NOx reduction catalyst and NOx reduction system
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
B01J-023/02
B01J-023/58
B01J-023/63
출원번호
US-0077791
(2002-02-20)
우선권정보
JP-0069384 (2001-03-12)
발명자
/ 주소
Nakamura, Masanori
Suga, Katsuo
출원인 / 주소
Nissan Motor Co., Ltd.
대리인 / 주소
Foley &
인용정보
피인용 횟수 :
9인용 특허 :
10
초록▼
A NOx reduction catalyst for exhaust gas discharged from an automotive internal combustion engine operable in a lean region and in a range including a stoichiometric region and a rich region. The NOx reduction catalyst comprises a catalytic noble metal. Additionally, an oxygen adsorbable and releasa
A NOx reduction catalyst for exhaust gas discharged from an automotive internal combustion engine operable in a lean region and in a range including a stoichiometric region and a rich region. The NOx reduction catalyst comprises a catalytic noble metal. Additionally, an oxygen adsorbable and releasable material is provided carrying at least a part of the catalytic noble metal. In this catalyst, the catalytic noble metal carried on the oxygen adsorbable and releasable material adsorbs SOx in the exhaust gas, in a form of at least one of sulfate and sulfite.
대표청구항▼
1. A NOx reduction catalyst for exhaust gas discharged from a combustion device operable in a lean region and in a range including a stoichiometric region and a rich region, the NOx reduction catalyst comprising:a refractory inorganic substrate; a catalytic noble metal; a NOx absorbing material whic
1. A NOx reduction catalyst for exhaust gas discharged from a combustion device operable in a lean region and in a range including a stoichiometric region and a rich region, the NOx reduction catalyst comprising:a refractory inorganic substrate; a catalytic noble metal; a NOx absorbing material which is a metal comprising barium and magnesium, supported on said refractory inorganic substrate, at least a part of said metal comprising barium and magnesium forms a double carbonate represented by the following general formula: BaxMgy(CO3)2 where x and y are atom ratios in which x=0.5 to 1.999; y=0.001 to 1.5; and x+y=2.0; andan oxygen adsorbable and releasable material which carries at least a part of said catalytic noble metal, wherein said catalytic noble metal carried on the oxygen adsorbable and releasable material adsorbs SOx in the exhaust gas, in a form of at least one of sulfate and sulfite. 2. A NOx reduction catalyst as claimed in claim 1, wherein said catalytic noble metal includes platinum.3. A NOx reduction catalyst as claimed in claim 1, further comprising at least one metal selected from the group consisting of alkali metal, alkali earth metal other than barium and magnesium and rare earth metal, wherein said at least one metal adsorbs NOx in exhaust gas in the lean region and reduces the adsorbed NOx info nitrogen in the range including the stoichiometric region and the rich region.4. A NOx reduction catalyst as claimed in claim 1, wherein said catalytic noble metal includes rhodium.5. A NOx reduction catalyst as claimed in claim 1, wherein said combustion device is an internal combustion engine.6. A NOx reduction catalyst as claimed in claim 1, wherein said combustion device is a combustor.7. A NOx reduction catalyst for exhaust gas discharged from a combustion device operable in a lean region and in a range including a stoichiometric region and a rich region, the NOx reduction catalyst comprising:a refractory inorganic substrate; a first catalytic coat layer including a catalytic noble metal, a NOx absorbing material which is a metal comprising barium and magnesium, supported on said refractory inorganic substrate, at least a part of said metal comprising barium and magnesium forms a double carbonate represented by the following general formula: BaxMgy(CO3)2 where x and y are atom ratios in which x=0.5 to 1.999; y=0.001 to 1.5; and x+y=2.0, and an oxygen adsorbable and releasable material which carries at least a part of said catalytic noble metal, wherein said catalytic noble metal carried on the oxygen adsorbable and releasable material adsorbs SOx in the exhaust gas, in a form of at least one of sulfate and sulfite; anda second catalytic coat layer formed on said first catalytic coat layer, exhaust gas flowing though a position nearer to said second catalytic coat layer than to said first catalytic coat layer, said second catalytic coat layer including a catalytic noble metal, a NOx absorbing material which is a metal selected form the group consisting of barium and magnesium, supported on said refractory inorganic substrate, at least a part of said metal selected from the group consisting of barium and magnesium forms a double carbonate represented by the following general formula: BaxMgy(CO3)2 where x and y are atom ratios in which x=0.5 to 1.999; y=0.001 to 1.5; and x+y=2.0, and an oxygen adsorbable and releasable material which carries at least a part of said catalytic noble metal, wherein said catalytic noble metal carried on the oxygen adsorbable and releasable material adsorbs SOx in the exhaust gas, in a form of at least one of sulfate and sulfite,wherein said oxygen adsorbable and releasable material included in said first catalytic coat layer is larger in amount than said oxygen adsorbable and releasable material included in said second catalytic coat layer. 