초록 ▼

The present invention is directed to a catalyzed metallic substrate, such as a metal plate. There is a catalyst layer supported on the substrate surface. The article is useful as part of exhaust systems which can be used with small engines for applications such as motorcycles, lawn mowers, chain saw

The present invention is directed to a catalyzed metallic substrate, such as a metal plate. There is a catalyst layer supported on the substrate surface. The article is useful as part of exhaust systems which can be used with small engines for applications such as motorcycles, lawn mowers, chain saws, weed trimmers and the like. The present invention includes methods to prepare the catalyzed metal substrate and methods of use of the catalyzed substrate.

대표청구항 ▼

1. An article comprising:a metal substrate, having a substrate surface comprising at least one metal oxide selected from the group consisting of alumina and rare earth metal oxides; a catalyst comprising at least one catalyst layer having an outer catalyst layer surface, the catalyst layer supported

1. An article comprising:a metal substrate, having a substrate surface comprising at least one metal oxide selected from the group consisting of alumina and rare earth metal oxides; a catalyst comprising at least one catalyst layer having an outer catalyst layer surface, the catalyst layer supported on the substrate surface; the catalyst comprising at least one catalytically active particulate material and outer the catalyst layer surface comprises agglomerates of the catalytically active particulate material having an average diameter of from about 20 to about 200 micrometers, and wherein the agglomerates at the outer catalyst layer surface adhere to each other to form peaks from about 20 to about 500 micrometers formed by depositing of at least two strata of the catalytically active particulate material with each strata being up to 20 micrometers in thickness. 2. The article as recited in claim 1 wherein the catalytically active material comprises at least one precious metal component and at least one refractory component.3. The article as recited in claim 2 wherein the catalyst comprises at least two refractory components including a first refractory component and a second refractory component wherein the average particle size of the second refractory oxide component is greater than the average particle size of the first component.4. The article as recited in claim 2 wherein the refractory component is selected from the group consisting of silica, alumina and titania compounds.5. The article as recited in claim 4 wherein the refractory component is selected from the group consisting of alumina, silica, silica-alumina, alumina-silicates, alumina-zirconia, alumina-chromia, and alumina-ceria.6. The article as recited in claim 5 wherein the refractory component is activated alumina.7. The article as recited in claims 1 wherein the catalyst composition further comprises a nickel or iron component.8. The article of claim 1 wherein the catalyst further comprises at least one component selected from the group consisting of:at least one rare earth metal component; an oxygen storage composition; at least one first stabilizer; and a compound containing zirconium. 9. The article as recited in claim 8 wherein at least one of said rare earth metal component is selected from the group consisting of lanthanum components and neodymium components.10. The article as recited in claim 8 wherein the oxygen storage component is selected from the group consisting of cerium and praseodymium compounds.11. The article as recited in claim 8 wherein the stabilizer is at least one alkaline earth metal component derived from a metal selected from the group consisting of magnesium, barium, calcium and strontium.12. The article as recited in claim 8 further comprising a particulate composite of zirconia compound and rare earth oxide.13. The article as recited in claim 12 wherein the rare earth oxide is ceria and, optionally, further comprises lanthana, neodymia and mixtures thereof.14. The article as recited in claim 1 wherein the metal substrate is in the form of a metal plate at least 0.005 inches thick.15. The article as recited in claim 14 wherein the metal plate is at least 0.025 inches thick.16. The article as recited in claim 14 wherein the metal plate is corrugated.17. The article as recited in claim 14 wherein the metal plate contains a plurality of holes.18. The article as recited in claim 1 wherein the metal substrate is in the form of at least part of an exhaust system wall defining an exhaust stream passage, wherein the exhaust system wall of exhaust stream passage defines the substrate surface.19. The article as recited in claim 1 wherein the metal substrate is in the form of a baffle plate of an exhaust system muffler.20. The article as recited in claim 19 wherein the baffle plate is at least 0.025 inches thick.21. The article as recited in claim 19 wherein the baffle plate is corrugated.22. The article as recited in claim 19 wherein the baffle plate contains a plurality of holes.23. A method comprising the steps of:depositing at least two strata of a catalyst on a substrate surface of a substrate to form a catalyst layer with each strata being up to 20 micrometers in thickness, the substrate surface comprising at least one metal oxide selected from the group consisting of alumina and rare earth metal oxides, and the catalyst comprising at least one catalytically active particulate material deposited to form agglomerates of the catalytically active particulate material having an average diameter of from about 20 to about 200 micrometers and wherein the agglomerates at the outer catalyst layer surface adhere to each other to form peaks from about 20 to about 500 micrometers. 24. The method as recited in claim 23 wherein the catalytically active material comprisesat least one precious metal component; and at least one first refractory component. 25. The method as recited in claim 24 wherein the catalyst comprises at least two refractory components including a first refractory component and a second refractory component wherein the average particle size of the second refractory oxide component is greater than the average particle size of the first component.26. The method as recited in claim 23 wherein the step of depositing at least two strata further comprises depositing an aqueous slurry of the catalyst to form each strata as a composition having an amount of fluid to be less than incipient wetness and repeating this step for each succeeding strata.27. The method as recited in claim 23 wherein the step of depositing each stratum comprises spraying the slurry.28. The method as recited in claim 23 further comprising the step of drying each stratum prior to depositing the succeeding stratum.29. The method as recited in claim 23 wherein each stratum of the layer comprises the same catalyst composition.30. The method as recited in claim 23 wherein the strata of the layer comprise different catalyst compositions.31. The method as recited in claim 23 wherein there are at least two catalyst layers.32. The method as recited in claim 23 further comprising the step of forming a tie layer comprising a refractory metal compound adjacent to the substrate surface and between the substrate surface and the catalyst.33. The method as recited in claim 23 further comprising the step of roughening the substrate surface to form a rough substrate surface.34. The method as recited in claim 33 further wherein the step of roughening the substrate surface comprises sandblasting the surface.35. The method as recited in claim 33 further wherein the step of roughening the substrate surface comprises chemically treating the surface.36. The method as recited in claim 23 further comprising the step of calcining the rough substrate surface to form a layer comprising alumina on a substrate surface.37. The method as recited in claim 36 wherein the step of calcining the substrate is conducted from about 800° C. to about 1100° C. for from 0.5 hours to about 10.0 hours.38. The method as recited in claim 23 further comprising the step of calcining the at least one catalyst layer.39. The method as recited in claim 38 further comprising the steps of forming and then calcining the at least one bottom layer followed by forming and then calcining the at least one top layer.40. The method as recited in claim 23 further comprising the step of adding to the catalyst at least one of the following materials to selected from the group consisting of:at least one rare earth metal component; an oxygen storage composition; at least one stabilizer; and a compound containing zirconium. 41. A method comprising the steps of:contacting a gas containing at least one component selected from the group consisting of nitrogen oxide, carbon monoxide and/or hydrocarbon with an article comprising: a metal substrate, having a substrate surface comprising at least one metal oxide selected from the group consisting of alumina and a rare earth metal; a catalyst comprising at least one catalyst layer having an outer catalyst layer surface, the catalyst layer supported on the substrate surface; the catalyst comprising at least one catalytically active particulate material and the outer catalyst layer surface comprises agglomerates of the catalytically active particulate material having an average diameter of from about 20 to about 200 micrometers, and wherein the agglomerates at the outer catalyst layer surface adhere to each other to form peaks from about 20 to about 500 micrometers formed by depositing of at least two strata of the catalytically active particulate material with each strata being up to 20 micrometers in thickness.