초록 ▼

A thermoplastic resin composition containing an oxygen-absorbing agent, wherein a resin matrix of the thermoplastic resin composition is substantially non-compatible and is composed of a blend of thermoplastic resins or elastomers, and the non-compatible thermoplastic resins and elastomers are prese

A thermoplastic resin composition containing an oxygen-absorbing agent, wherein a resin matrix of the thermoplastic resin composition is substantially non-compatible and is composed of a blend of thermoplastic resins or elastomers, and the non-compatible thermoplastic resins and elastomers are present as a non-uniformly distributed structure in the resin matrix. The packaging container or cap of this invention suppresses the lowering of flavor retention incident to the dissolving out of the oxygen absorbing agent or its oxidation product even after retorting sterilization. The preservability of the contents and flavor retention can be achieved for a long period of time. According to a preferred embodiment, the oxygen absorbing speed can be increased. After storage for a long time, or after heat sterilization, a rugged state does not occur. There can be formed the oxygen-absorbing resin composition and the packaging container having excellent outer appearance.

대표청구항 ▼

1. A thermoplastic resin composition comprising a blend of a plurality of thermoplastic resins and/or elastomers, and oxygen absorbing agent particles dispersed in the thermoplastic resins and/or the elastomers, wherein:the plurality of the thermoplastics resins and/or the elastomers are incompatibl

1. A thermoplastic resin composition comprising a blend of a plurality of thermoplastic resins and/or elastomers, and oxygen absorbing agent particles dispersed in the thermoplastic resins and/or the elastomers, wherein:the plurality of the thermoplastics resins and/or the elastomers are incompatible with each other; and the oxygen absorbing agent particles comprise a reducing iron powder and a layer of an oxidation promoter or a catalyst which sticks to the surface of the iron powder, the oxygen absorbent agent particles having an average particle diameter of 10 to 50 μm as measured by a laser scattering method, and having a flat or spindle-like shape; and wherein the oxygen absorbing agent particles have an aspect ratio (short axis/long axis) of 6.0 or below, which are being present in an amount of at least 50%, and have a compression degree of at least 20%. 2. An oxygen-absorbing resin composition according to claim 1, wherein either the incompatible thermoplastic resins and/or the elastomers are propylene polymers (A) and the other ones are ethylene polymers (B), the blend thereof having a weight ration (A:B) of from 100:1 to 1:1.3. An oxygen-absorbing resin composition according to claim 1 wherein the oxygen absorbing agent is contained in an amount of 1 to 200% by weight based on the blend.4. An oxygen-absorbing resin composition according to claim 1, wherein the oxygen absorbing agent particles have the oxidation promoter or the catalyst which is present in an amount of 0.1 to 5% by weight of the reducing iron powder, and have a specific surface area of at least 0.5 m2/g and an apparent density of not larger than 2.2 g/cc.5. An oxygen-absorbing resin composition according to claim 1 wherein the oxygen absorbing agent particle is obtained by dry milling a reducing iron powder and a powder of an oxidation promotor or a catalyst.6. An oxygen-absorbing resin composition obtained by blending 1 to 200 parts by weight of an oxygen-absorbing agent into 100 parts by weight of a thermoplastic resin, the oxygen-absorbing agent comprising oxygen-absorbing agent particles which comprise a reducing iron powder and an oxidation-promoting agent or a catalyst firmly adhered to surfaces of said reducing iron powder, and which has a specific surface area of not smaller the 9.5 m2/g and an apparent density of not larger than 2.2 g/cc, and in which the oxidation-promoting agent or the catalyst is present in an amount of from 0.1 to 5% by weight per the reducing iron powder, wherein the oxygen absorbing agent particles have an average particle diameter of 10 to 50 μm as measured by a laser scattering method and an aspect ratio (short axis/long axis size) of 0.6 or below being present in an amount of at least 50 % and is a flat or spindle-shaped particle having a compression degree of at least 20%.7. An oxygen-absorbing multilayer plastic container molded from a laminated body obtained by laminating a thermoplastic resin layer having no oxygen absorbing agent compounded on both sides of a layer composed of the oxygen-absorbing resin composition according to claim 1.8. An oxygen-absorbing multilayer plastic cap which is molded from a laminated body obtained by laminating a thermoplastic resin containing no oxygen-absorbing agent on both sides of a layer composed of the oxygen-absorbing resin composition described in claim 1.9. A liner material for caps which contains a layer composed of the oxygen-absorbing resin composition according to claim 1.