초록 ▼

An electrode comprising a noble-metal free grid comprising lead, wherein the grid has an essentially PbO free PbO2coating covering all, or essentially all of the surface of the grid. Also described is a method of forming an electrode, comprising applying an essentially PbO free PbO2coating to a nobl

An electrode comprising a noble-metal free grid comprising lead, wherein the grid has an essentially PbO free PbO2coating covering all, or essentially all of the surface of the grid. Also described is a method of forming an electrode, comprising applying an essentially PbO free PbO2coating to a noble-metal free grid comprising lead, wherein the coating covers all, or essentially all of the surface of the grid.

대표청구항 ▼

1. An electrode comprising: a noble-metal free grid comprising lead, wherein said grid has an essentially PbO free PbO 2coating essentially covering the surface of said grid, wherein the surface area of said essentially PbO free PbO2coating exceeds the geometric surface area of said grid by more tha

1. An electrode comprising: a noble-metal free grid comprising lead, wherein said grid has an essentially PbO free PbO 2coating essentially covering the surface of said grid, wherein the surface area of said essentially PbO free PbO2coating exceeds the geometric surface area of said grid by more than about 60 area percent. 2. The electrode of claim 1, wherein said noble metal free grid further comprises calcium, tin, or a combination comprising at least one of the foregoing. 3. The electrode of claim 1, wherein said essentially PbO free PbO2coating comprises at least about 90 weight percent alpha-PbO2. 4. The electrode of claim 1, wherein said essentially PbO free PbO2coating comprises at least about 90 weight percent beta-PbO2. 5. The electrode of claim 1, wherein said essentially PbO free PbO2coating has an effective surface area greater than the geometric surface area of said grid. 6. The electrode of claim 1, wherein said essentially PbO free PbO2coating covers in excess of 99 area percent of the geometric surface area of said grid. 7. The electrode of claim 1, wherein said essentially PbO free PbO2coating covers in excess of 99.9% of the geometric surface area of said grid. 8. The electrode of claim 1, wherein said essentially PbO free PbO2coating has an average thickness of at least about 5 microns. 9. The electrode of claim 8, wherein said essentially PbO free PbO2coating has an average thickness of at most about 500 microns. 10. The electrode of claim 1, wherein said essentially PbO free PbO2coating has an average thickness of at least about 10 microns. 11. The electrode of claim 10, wherein said essentially PbO free PbO2coating has an average thickness of at most about 250 microns. 12. The electrode of claim 1, wherein said essentially PbO free PbO2coating has an average thickness of at least about 15 microns. 13. The electrode of claim 12, wherein said essentially PbO free PbO2coating has an average thickness of at most about 50 microns. 14. The electrode of claim 1, wherein said essentially PbO free PbO2coating has a density greater than about 8.5 grams per cubic centimeter. 15. The electrode of claim 1, wherein a cross-section of said electrode taken perpendicular to the surface of said coating comprises a continuous, or an essentially continuous interface at the boundary between said coating and said grid; wherein said essentially continuous interface is defined as being continuous on average at least about 1 micron at 80 times magnification. 16. The electrode of claim 15, wherein said essentially continuous interface is continuous on average at least about 5 microns at 80 times magnification. 17. The electrode of claim 16, wherein said essentially continuous interface is continuous on average at least about 15 microns at 80 times magnification. 18. The electrode of claim 1, wherein said coating has a percent void area at an interface between said coating and said grid less than about 50 area percent of the total area of said interface. 19. The electrode of claim 1, wherein said coating has a percent void area at an interface between said coating and said grid less than about 30 area percent of the total area of said interface. 20. The electrode of claim 1, wherein said coating has a percent void area at an interface between said coating and said grid less than about 10 area percent of the total area of said interface. 21. A method of making a battery comprising: introducing at least two electrodes into an outer case; and surrounding said electrodes with an electrolyte, wherein at least one of said electrodes is the electrode of claim 1. 