초록 ▼

The present invention relates an acoustical insulation material for sound attenuation containing a nonwoven web. Surprisingly, it has been discovered that an acoustical insulation material made from a nonwoven web of thermoplastic fibers having an average fiber diameter of less than about 7 microns,

The present invention relates an acoustical insulation material for sound attenuation containing a nonwoven web. Surprisingly, it has been discovered that an acoustical insulation material made from a nonwoven web of thermoplastic fibers having an average fiber diameter of less than about 7 microns, wherein the acoustical insulation has a thickness less than about 3 mm and a density of greater than about 50 kg/m3 is effective as a sound insulation material. The acoustical insulation is very effective as an acoustical insulation material, despite the low thickness and high density of the acoustical insulation. A method of attenuating sound waves passing from a sound source area to a second area using the acoustical insulation material is also disclosed.

대표청구항 ▼

1. An acoustical insulation material nonwoven web comprising thermoplastic fibers having an average fiber diameter of less than about 7 microns, wherein the acoustical insulation material has a thickness less than about 3 mm and a density greater than about 50 kg/m3.2. The acoustical insulation mate

1. An acoustical insulation material nonwoven web comprising thermoplastic fibers having an average fiber diameter of less than about 7 microns, wherein the acoustical insulation material has a thickness less than about 3 mm and a density greater than about 50 kg/m3.2. The acoustical insulation material of claim 1, wherein the thermoplastic fibers have an average fiber diameter of less than about 5 microns.3. The acoustical insulation material of claim 2, wherein the thermoplastic fibers have an average fiber diameter of about 1.0 microns to about 4.0 microns.4. The acoustical insulation material of claim 1, wherein the thickness of the acoustical insulation is between about 0.2 mm to about 2.5 mm and the density of the acoustical insulation is between about 55 kg/m3 and about 150 kg/m3.5. The acoustical insulation material of claim 1, wherein the thickness of the acoustical insulation is between about 0.3 mm to about 1.0 mm and the density of the acoustical insulation is between about 58 kg/m3 and about 100 kg/m3.6. The acoustical insulation material of claim 3, wherein the thickness of the acoustical insulation is between about 0.3 mm to about 1.0 mm and the density of the acoustical insulation is between about 58 kg/m3 and about 100 kg/m3.7. The acoustical insulation material of claim 1, wherein the thermoplastic fibers comprise a thermoplastic polymer selected from the group consisting of polyolefins, polyesters, polyamides, polycarbonates, polyurethanes, polyvinylchloride, polytetrafluoroethylene, polystyrene, polyethylene terephathalate, polylactic acid and copolymers and blends thereof.8. The acoustical insulation material of claim 7, wherein the thermoplastic polymer comprises a polyolefin.9. The acoustical insulation material of claim 8, wherein the polyolefin comprises polypropylene.10. The acoustical insulation material of claim 1, wherein the nonwoven web is a material has a pressure drop of at least 1 mm of water at a flow rate of about 32 liters/min.11. The acoustical insulation material of claim 10, wherein the pressure drop is between about 3 mm and about 10 mm of water at a flow rate of about 32 liters/min.12. The acoustical insulation material of claim 1, wherein the thermoplastic fibers comprise monocomponent fibers.13. The acoustical insulation material of claim 1, wherein the thermoplastic fibers comprise multicomponent fibers.14. The acoustical insulation material of claim 13, wherein the multicomponent fibers have a side-by-side configuration.15. The acoustical insulation material of claim 14, wherein the multicomponent fibers comprises at least one component comprising polyethylene and at least one component comprising polypropylene.16. The acoustical insulation material of claim 13, wherein the multicomponent fibers are splitable.17. The acoustical insulation material of claim 13, wherein the thickness of the acoustical insulation is between about 0.2 mm to about 2.5 mm and the density of the acoustical insulation is between about 55 kg m3 and about 150 kg/m3.18. The acoustical insulation material of claim 1, wherein the nonwoven web is bonded.19. The acoustical insulation material of claim 1, wherein the nonwoven web is a meltblown nonwoven web and further comprises a second layer of coarse meltblown fibers having an average fiber diameter greater than about 10 microns.20. The acoustical insulation material of claim 1, wherein the thermoplastic fibers are meltblown thermoplastic fibers.21. An article of manufacture comprising the acoustical insulation of claim 1.22. A method of attenuating sound waves passing from a sound source area to a second area comprising positioning the acoustical insulation material of claim 1 between the sound source area and the second area.23. A method of attenuating sound waves passing from a sound source area to a second area comprising positioning the acoustical insulation material of claim 4 between the sound source area and the second area.24. A method of attenuating sound waves passing from a sound source area to a second area comprising positioning the acoustical insulation material of claim 6 between the sound source area and the second area.