초록 ▼

In order to achieve an economical and trouble-free continuous extrusion of plastic hollow profiles having at least one hollow chamber that is filled with foam, the profile tool of an extrusion device is configured in the shape of a pistol. The profile tool comprises a pistol shaft (102) with a melt

In order to achieve an economical and trouble-free continuous extrusion of plastic hollow profiles having at least one hollow chamber that is filled with foam, the profile tool of an extrusion device is configured in the shape of a pistol. The profile tool comprises a pistol shaft (102) with a melt feed channel (166), connected to the melt discharge opening of the extruder (300) and which opens into a melt radial distributor channel (164) that surrounds the lance guide channel (150). The profile tool is also equipped with a pistol barrel (101) comprising a melt ring channel (162), which extends from the melt radial distributor channel (164) to the profile nozzle (160) and comprising a lance guide channel (150), which extends in a continuous manner from a lance inlet (152) to the profile nozzle (160).

대표청구항 ▼

1. In a method for producing plastic hollow profiles with at least one hollow chamber that is filled with foam, said method comprising:(1) extruding a plastic hollow profile using a profile tool at a discharge speed VA; (2) cooling the plastic hollow profile as it moves forward at the discharge spee

1. In a method for producing plastic hollow profiles with at least one hollow chamber that is filled with foam, said method comprising:(1) extruding a plastic hollow profile using a profile tool at a discharge speed VA; (2) cooling the plastic hollow profile as it moves forward at the discharge speed VA; (3) directing a foam lance into the hollow chamber, with the foam lance tip positioned in an area of the plastic hollow profile, the temperature of the section of the plastic hollow profile surrounding the foam lance tip being cooled to a foam temperature TA; (4) injecting a reactive mixture made up of at least one foaming component into the hollow chamber with a foam substance temperature TS and foaming in a plastic isolating foam body by means of the continuous recalibration and recooling of the outer side of the plastic hollow profile; the improvement wherein the plastic hollow profile extruded out of the profile tool is taken off on a track which is slanted downward with an angle α in the range of 1-10° with respect to the horizontal.2. Method according to claim 1, wherein a reaction mixture is selected such that, given the temperature of the foam substance TS in the lance tip, it forms plastic foam with a reaction time in the range of 10 to 20 s.3. Method according to claim 2, wherein the reaction mixture contains an isocyanate as first reaction component, and at least one of a polyalcohol in water and a carboxylic acid as second reaction component, and wherein the reaction mixture is foamed into one of a polyurethane foam body, a polyisocyanurate foam body and a polyurea foam body.4. Method according to claim 3, wherein polyole and isocyanate are mixed with a ratio of 100 parts per weight polyole to 120 up to 160 parts per weight isocyanate.5. Method according to claim 4, wherein every 100 parts per weight of polyoles are loaded with 15 to 25 volume percent air and wherein the mixture of polyole and air is mixed with 120 to 160 parts per weight isocyanate.6. Method according to claim 1, wherein the reaction mixture is extruded from an unsaturated resin, a hardener and a propellant into a polyester resin foam body.7. Method according to claim 1, wherein the reaction mixture is extruded from a propellant and an expandable thermoplastic into a thermoplastic foam body.8. Method according to claim 7, wherein the thermoplastic is polystyrene.9. Method according to claim 2, wherein the discharge speed VA is between 1 and 8 m/min.10. Method according to claim 2, wherein the discharge speed VA is approximately equal to 2 m/min.11. Method according to claim 2, wherein the foaming temperature TA is in the range of 25° and 50° C.12. Method according to claim 2, wherein the foaming temperature TA is approximately equal to 30° C.13. Method according to claim 2, wherein the foam substance temperature Ts is in the range of 15° and 25° C.