초록 ▼

The present invention is directed to ion-sensitive, water-dispersible polymers. The present invention is also directed to a method of making ion-sensitive, water-dispersible polymers and their applicability as binder compositions. The present invention is further directed to fiber-containing fabrics

The present invention is directed to ion-sensitive, water-dispersible polymers. The present invention is also directed to a method of making ion-sensitive, water-dispersible polymers and their applicability as binder compositions. The present invention is further directed to fiber-containing fabrics and webs comprising ion-sensitive, water-dispersible binder compositions and their applicability in water-dispersible personal care products.

대표청구항 ▼

1. An ion-sensitive polymer formulation comprising a first polymer formed from three monomers: acrylic acid, butyl acrylate, and 2-ethylhexyl acrylate and a second polymer comprising a non-crosslinking poly(ethylene-vinyl acetate); wherein the polymer formulation is insoluble in a neutral salt solut

1. An ion-sensitive polymer formulation comprising a first polymer formed from three monomers: acrylic acid, butyl acrylate, and 2-ethylhexyl acrylate and a second polymer comprising a non-crosslinking poly(ethylene-vinyl acetate); wherein the polymer formulation is insoluble in a neutral salt solution containing at least about 0.3 weight percent salt, said salt comprising one or more monovalent ions; and wherein the polymer formulation is dispersible in water containing less than about 10 ppm of one or more multivalent ions. 2. The ion-sensitive polymer formulation of claim 1, wherein the first polymer is formed from a mixture comprising from about 35 to less than 80 mole percent acrylic acid; from greater than 0 to about 65 mole percent butyl acrylate; and from greater than 0 to about 45 mole percent 2-ethylhexyl acrylate. 3. The ion-sensitive polymer formulation of claim 1, wherein the first polymer is formed from a mixture comprising from about 50 to less than 67 mole percent acrylic acid; from about 15 to about 28 mole percent butyl acrylate; and from about 7 to about 15 mole percent 2-ethylhexyl acrylate. 4. The ion-sensitive polymer of claim 1, wherein the first polymer is formed from a mixture comprising from about 57 to less than 66 mole percent acrylic acid; from about 15 to about 28 mole percent butyl acrylate; and from about 7 to about 13 mole percent 2-ethylhexyl acrylate. 5. The ion-sensitive polymer formulation of claim 1, wherein the polymer formulation comprises from about 25 to about 35 weight percent non-crosslinking poly(ethylene-vinyl acetate). 6. The ion-sensitive polymer formulation of claim 1, wherein the polymer formulation comprises from about 1 to about 45 weight percent non-crosslinking poly(ethylene-vinyl acetate). 7. The ion-sensitive polymer formulation of claim 1, wherein the first polymer is formed from a mixture comprising from about 57 to less than 66 mole percent acrylic acid; from about 15 to about 28 mole percent butyl acrylate; and from about 7 to about 13 mole percent 2-ethylhexyl acrylate; and wherein the polymer formulation comprises from about 65 to about 75 mole percent of the first polymer and from about 25 to about 35 weight percent of the second polymer. 8. A binder composition for binding fibrous material into an integral web, said binder composition comprising the ion-sensitive polymer formulation of claim 1. 9. A method of making an ion-sensitive polymer formulation comprising combining an acrylic acid terpolymer and a non-crosslinking poly(ethylene-vinyl acetate), wherein the polymer formulation in insoluble in a neutral salt solution containing at least about 0.3 weight percent salt, said salt comprising one or more monovalent ions; and wherein the polymer formulation is dispersible in water containing less than about 10 ppm of one or more multivalent ions, wherein the acrylic acid terpolymer is formed from three monomers: acrylic acid, butyl acrylate, and 2-ethylhexyl acrylate. 10. The method of claim 9, wherein the acrylic acid terpolymer is formed from a mixture comprising from about 35 to less than 80 mole percent acrylic acid; from greater than 0 to about 65 mole percent butyl acrylate; and from greater than 0 to about 45 mole percent 2-ethylhexyl acrylate. 11. The method of claim 9, wherein the acrylic acid terpolymer is formed from a mixture comprising from about 50 to less than 67 mole percent acrylic acid; from about 15 to about 28 mole percent butyl acrylate; and from about 7 to about 15 mole percent 2-ethylhexyl acrylate. 12. The method of claim 9, wherein the acrylic acid terpolymer is formed from a mixture comprising from about 57 to less than 66 mole percent acrylic acid; from about 15 to about 28 mole percent butyl acrylate; and from about 7 to about 13 mole percent 2-ethylhexyl acrylate. 13. The method of claim 9, wherein the polymer formulation comprises from about 65 to about 75 weight percent of the acrylic acid terpolymer. 14. The method of claim 9, where in the polymer formulation comprises from about 25 to about 35 weight percent of the non-crosslinking poly(ethylene-vinyl acetate). 15. The method of claim 9, wherein the polymer formulation comprises from about 1 to about 45 weight percent of the non-crosslinking poly(ethylene-vinyl acetate). 16. The method of claim 9, wherein the acrylic acid terpolymer is formed from a mixture comprising from about 57 to less than 66 mole percent acrylic acid; from about 15 to about 28 mole percent butyl acrylate; and from about 7 to about 13 mole percent 2-ethylhexyl acrylate; and wherein the polymer formulation comprises from about 65 to about 75 weight percent of the acrylic acid terpolymer and the polymer formulation comprises from about 25 to about 35 weight percent of the non-crosslinking poly(ethylene-vinyl acetate).