초록 ▼

A titanium dioxide film (2) having at least photocatalytic activity, whose light linear transmittance corresponding to light having a wavelength of 550 nm is not less than 50% and whose thickness is 0.1 to 5 μm or so, is formed on a transparent substrate (1) constituted by a glass plate or the like.

A titanium dioxide film (2) having at least photocatalytic activity, whose light linear transmittance corresponding to light having a wavelength of 550 nm is not less than 50% and whose thickness is 0.1 to 5 μm or so, is formed on a transparent substrate (1) constituted by a glass plate or the like. Preferably, a precoat film (3), which has optical transmissivity and is constituted by a SiO2 film having a thickness of 0.02 to 0.2 μm or so, is provided between the transparent substrate (1) and the titanium dioxide film (2). Thereby, excellent photocatalytic action and optical transmissivity can be obtained. Moreover, members composing various structures such as a glass window, which are especially required to have optical transparency, can be further provided with photocatalytic activities.

대표청구항 ▼

1. A window glass comprising:a transparent plate having first and second opposing surfaces and formed of a soda lime glass; and a titanium dioxide film having a first surface deposited on at least one of the surfaces of said transparent plate, said titanium dioxide film having a photocatalytic activ

1. A window glass comprising:a transparent plate having first and second opposing surfaces and formed of a soda lime glass; and a titanium dioxide film having a first surface deposited on at least one of the surfaces of said transparent plate, said titanium dioxide film having a photocatalytic activity, a linear transmittance of at least 50% for light having a wavelength of 550 nm and a linear transmittance of 50% or less for light having a wavelength of 350 nm. 2. A window glass according to claim 1 wherein at least 0.5 μg of linoleic acid deposited per cm2 on a second surface of said titanium dioxide film is decomposed when said titanium dioxide film is irradiated with ultraviolet light, including light in the 300 to 400 nm range at an intensity of 5 mW/cm2.3. A window glass according to claim 1, wherein the thickness of the titanium dioxide film is in the range of approximately 0.1 to 5.0 μm.4. A window glass according to claim 1, wherein the titanium dioxide film contains anatase crystals.5. A window glass according to claim 1, further comprising a precoat film has a transparency characteristic that is disposed between the transparent plate and the titanium dioxide film.6. A window glass according to claim 5, wherein the thickness of the precoat film is in the range of approximately 0.02 to 0.2 μm.7. A window glass according to claim 5 wherein the precoat film is made from of one of a silicone dioxide film, a tin oxide film, an indium-doped tin oxide film, an indium oxide film, a tin-doped indium oxide film, a germanium oxide film, an aluminum oxide film, a zirconium oxide film and a SiO2+metallic oxide film.8. A window glass according to claim 7, wherein the precoat film is made of a SiO2+metallic oxide film and the metallic oxide is selected from the group consisting of P2O5, B2O3, ZrO2, TiO2 and Ta2O5.9. A window glass according to claim 7, wherein the precoat film is made of a SiO2+metallic oxide film in which approximately 5% by weight of P2O5 is added to SiO2.10. A window glass according to claim 5, wherein the precoat film is made of SiO2.