초록 ▼

The invention relates to a catalyst composition, a method of making the same and its use in the conversion of a feedstock, preferably an oxygenated feedstock, into one or more olefin(s), preferably ethylene and/or propylene. The catalyst composition comprises a molecular sieve and at least one oxide

The invention relates to a catalyst composition, a method of making the same and its use in the conversion of a feedstock, preferably an oxygenated feedstock, into one or more olefin(s), preferably ethylene and/or propylene. The catalyst composition comprises a molecular sieve and at least one oxide of a metal from Group 4, optionally in combination with at least one metal from Groups 2 and 3, of the Periodic Table of Elements.

대표청구항 ▼

1. A catalyst composition comprising a molecular sieve and at least one oxide of a metal selected from Group 4 of the Periodic Table of Elements, wherein said metal oxide has an uptake of carbon dioxide at 100° C. of at least 0.03 mg/m2 of the metal oxide.2. The catalyst composition of claim 1 where

1. A catalyst composition comprising a molecular sieve and at least one oxide of a metal selected from Group 4 of the Periodic Table of Elements, wherein said metal oxide has an uptake of carbon dioxide at 100° C. of at least 0.03 mg/m2 of the metal oxide.2. The catalyst composition of claim 1 wherein said metal oxide has an uptake of carbon dioxide at 100° C. of at least 0.035 mg/m2 of the metal oxide.3. The catalyst composition of claim 1 wherein said metal oxide has an uptake of carbon dioxide at 100° C. of less than 10 mg/m2 of the metal oxide.4. The catalyst composition of claim 1 wherein said metal oxide has an uptake of carbon dioxide at 100° C. of less than 5 mg/m2 of the metal oxide.5. The catalyst composition of claim 1 and also including at least one of a binder and a matrix material different from said metal oxide.6. The catalyst composition of claim 1 wherein said metal oxide has a surface area greater than 10 m2/g.7. The catalyst composition of claim 1 and also including a binder and a matrix material each being different from one another and from said metal oxide.8. The catalyst composition of claim 7 wherein the binder is an alumina sol and the matrix material is a clay.9. The catalyst composition of claim 1 wherein said metal oxide is selected from zirconium oxide and hafnium oxide.10. The catalyst composition of claim 1 and also including an oxide of a metal selected from Group 2 and Group 3 of the Periodic Table of Elements.11. The catalyst composition of claim 10 wherein the Group 4 metal oxide comprises zirconium oxide and the Group 2 and/or Group 3 metal oxide comprises one or more oxides selected from the group consisting of calcium oxide, barium oxide, lanthanum oxide, yttrium oxide and scandium oxide.12. The catalyst composition of claim 1 wherein the molecular sieve comprises a framework inciuding at least two tetrahedral units selected from [SiO4], [AlO4] and [P04] units.13. The catalyst composition of claim 12 wherein the molecular sieve comprises a silicoaluminophosphate.14. The catalyst composition of claim 12 wherein the molecular sieve comprises a CHA framework-type molecular sieve.15. The catalyst composition of claim 14 wherein the molecular sieve further comprises an AEI framework-type molecular sieve.16. The catalyst composition of claim 1 wherein the weight ratio of the molecular sieve to metal oxide is in the range of from 5 percent to 800 percent.17. A molecular sieve catalyst composition comprising an active Group 4 metal oxide and a Group 2 and/or a Group 3 metal oxide, a binder, a matrix material, and a silicoaluminophosphate molecular sieve.18. A method for making a catalyst composition, the method comprising physically mixing first particles comprising a molecular sieve with second particles comprising a Group 4 metal oxide having an uptake of carbon dioxide at 100° C. of at least 0.03 mg/m2 of the metal oxide particles.19. The method of claim 18 wherein said second particles have a surface area greater than 10 m2/g.20. The method of claim 18 wherein said second particles have a surface area greater than 15 m2/g.21. The method of claim 18 wherein said first particles comprise a silicoaluminophosphate molecular sieve and/or an aluminophosphate molecular sieve.22. The method of claim 18 wherein at least one said first and said second particles also include at least one of a binder and a matrix material.23. The method of claim 18 wherein said first particles comprise a silicoaluminophosphate molecular sieve, a binder including an alumina sol and a matrix material including a clay.24. The method of claim 18 wherein said second particles also comprise a Group 2 and/or Group 3 metal oxide.25. The method of claim 18 wherein said second particles comprise zirconium oxide and at least one of calcium oxide, barium oxide, lanthanum oxide, yttrium oxide and scandium oxide.26. A method of making a catalyst composition, the method comprising:(i) synthesizing a molecular sieve from a reaction mixture comprising at least one templating agent and at least two of a silicon source, a phosphorus source and an aluminum source; and (ii) recovering the molecular sieve synthesized in (i); (iii) forming a hydrated precursor of a Group 4 metal oxide by precipitation from a solution containing a source of Group 4 metal ions; (iv) recovering the hydrated precursor formed in (iii); (v) calcining the hydrated precursor recovered (iv) to form a calcined Group 4 metal oxide that has an uptake of carbon dioxide at 100° C. of at least 0.03 mg/m2 of the metal oxide; and (vi) physically mixing the molecular sieve recovered in (i) and the calcined metal oxide produced in (v). 27. The method of claim 26 wherein the molecular sieve and/or the Group 4 metal oxide is combined with a binder and/or a matrix material prior to (vi).28. The method of claim 26 wherein the weight ratio of the molecular sieve to the calcined metal oxide is in the range of from 30 percent to 400 percent.29. The method of claim 26 wherein the calcined metal oxide has a surface area greater than 10 m2/g.30. The method of claim 26 wherein the molecular sieve is spray dried with a matrix material and a binder prior to (vi).31. The method of claim 30 wherein the molecular sieve is a silicoaluminophosphate, the binder is an alumina sol and the matrix material is a clay.32. The method of claim 26 wherein a mixed metal oxide is produced in (iii) by precipitation from at least one solution containing a Group 4 metal oxide precursor and at least one of a Group 2 metal oxide precursor and a Group 3 metal oxide precursor.33. The method of claim 26 wherein said precipitation is conducted at a pH above 7.34. The method of claim 26 wherein (iii) also includes hydrothermally treating the precipitate at a temperature of at least 80° C. for up to 10 days.35. The method of claim 26 wherein (v) is conducted at a temperature in the range of from about 400° C. to about 900° C.