초록 ▼

Method of producing a composite nonwoven for receiving and storing liquids or the like, comprising a carded nonwoven, which is treated in order to consolidate it, and a pulp layer, such as a wood pulp fiber layer, applied to the consolidated carded nonwoven and brought into secure contact with same,

Method of producing a composite nonwoven for receiving and storing liquids or the like, comprising a carded nonwoven, which is treated in order to consolidate it, and a pulp layer, such as a wood pulp fiber layer, applied to the consolidated carded nonwoven and brought into secure contact with same, characterized in that the carded nonwoven is consolidated dry before being coated with the super-absorbent material, then the layer formed from the pulp fibers is applied to this pre-consolidated carded nonwoven and everything is interconnected.

대표청구항 ▼

1. Method of producing a composite nonwoven for receiving and storing liquids comprising the steps of:forming a carded nonwoven; pre-consolidating the carded nonwoven in order to consolidate it in a dry state with only light bonding of fibers of the carded nonwoven; applying a layer of pulp fibers t

1. Method of producing a composite nonwoven for receiving and storing liquids comprising the steps of:forming a carded nonwoven; pre-consolidating the carded nonwoven in order to consolidate it in a dry state with only light bonding of fibers of the carded nonwoven; applying a layer of pulp fibers to pre-consolidated carded nonwoven; and interconnecting the layer of pulp fibers and the pre-consolidated carded nonwoven. 2. Method according to claim 1, characterised in that the step of pre-consolidating is carried out by means of compressed air.3. Method according to claim 1, characterised in that the step of pre-consolidating is produced by calendering.4. Method according to claim 1, characterised in that the step of interconnecting the pulp fibers to the pre-consolidated carded nonwoven comprises hydrodynamic needling the layer of pulp fibers and the pre-consolidated carded nonwoven and drying the composite nonwoven.5. Method according to claim 1, further comprising applying a third layer of carded fibers as a cover layer to the layer of pulp fibers, and the step of interconnecting the layer of pulp fibers and the pre-consolidated carded nonwoven comprises hydrodynamic needling the third layer, the layer of pulp fibers and the pre-consolidated carded nonwoven for connection purposes.6. Method according to claim 4, further comprising calendaring the dried composite nonwoven.7. Method according to claim 1, characterised in that the pulp fibers comprise wood pulp fibers.8. Method according to claim 3, characterised in that the calendaring is conducted with a nip pressure less than 90 N/mm.9. Method according to claim 8, characterised in that the calendaring is conducted with a temperature of the calendaring rollers 5-10% below a melting temperature of fibers in the carded nonwoven.10. Method according to claim 3, characterised in that the calendaring takes place over a contact surface of 10-30% of calendaring rolls.11. Method according to claim 1, characterised in that the steps are carried out in a continuous plant.12. A composite nonwoven for receiving and storing liquids produced by the method of claim 1.13. A composite nonwoven for receiving and storing liquids produced by the method of claim 5.