초록 ▼

The present invention relates to a method for making an open celled microcellular foam comprising providing at least one foamable polymer and a crosslinking agent in an extruder, injecting at least one blowing agent into said at least one foamable polymer and said crosslinking agent in said extruder

The present invention relates to a method for making an open celled microcellular foam comprising providing at least one foamable polymer and a crosslinking agent in an extruder, injecting at least one blowing agent into said at least one foamable polymer and said crosslinking agent in said extruder, blending said blowing agent injected into said at least one foamable polymer and said crosslinking agent in said extruder, feeding said blended blowing agent, at least one foamable polymer and said crosslinking agent in said extruder to a die, and depressurizing said blended blowing agent, said at least one foamable polymer and said crosslinking agent.

대표청구항 ▼

1. A method for making an open celled microcellular foam comprising providing at least one foamable polymer, an immiscible thermoplastic polymer and a crosslinking agent in an extruder, injecting at least one blowing agent into said at least one foamable polymer, said immiscible thermoplastic polyme

1. A method for making an open celled microcellular foam comprising providing at least one foamable polymer, an immiscible thermoplastic polymer and a crosslinking agent in an extruder, injecting at least one blowing agent into said at least one foamable polymer, said immiscible thermoplastic polymer and said crosslinking agent in said extruder, blending said blowing agent injected into said at least one foamable polymer, said immiscible thermoplastic polymer and said crosslinking agent in said extruder, feeding said blended blowing agent, at least one foamable polymer, said immiscible thermoplastic polymer and said crosslinking agent in said extruder to a die, and depressurizing said blended blowing agent, said at least one foamable polymer, said immiscible thermoplastic polymer and said crosslinking agent, wherein said foamable polymer comprises a thermoplastic foamable polymer.2. The method of claim 1 wherein said thermoplastic foamable polymer comprises at least one member selected from the group consisting of polyolefins, polyester, polystyrenes, acrylics, poly(vinyl alcohol) or polyamides or copolymers thereof.3. The method of claim 1 wherein said thermoplastic foamable polymer comprises polyethylene or polypropylene.4. The method of claim 1 wherein said extruder is under pressures greater than the solubility pressure of said blowing agent after injecting said blowing agent into said at least one foamable polymer and said crosslinking agent.5. The method of claim 4 wherein the temperature in said extruder is greater than the melting point or glass transition temperature of said foamable polymer.6. The method of claim 1 wherein said extruder and said die are under pressures greater than the solubility pressure of said blowing agent after injecting said blowing agent into said at least one foamable polymer and said crosslinking agent and downstream process equipment.7. The method of claim 6 wherein the temperature in said extruder is greater than the melting point or glass transition temperature of said foamable polymer.8. The method of claim 1 wherein said blowing agent comprises a physical blowing agent.9. The method of claim 8 wherein said blowing agent comprises a gas.10. The method of claim 9 wherein said gas comprises CO2 or normal or isobutane.11. The method of claim 1 wherein said open celled microcellular foam comprises open cells less than 50 microns in average diameter.12. The method of claim 1 wherein said open celled microcellular foam comprises open cells from 10 to 50 microns in average diameter.13. The method of claim 1 wherein said open celled microcellular foam comprises more than 80% open cells by volume.14. The method of claim 1 wherein said open celled microcellular foam comprises from 60% to 90% open cells by volume.15. The method of claim 1 wherein said crosslinker comprises a peroxide or an epoxide.16. The method of claim 1 wherein said crosslinker comprises from 0.01 to 10% by weight of said thermoplastic foamable polymer.17. The method of claim 1 further comprising passing said at least one foamable polymer and said blowing agent in said extruder through a cooling device.18. The method of claim 17 wherein said cooling device is at a temperature below the melting point or glass transition temperature of said foamable polymer.19. The method of claim 1 wherein said immiscible thermoplastic polymer comprises polystyrene.