Low-boron glass fibers and glass compositions for making the same
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C03C-003/112
C03C-013/06
출원번호
US-0010531
(2001-12-05)
발명자
/ 주소
Sircar, Anup
출원인 / 주소
Evanite Fiber Corporation
대리인 / 주소
Klarquist Sparkman, LLP
인용정보
피인용 횟수 :
13인용 특허 :
22
초록▼
Low-boron, high-barium glass compositions and fine-diameter glass fibers for forming clean room HEPA and ULPA filters, are provided. The compositions and resulting glass fibers preferably comprise a low concentration, less than about 1 weight percent, of boric oxide, a relatively high concentration
Low-boron, high-barium glass compositions and fine-diameter glass fibers for forming clean room HEPA and ULPA filters, are provided. The compositions and resulting glass fibers preferably comprise a low concentration, less than about 1 weight percent, of boric oxide, a relatively high concentration of barium, such as from about 5.5 to about 18 weight percent barium oxide, and a concentration of alkali oxide ranging from about 10 to about 14.5 weight percent. Alumina is preferably present in the glass fiber compositions and the resulting glass fibers in a range of from about 4 weight percent to about 8 weight percent, and calcium oxide and magnesium oxide are preferably present in a range of from about 1 weight percent to about 6 weight percent and from about 0 weight percent to about 3.5 weight percent, respectively. The glass fiber compositions also preferably include from about 2 to about 6 weight percent zinc oxide, from about 0.1 to about 1.5 weight percent fluorine, and very low concentrations of manganese oxide, ferric oxide and various impurities such as strontium oxide, lithium oxide, titanium oxide, and zirconium oxide. Preferably, the balance of the composition is silicon dioxide.
대표청구항▼
1. A low-boron, high-barium concentration glass fiber composition comprising:less than about 1 weight percent boron;from about 5.5 to about 18 weight percent barium oxide;from about 10 to about 14.5 weight percent alkali metal oxide;from about 4 to about 8 weight percent alumina;from about 1 to abou
1. A low-boron, high-barium concentration glass fiber composition comprising:less than about 1 weight percent boron;from about 5.5 to about 18 weight percent barium oxide;from about 10 to about 14.5 weight percent alkali metal oxide;from about 4 to about 8 weight percent alumina;from about 1 to about 9 weight percent alkaline earth oxide, excluding barium oxide;from about 2 to about 6 weight percent zinc oxide;from about 0.1 to about 1.5 weight percent fluorine; anda balance of the glass fiber composition being silica. 2. The glass fiber composition of claim 1, wherein the boron is present as B 2 O 3 , alkali metal oxide is present as Na 2 O or K 2 O, and alkaline earth oxide is present as GaO or MgO. 3. The glass fiber composition of claim 1, wherein the alkali oxide is present as Na 2 O and K 2 O and alkaline earth oxide is present as CaO and MgO. 4. The glass fiber composition of claim 1, further comprising less than about 0.2 weight percent of one or more compounds selected from the group consisting of MnO, SrO, Li 2 O, TiO 2 , ZrO 2 and Fe 2 O 3 . 5. A low-boron, high-barium glass fiber composition comprising:less than about 1 weight percent of boric oxide;from about 6 to about 16 weight percent barium oxide;from about 10 to about 12.5 weight percent of alkali metal oxide;from about 5 to about 6 weight percent of alumina oxide;from about 1 to about 9 weight percent alkaline earth oxide, excluding barium oxide;from about 2 to about 5 weight percent zinc oxide;from about 0.1 to about 1.0 weight percent fluorine; anda balance of the composition being silica. 6. The glass fiber composition of claim 5, wherein the glass fiber composition forms glass fibers having an average diameter of from about 0.1 μm to about 3.0 μm. 7. The glass fiber composition of claim 5, wherein boron is present as B 2 O 3 , alkali metal oxide is present as Na 2 O and K 2 O, and alkaline earth oxide is present as CaO and MgO. 8. The glass fiber composition of claim 5, further comprising less than about 0.2 weight percent of one or more compounds selected from the group consisting of MnO, SrO, Li 2 O, TiO 2 , ZrO 2 , and Fe 2 O 3 . 9. A low-boron, high-barium glass fiber composition comprising:less than about 1 weight percent of boron;from about 6 to about 16 weight percent barium oxide;from about 10 to about 12.5 weight percent of alkali metal oxide;from about 5 to about 6 weight percent of alumina oxide;from about 1 to about 9 weight percent alkaline earth oxide, excluding barium oxide;from about 2 to about 5 weight percent zinc oxide;from about 0.1 to about 1.0 weight percent fluorine;a balance of the composition being silica; andwherein the glass fiber composition forms glass fibers having an average diameter of from about 0.1 μm to about 8.15 μm. 10. The glass fiber composition of claim 9, wherein the glass fibers have an average diameter of from about 0.1 μm to about 3.0 μm.
Hyre Jon (5738 Camp Bowie Blvd. Forth Worth TX 76107), Ignition device and apparatus for filtering and purifying side-stream and second-hand tobacco smoke.
Battigelli Jean A. (Rantigny FRX) Bouquet Francois (Rantigny FRX) Fezenko Igor (Aubervilliers FRX) Massol Jean-Jacques (Asnieres FRX), Method for centrifugal fiberization of hard glass.
McGinnis, Peter B.; Hofmann, Douglas; Baker, David J.; Wingert, John W.; Bemis, Byron, Method of manufacturing S-glass fibers in a direct melt operation and products formed therefrom.
McGinnis, Peter Bernard; Hofmann, Douglas; Baker, David J.; Wingert, John W.; Bemis, Byron, Method of manufacturing high strength glass fibers in a direct melt operation and products formed there from.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.