8. A NOx reduction catalyst as claimed in claim 7, wherein a weight ratio between said oxygen adsorbable and releasable material in said second catalytic coat layer and said oxygen adsorbable and releasable material in said first catalytic coat layer is within a range of from 0.01:0.99 to 1:1.9. A NOx reduction catalyst as claimed in claim 7, wherein rhodium is included only in said second catalytic coat layer.10. A NOx reduction catalyst for exhaust gas discharged from a combustion device operable in a lean region and in a range including a stoichiometric region and a rich region, the NOx reduction catalyst comprising:a refractory inorganic substrate; at least one catalytic noble metal selected from the group consisting of platinum and rhodium, supported on said refractory inorganic substrate; a NOx adsorbing material which is a metal comprising barium and magnesium, supported on said refractory inorganic substrate, at least a portion of said metal comprising barium and magnesium forms a double carbonate represented by the following general formula: BaxMgy(CO3)2 where x and y are atom ratios in which x=0.5 to 1.999; y=0.001 to 1.5; and x+y=2.0;an oxygen adsorbable and releasable material including ceria and supported on said refractory inorganic substrate, said oxygen adsorbable and releasable material carrying at least a part of said catalytic noble metal; wherein said catalytic noble metal carried on said oxygen adsorbable an releasable material adsorbs SOx in the exhaust gas, in the form of at least one of sulfate an sulfite. 11. A NOx reduction catalyst as claimed in claim 10, further comprising at least one metal selected from the group consisting of sodium, cesium and potassium, supported on said refractory inorganic substrate.12. A NOx reduction catalyst as claimed in claim 11, wherein said sodium is contained in a form of sodium oxide in an amount ranging from 0.5 to 20.0 g per one liter of said substrate.13. A NOx reduction catalyst as claimed in claim 11, wherein said cesium is contained in a form of cesium oxide in an amount ranging from 5 to 30 g per one liter of said substrate.14. A NOx reduction catalyst as claimed in claim 11, wherein said potassium is contained in a form of potassium oxide in an amount ranging from 5 to 30 g per one liter of said substrate.15. A NOx reduction catalyst as claimed in claim 10, where said ceria is contained in an amount ranging from 3 to 100 g per one liter of said substrate.16. A NOx reduction catalyst as claimed in claim 10, wherein said at least one catalytic noble metal is contained in an amount ranging from 1.4 to 4.3 g per one liter of said substrate.17. A NOx reduction catalyst as claimed in claim 10, wherein said ceria is combined with zirconium to form a double oxide.18. A NOx reduction catalyst as claimed in claim 10, wherein said barium and said magnesium are contained respectively in an amount ranging from 5 to 30 g in a form of barium oxide and in an amount ranging from 1 to 10 g in a form of magnesium oxide per one liter of said substrate.19. A NOx reduction catalyst for exhaust gas discharged from a combustion device operable in a lean region and in a range including a stoichiometric region and a rich region, the NOx reduction catalyst comprising:a refractory inorganic substrate; a catalytic noble metal including platinum; a NOx absorbing material which is a metal comprising barium and magnesium, supported on said refractory inorganic substrate, at least a part of said metal comprising barium and magnesium forms a double carbonate represented by the following general formula: BaxMgy(CO3)2 where x and y are atom ratios in which x=0.5 to 1.999; y=0.001 to 1.5; and x+y=2.0; andan oxygen adsorbable and releasable material which carries at least a part of said catalytic noble metal, said oxygen adsorbable and releasable material including ceria which carries platinum in an amount ranging from 5 to 50% by weight of a whole amount of platinum contained in said NOx reduction catalyst, wherein said platinum carried on said ceria adsorbs SOx in the exhaust gas, in a form of at least one of sulfate and sulfite. 