초록 ▼

Structured zeolite coated structures comprising thick porous inorganic zeolite coatings disposed on monolithic support structures, which can be honeycomb shaped, are disclosed. The zeolite coatings have open interconnected pores of controlled pore size and are characterized by improved durability, p

Structured zeolite coated structures comprising thick porous inorganic zeolite coatings disposed on monolithic support structures, which can be honeycomb shaped, are disclosed. The zeolite coatings have open interconnected pores of controlled pore size and are characterized by improved durability, physical integrity, and adherence sufficient to enable use as supports for catalysts in liquid phase applications under harsh reaction conditions. Methods for making zeolite coated structures are also disclosed.

대표청구항 ▼

1. A zeolite coated monolithic article comprising:an uncoated monolithic support structure including walls having open porosity; and a porous inorganic zeolite coating disposed directly upon the uncoated monolithic support structure, wherein the zeolite coating has a permanent alumina binder compone

1. A zeolite coated monolithic article comprising:an uncoated monolithic support structure including walls having open porosity; and a porous inorganic zeolite coating disposed directly upon the uncoated monolithic support structure, wherein the zeolite coating has a permanent alumina binder component, an open, interconnected porosity characterized by a mean pore size in the range of about 0.2 to 104 nanometers, a porosity of 30% to 65%, and a thickness in excess of 100 μm. 2. The zeolite coated monolithic article of claim 1, further including a metal, metal oxide, or metal sulfide catalytically active species disposed on or within the zeolite coating.3. The zeolite coated monolithic article of claim 1 incorporating at least two zeolite coating layers differing in density, pore morphology, or catalytic species composition from one another.4. A method of making a zeolite coated monolithic article comprising the steps of:(a) providing a monolithic support structure; (b) providing a wash-coating slurry comprising a pore-forming additive and a zeolite powder dispersed in a sol-gel binder slurry phase which contains an alumina inorganic binder precursor; (c) depositing the slurry directly upon on surfaces of the monolithic support structure to form a first slurry coating layer; (d) heating the first slurry coating layer to a temperature at least sufficient to remove the liquid phase therefrom to provide a first deposited layer; (e) repeating steps (a)-(d) above to form additional deposited layers to form a porous multi-layered zeolite coating incorporating an alumina binder. 5. The method according to claim 4, wherein the monolithic cordierite support structure is a ceramic honeycomb support structure.6. The method according to claim 4, wherein the multi-layered zeolite coating has a thickness of at least 100 μm.7. The method according to claim 4 which further comprises the step of providing one or more catalytically active species selected from the group consisting of precious metal catalysts and transition metal catalysts on or within at least one deposited zeolite layer.8. The method according to claim 4 wherein the wash-coating slurry further comprises at least one of a gel-promoting constituent and a pore-forming additive.9. A zeolite coated monolithic ceramic article comprising:a monolithic ceramic support structure including walls having open porosity; and a porous inorganic zeolite coating disposed directly upon the ceramic support structure, wherein the zeolite coating has an open, interconnected porosity characterized by a mean pore size in the range of about 0.2 to 104 nanometers and a porosity of 30% to 65%, and is formed by the method comprising the steps of: (a) providing a monolithic ceramic support structure; (b) providing a wash-coating slurry comprising a zeolite powder dispersed in slurry phase which contains an inorganic binder sol precursor; (c) depositing the slurry on surfaces of the monolithic support structure to form a first slurry coating layer; (d) heating the first slurry coating layer to a temperature at least sufficient to remove the liquid phase therefrom to provide a first deposited layer; (e) repeating steps (a)-(d) above to form additional deposited layers to form a multi-layered coating.