초록 ▼

A low density slurry bridge mix for use in an inflatable restraint system is provided. The low density slurry bridge mix includes zirconium metal, a thermal conductivity enhancer such as aluminum metal, potassium perchlorate oxidant, and a binder material and has a dry density of about 45 to about 6

A low density slurry bridge mix for use in an inflatable restraint system is provided. The low density slurry bridge mix includes zirconium metal, a thermal conductivity enhancer such as aluminum metal, potassium perchlorate oxidant, and a binder material and has a dry density of about 45 to about 65 percent of theoretical density. The low density slurry bridge mix may be used in an initiator including an unground header attached to a raised bridgewire wherein the low density slurry bridge mix surrounds and adheres to the bridgewire.

대표청구항 ▼

1. A low density slurry bridge mix comprising:about 25 to about 35 compositions weight percent zirconium metal; about 10 to about 20 composition weight percent thermal conductivity enhancer; about 45 to about 65 composition weight percent potassium perchlorate oxidant; and about 1.5 to about 5.0 com

1. A low density slurry bridge mix comprising:about 25 to about 35 compositions weight percent zirconium metal; about 10 to about 20 composition weight percent thermal conductivity enhancer; about 45 to about 65 composition weight percent potassium perchlorate oxidant; and about 1.5 to about 5.0 composition weight percent binder material; wherein the low density slurry bridge mix has a dry density of about 45% to about 65% of theoretical density. 2. The low density slurry bridge mix of claim 1 wherein the thermal conductivity enhancer comprises a metal selected from the group consisting of aluminum, magnesium, tungsten, and combinations thereof.3. The low density slurry bridge mix of claim 1 wherein the thermal conductivity enhancer comprises a metal oxide selected from the group consisting of cupric oxide, gold, silver and palladium oxides, and combinations thereof.4. The low density slurry bridge mix of claim 1 wherein the thermal conductivity enhancer comprises aluminum metal.5. The low density slurry bridge mix of claim 1 having adhesive properties effective to adhere the low density slurry bridge mix to an associated bridgewire.6. The low density slurry bridge mix of claim 1 wherein the binder material comprises an acrylic binder.7. A low density slurry bridge mix comprising:about 25 to about 35 composition weight percent zirconium metal; about 10 to about 20 composition weight percent aluminum metal thermal conductivity enhancer; about 48 to about 65 composition weight percent potassium perchlorate oxidant; and about 1.5 to about 5 composition weight percent acrylic binder; wherein the low density slurry bridge mix has a dry density of about 45% to about 65% of theoretical density. 8. The low density slurry bridge mix of claim 1 further comprising a metal oxide supplemental oxidant.9. The low density slurry bridge mix of claim 8 wherein the metal oxide supplemental oxidant is selected from the group consisting of cupric oxide, gold, silver, platinum, and palladium oxides, and combinations thereof.10. The low density slurry bridge mix of claim 8 wherein the metal oxide supplement oxidant comprises cupric oxide.11. The low density slurry bridge mix of claim 8 comprising about 10 to about 20 composition weight percent metal oxide supplemental oxidant.12. An electrical initiator comprising:a raised bridgewire; and the low density slurry bridge mix of claim 1, wherein the low density slurry bridge mix is adhered to the raised bridgewire. 13. The electrical initiator of claim 12 wherein the raised bridgewire is encased in and adhesively bonded to the low density slurry bridge mix.14. The electrical initiator of claim 12 wherein the thermal conductivity enhancer comprises aluminum metal.15. The electrical initiator of claim 12 wherein the low density slurry bridge mix comprises:about 25 to about 35 composition weight percent zirconium metal; about 10 to about 20 composition weight percent aluminum metal thermal conductivity enhancer; about 48 to about 65 composition weight percent potassium perchlorate oxidant; and about 1.5 to about 5 composition weight percent acrylic binder. 16. The electrical initiator of claim 12 wherein the low density slurry bridge mix further comprises a metal oxide supplement oxidant.17. The electrical initiator of claim 16 wherein the metal oxide supplemental oxidant is selected from the group consisting of cupric oxide, gold, silver, platinum and palladium oxides, and combinations thereof.18. The electrical initiator of claim 17 wherein the metal oxide supplemental oxidant comprises cupric oxide.19. The electrical initiator of claim 16 wherein the low density slurry bridge mix comprises about 10 to about 20 composition weight percent metal oxide supplemental oxidant.20. The electrical initiator of claim 12 further comprising an unground header.21. The electrical initiator of claim 20 wherein the low density slurry bridge mix has adhesive properties effective to adhere the low density slurry bridge mix to the unground header.22. A low density slurry bridge mix having adhesive properties effective to adhere the low density slurry bridge mix to an associated bridgewire comprising:about 25 to about 35 composition weight percent zirconium metal; about 10 to about 20 composition weight percent aluminum metal thermal conductivity enhancer; about 48 to about 65 composition weight percent potassium perchlorate oxidant; about 10 to about 20 composition weight percent metal oxide supplemental oxidant; and about 1.5 to about 5 composition weight percent acrylic binder; wherein the low density slurry bridge mix has a dry density of about 45% to about 60% of theoretical density. 23. The low density slurry bridge mix of claim 22 wherein the metal oxide supplemental oxidant comprises cupric oxide.24. The low density slurry bridge mix of claim 7 further comprising a metal oxide supplemental oxidant.25. The low density slurry bridge mix of claim 24 wherein the metal oxide supplemental oxidant is selected from the group consisting of cupric oxide, gold, silver, platinum, and palladium oxides, and combinations thereof.26. The low density slurry bridge mix of claim 24 wherein the metal oxide supplement oxidant comprises cupric oxide.27. The low density slurry bridge mix of claim 24 comprising about 10 to about 20 composition weight percent metal oxide supplemental oxidant.