22. A method of forming an electrode, comprising: applying an essentially PbO free PbO 2coating to the surface of a noble-metal free grid comprising lead, wherein said coating essentially covers the surface of said grid, and wherein the surface area of said essentially PbO free PbO2coating exceeds the geometric surface area of said grid by more than about 60 area percent. 23. T he method of claim 22, wherein said coating is applied to said grid by electrolytic deposition, non-electrolytic deposition, or a combination comprising at least one of the foregoing. 24. The method of claim 22, wherein said noble metal free grid further comprises calcium, tin, or a combination comprising at least one of the foregoing. 25. The method of claim 22, wherein said essentially PbO free PbO2coating comprises at least about 90 weight percent alpha-PbO2. 26. The method of claim 22, wherein said essentially PbO free PbO2coating comprises at least about 90 weight percent beta-PbO2. 27. The method of claim 22, wherein said essentially PbO free PbO2 coating has an effective surface area greater than the geometric surface area of said grid. 28. The method of claim 22, wherein said essentially PbO free PbO2coating covers in excess of 99 area percent of the geometric surface area of said grid. 29. The method of claim 22, wherein said essentially PbO free PbO2coating covers in excess of 99 area percent of the geometric surface area of said grid. 30. The method of claim 22, wherein said essentially PbO free PbO2coating has an average thickness of at least about 5 microns. 31. The method of claim 30, wherein said essentially PbO free PbO2coating has an average thickness of at most about 500 microns. 32. The method of claim 22, wherein said essentially PbO free PbO2coating has an average thickness of at least about 10 microns. 33. The method of claim 32, wherein said essentially PbO free PbO2coating has an average thickness of at most about 250 microns. 34. The method of claim 22, wherein said essentially PbO free PbO2coating has an average thickness of at least about 15 microns. 35. The method of claim 34, wherein said essentially PbO free PbO2coating has an average thickness of at most about 50 microns. 36. The method of claim 22, wherein said essentially PbO free PbO2coating has a density greater than about 8.5 grams per cubic centimeter. 37. The method of claim 22, wherein a cross-section of said electrode taken perpendicular to the surface of said coating comprises a continuous, or an essentially continuous interface at the boundary between said coating and said grid; wherein said essentially continuous interface is defined as being continuous on average at least about 1 micron at 80 times magnification. 38. The method of claim 37, wherein said essentially continuous interface is continuous on average at least about 5 microns at 80 times magnification. 39. The method of claim 37, wherein said essentially continuous interface is continuous on average at least about 15 microns at 80 times magnification. 40. The method of claim 22, wherein said coating has a percent void area at an interface between said coating and said grid less than about 50 area percent of the total area of said interface. 41. The method of claim 22, wherein said coating has a percent void area at an interface between said coating and said grid less than about 30 area percent of the total area of said interface. 42. The method of claim 22, wherein said coating has a percent void area at an interface between said coating and said grid less than about 10 area percent of the total area of said interface. 43. A method of forming an electrode, comprising: electrolytically depositing an essentially PbO free PbO 2coating onto the surface of a noble-metal free grid comprising lead, tin and calcium, wherein said coating has a thickness not less than 5 microns and not more than 500 microns, and wherein said coating covers all, or essentially all of the surface of said grid to produce a coated grid; applying a paste comprising lead and lead oxide to the surface of said coated grid to produce a pasted grid; contacting said pasted grid with steam for at least one hour to produce a steamed grid; curing said steamed grid at about 50 percent humidity and about 55° C. for at least about 24 hours to produce a cured grid; followed by contacting said grid with aqueous sulf uric acid prior to passing an external electric current of sufficient voltage and amperage through said cured grid for a sufficient period of time to convert at least a portion of said applied paste into lead dioxide. 44. A battery comprising: at least two electrodes disposed in an outer case and surrounded by an electrolyte, wherein at least one of said electrodes is the electrode of claim 43. 45. A method of making a battery comprising: introducing at least two electrodes into an outer case; and surrounding said electrodes with an electrolyte, wherein at least one of said electrodes is the electrode of claim 43.