초록 ▼

A laminated composite fabric material used for example in the manufacture of automobile air bags has at least one thermoplastic coating layer that is pressure laminated to a pre-treated fabric using an adhesive. The fabric, pre-treated with a curing agent such as an alkyl ether amine, resists penetr

A laminated composite fabric material used for example in the manufacture of automobile air bags has at least one thermoplastic coating layer that is pressure laminated to a pre-treated fabric using an adhesive. The fabric, pre-treated with a curing agent such as an alkyl ether amine, resists penetration by the adhesive, resulting in a softer, more pliable composite fabric. The composite fabric also optionally includes a layer comprising a silicone polyurethane copolymer or acrylic cross-linked with a blocked isocyanate, which functions as a non-stick coating. The invention also relates to a method for manufacturing a laminated composite fabric.

대표청구항 ▼

1. A process for manufacturing a coated fibrous fabric comprising: coating a fabric with a curing compound that increases viscosity of an adhesive; applying an adhesive to the coated fabric; and pressure laminating a thermoplastic film to the adhesive-coated fabric, wherein the curing compound compr

1. A process for manufacturing a coated fibrous fabric comprising: coating a fabric with a curing compound that increases viscosity of an adhesive; applying an adhesive to the coated fabric; and pressure laminating a thermoplastic film to the adhesive-coated fabric, wherein the curing compound comprises at least two amine moieties per molecule of curing agent, and reduces penetration of the adhesive into the fabric compared with a coated fabric manufactured without the curing compound.2. The process of claim 1 wherein the compound adheres to the fibers and thereby substantially prevents the adhesive from physically entering the fabric.3. The process of claim 1 wherein the curing compound increases the viscosity of the adhesive contacting the fabric and thereby substantially preventing the adhesive from entering the fabric.4. The process of claim 1 wherein the compound is a cross linking agent, which cross links the adhesive contacting the fabric and thereby substantially prevents the adhesive from entering the fabric.5. The process of claim 3 wherein the coated fibrous fabric further comprises a silicone- or acrylicic-containing compound or mixture thereof applied to the film in an amount sufficient to ensure no sticking or blocking under heat and pressure of the coated fibrous fabric.