초록 ▼

The present invention employs alkyl polysilicate to form silicone-polyester-polysilicate hybrid compositions with an appropriate proportion to modify silicone-polyester resin, or directly adds the alkyl polysilicate at an appropriate proportion into silicone-polyester resin to produce a hybrid compo

The present invention employs alkyl polysilicate to form silicone-polyester-polysilicate hybrid compositions with an appropriate proportion to modify silicone-polyester resin, or directly adds the alkyl polysilicate at an appropriate proportion into silicone-polyester resin to produce a hybrid composition. The composition in high baking temperature forms a hybrid structure having good thermal resistance, especially, hot-oil resistance and hot hardness, and good adhesion to metals such as carbon steel, stainless steel and aluminum. The present invention can be used in the field of the protective coating for heat-resistant metal such as frying pans and electric irons to be a kind of novel heat-resistant composition having hybrid structure. The composition in accordance with the present invention comprises (A)silicone-polyester; (B)alkyl polysilicate and the structure thereof comprises (RO)3?Si?O?(Si(OR)2?O)n?R, where n=0?20 and R represents ?CH3, ?C2H5, ?C3H7, or ?C4H9. The composition mentioned above comprises the compounds of (A) and (B) or the copolymer comprised by (A) and (B).

대표청구항 ▼

1. A heat-resistant material, said material being a kind of silicone-polyester-polysilicate composition consisting essentially of:1) silicone-polyester 2) alkyl polysilicate wherein said material is formed by a combination method of bonding said silicone-polyester and said alkyl polysilicate, and a

1. A heat-resistant material, said material being a kind of silicone-polyester-polysilicate composition consisting essentially of:1) silicone-polyester 2) alkyl polysilicate wherein said material is formed by a combination method of bonding said silicone-polyester and said alkyl polysilicate, and a solid weight ratio of said alkyl polysilicate to said silicone-polyester is about 3:100 to 15:100; wherein said silicone-polyester comprises a silicone resin and a polyester, wherein a combination percentage of said silicone resin is higher than said polyester, and said silicone-polyester has OH functional group which can react with said alkyl polysilicate; and said alkyl polysilicate is (RO)3?Si?O?[Si(OR)2?O]n?R, wherein n represents a numeric and about less than 20 and R represents an alkyl functional group. 2. The material according to claim 1, wherein said silicone resin is from 50% to 80% by weight of said silicone-polyester, said polyester is from 50% 20% by weight of said silicone-polyester and said alkyl functional group of said alkyl polysilicate comprises ?CH3, ?C2H5, ?C3H7, or ?C4H9.3. The material according to claim 2, wherein said combination method comprises a step for copolymerizing said silicon-polyester and said alkyl polysilicate.4. The material according to claim 2, wherein said combination method comprises a step for polymerizing said silicone and said polyester, and then adding said alkyl polysilicate for a blending reaction.5. The material according to claim 1, wherein a coating formed from said heat-resistant material withstands 80 circulations of a 260° C. hot-oil resistant test.6. A heat-resistant material utilized as a substrate coating, said material being a kind of silicone-polyester-polysilicate composition consisting essentially of:1) silicone-polyester 2) alkyl polysilicate wherein said material is formed by a combination method of bonding said silicone-polyester and said alkyl polysilicate, and a solid weight ratio of said alkyl polysilicate to said silicone-polyester is about 3:100 to 15:100; wherein said silicone-polyester comprises a silicone resin and a polyester, wherein a combination percentage of said silicone resin is higher than said polyester, and said silicone-polyester has OH functional group which can react with said alkyl polysilicate; and said alkyl polysilicate is (RO)3?Si?O?[Si(OR)2?O]n?R wherein n represents a numeric and about less than 20 and R represents an alkyl functional group. 7. The material according to claim 6, wherein said substrate comprises metal or glass.8. The material according to claim 7, wherein said silicone resin is from 50% to 80% by weight of said silicone-polyester, said polyester is from 50% m 20% by weight of said silicone-polyester, and said alkyl functional group of said alkyl polysilicate comprises ?CH3, ?C2H5, ?C3H7, or ?C4H9.9. The material according to claim 7, wherein said combination method comprises a step for copolymerizing said silicon-polyester and said alkyl polysilicate.10. The material according to claim 7, wherein said combination method comprises a step for polymerizing said silicone and said polyester, and then adding said alkyl polysilicate for a blending reaction.11. The material according to claim 6, wherein the substrate coating formed from said heat-resistant material withstands 80 circulations of a 260° C. hot-oil resistant test.