20. A NOx reduction system for exhaust gas discharged from a combustion device operable in a lean region and in a range including a stoichiometric region and a rich region, the NOx reduction system comprising:a refractory inorganic substrate; a NOx reduction catalyst including a catalytic noble metal, a NOx absorbing material which is a metal comprising barium and magnesium, supported on said refractory inorganic substrate, at least a part of said metal comprising barium and magnesium forms a double carbonate represented by the following general; formula: BaxMgy(CO3)2 where x and y are atom ratios in which x=0.5 to 1.999; y=0.001 to 1.5; and x+y=2.0, and an oxygen adsorbable and releasable material which carries at least a part of said catalytic noble metal, wherein said catalytic noble metal carried on the oxygen adsorbable and releasable material adsorbs SOx in the exhaust gas, in a form of at least one of sulfate and sulfite; anda device for controlling an air-fuel (air/fuel) ratio of an air-fuel mixture to be supplied to the combustion device, within a range of not smaller than 15 in the lean region. 21. A NOx reduction system for exhaust gas discharged from a combustion device operable in a lean region and in a range including a stoichiometric region and a rich region, the NOx reduction system comprising:a refractory inorganic substrate; an exhaust gas passageway through which exhaust gas from the combustion device flows; a NOx reduction catalyst disposed in said exhaust gas passageway and including a catalytic noble metal, a NOx absorbing material which is a metal comprising barium and magnesium, supported on said refractory inorganic substrate, at least a part of said metal comprising barium and magnesium forms a double carbonate represented by the following general formula: BaxMgy(CO3)2 where x and y are atom ratios in which x=0.5 to 1.999; y=0.001 to 1.5; and x+y=2.0, and an oxygen adsorbable and releasable material which carries at least a part of said catalytic noble metal, wherein said catalytic noble metal carried on the oxygen adsorbable and releasable material adsorbs SOx in the exhaust gas, in a form of at least one of sulfate and sulfite; anda device for causing secondary air to flow into said exhaust gas passageway upstream of said NOx reduction catalyst in the range including the stoichiometric region and the rich region. 22. A method of reducing NOx in exhaust gas discharged from a combustion device which is operable in a lean region and in a range including a stoichiometric region and a rich region, said method comprising:providing the combustion device with a NOx reduction catalyst including a refractory inorganic substrate, a catalytic noble metal, a NOx absorbing material which is a metal comprising barium and magnesium, supported on said refractory inorganic substrate, wherein at least a part of said metal comprising barium and magnesium forms a double carbonate represented by the following general formula: BaxMgy(CO3)2 where x and y are atom ratios in which x=0.5-1.999, y=0.001-1.5; and x+y=2, and an oxygen adsorbable and releasable material which carries at least a part of said catalytic noble metal; and causing exhaust gas to flow through the NOx reduction catalyst to allow the catalytic noble metal carried on the oxygen adsorbable and releasable material to adsorb SOx in the exhaust gas, in a form of at least one of sulfate and sulfite.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (10)
Wan Chung-Zong (Somerset NJ) Dettling Joseph C. (Howell NJ), Aluminum-stabilized ceria catalyst compositions, and methods of making the same.
Wan Chung-Zong (Somerset NJ) Tauster Samuel J. (Englishtown NJ) Rabinowitz Harold N. (Upper Montclair NJ), Catalyst composition containing platinum and rhodium components.
Dieter Lindner DE; Renee Van Yperen DE; Lothar Mussmann DE; Egbert Lox DE; Thomas Kreuzer DE, Exhaust gas treatment catalyst for internal combustion engines with two catalytically active layers on a carrier structure.
Efstathiou, Angelos M.; Savva, Petros G.; Costa, Costas N., Catalyst containing platinum and palladium for the selective reduction of NOx with hydrogen (H2-SCR).
Park, Jong-Ho; Jung, Tae Sung; Yoon, Hyung Chul; Guahk, Young Tae; Beum, Hee-Tae; Park, Jong-kee; Han, Sang-Sup; Kim, Jong-Nam; Cho, Soon-Haeng, Continuous oxygen production method and continuous oxygen adsorption and desorption device using oxygen adsorbing agent.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.