초록 ▼

Disclosed are adhesive formulations as creping process aids for producing an absorbent creped cellulosic sheet having a high level of surface-perceived softness that comprises continuously forming a web of cellulosic papermaking fibers, adhering said web to a thermal drying means by means of adhesiv

Disclosed are adhesive formulations as creping process aids for producing an absorbent creped cellulosic sheet having a high level of surface-perceived softness that comprises continuously forming a web of cellulosic papermaking fibers, adhering said web to a thermal drying means by means of adhesive compositions comprising polymers having at least one primary or secondary amine group in the backbone such as chitosan, plolyvinylamine, polyvinyl alcohol-vinyl amine and polyaminoamide in combination with crosslinking agents such as zirconium compounds having a valence of plus four including ammonium zirconium carbonate, zirconium acetylacetonate, zirconium acetate, zirconium carbonate, zirconium sulfate, zirconium phosphate, potassium zirconium carbonate, zirconium sodium phosphate and sodium zirconium tartrate and creping said treated web from said thermal drying means. In the method for producing the absorbent creped cellulosic sheets, the zirconium crosslinking agent is advantageously applied directly and separately on the Yankee dryer at the time the base polymer is applied to the surface. The crosslinking agent functions to crosslink the polymer to the fibrous web. The absorbent paper products are used as bathroom tissue and towels.

대표청구항 ▼

1. An adhesive composition comprising an organic polymer having in the polymer backbone amine groups selected from the group consisting of primary and secondary amine groups and mixtures thereof and a crosslinking agent for crosslinking the polymer to a fibrous web, said agent being selected from zi

1. An adhesive composition comprising an organic polymer having in the polymer backbone amine groups selected from the group consisting of primary and secondary amine groups and mixtures thereof and a crosslinking agent for crosslinking the polymer to a fibrous web, said agent being selected from zirconium compounds wherein the zirconium has a valence of plus four, wherein the composition is a releasable adhesive. 2. An adhesive composition as claimed in claim 1 characterized in that the organic polymer is selected from the group consisting of chitosan, polyvinylamine, polyvinyl alcohol-vinyl amine and polyaminoamide. 3. An adhesive composition as claimed in claim 1 or claim 2 characterized in that the crosslinking agent is a zirconium compound selected from the group consisting of ammonium zirconium carbonate, zirconium acetylacetonate, zirconium acetate, zirconium carbonate, zirconium sulfate, zirconium phosphate, potassium zirconium carbonate, zirconium sodium phosphate and sodium zirconium tartrate. 4. An adhesive composition as claimed in claim 3 characterized in that the organic polymer is selected from the group consisting of polyvinyl alcohol-vinyl amine copolymers of the following structure:wherein m and n have values of 1 to 99 and 99 to 1 respectively. 5. The adhesive composition of claim 4 wherein m and n have values of 1 to 99 and 2 to 20 respectively. 6. The adhesive composition of claim 1 or claim 2 wherein the crosslinking agent is ammonium zirconium carbonate. 7. An adhesive composition as claimed in claim 6 characterized in that the organic polymer is selected from the group consisting of polyvinyl alcohol-vinyl amine copolymers of the following structure:wherein m and n have values of 1 to 99 and 99 to 1 respectively. 8. The adhesive composition of claim 7 wherein m and n have values of 1 to 99 and 2 to 20 respectively. 9. An adhesive composition as claimed in claim 1 wherein the organic polymer is dissolved in water to create a solution, wherein the solution has a liquid component and a solid component and the liquid component is about 90 to about 99% by weight of said solution. 10. An adhesive composition as claimed in claim 1 wherein the weight ratio of the zirconium crosslinking agent to the organic polymer is about 4:1. 11. An adhesive composition as claimed in claim 1 wherein the weight ratio of the zirconium crosslinking agent to the organic polymer is about 0.05:1 to about 2:1. 12. The adhesive composition of claim 1 wherein the adhesive composition, when adhered to a Yankee dryer, exhibits a peel force of about 300 to about 900 grams per 12 inches of fibrous web when using a papermaking machine having a speed of less than 150 feet per minute. 13. The adhesive composition of claim 1 wherein said composition is sprayable. 14. The adhesive composition of claim 1 or claim 2 wherein the crosslinking agent is potassium zirconium carbonate.