 8, in which 90 to 99% of the cobalt is in the form of one or more catalytically inactive complexes with a complexing agent selected from the group consisting of phosphoric acid, phosphorous acid, phosphonic acid and the esters of such acids. 13. A heat stable, antimony-free polyester of neutral color as claimed in claim 8, which comprises 5 to 25 ppm of an optical brightener. 14. A heat-stable, antimony-free polyester of neutral color as claimed in claim 8, in which the catalytically inactive complexes of manganese and of cobalt are complexes with phosphorous acid or an ester thereof. 15. A heat-stable, antimony-free polyester of neutral color as claimed in claim 8, which further comprises up to 1000 ppm of crosslinking structural groups. 16. The process as claimed in claim 1, wherein the transesterification catalyst is manganese in the form of a manganese compound. 17. The process as claimed in claim 1, wherein the polycondensation is carried out in the presence of up to 1000 ppm of organic crosslinking agents. 18. The process as claimed in claim 1, wherein the polycondensation is carried out in the presence of up to 50 ppm of an optical brightener. 19. The process as claimed in claim 3, wherein the end viscosity of the heat-stable antimony-free polyester is 0.7 to 2.0 dl/g, measured in dichloroacetic acid at 25° C. 20. A heat-stable, antimony-free polyester of neutral color as claimed in claim 9, which further comprises up to 50 ppm of an optical brightener. 21. A heat-stable, antimony-free polyester of neutral color as claimed in claim 10, which further comprises up to 25 ppm of an optical brightener. 22. The process as claimed in claim 1, wherein the titanium compound is potassium titanyloxalate.