초록 ▼

An alginate gel adsorbent to remove heavy metal ions according to the present invention is prepared by adding dropwisely 0.1-5 wt % alginate solution to a polyvalent cationic solution thereby cross-linking alginic acid with polyvalent cations. An alginate gel adsorbent containing activated carbon ca

An alginate gel adsorbent to remove heavy metal ions according to the present invention is prepared by adding dropwisely 0.1-5 wt % alginate solution to a polyvalent cationic solution thereby cross-linking alginic acid with polyvalent cations. An alginate gel adsorbent containing activated carbon capable of simultaneously removing heavy metal ions and organotoxic materials, that is, activated carbon/alginate gel adsorbent, is prepared by adding dropwisely a mixed solution of 0.17-10 wt % of alginate and 0.1-10 wt % of activated carbon powder to a polyvalent cationic solution thereby cross-linking alginic acid with polyvalent cations in order to immobilize polyvalent cation to alginic acid containing activated carbon. The polyvalent cationic solution is selected from the group consisting of calcium chloride (CaCl2), strontium chloride (SrCl2), barium chloride (BaCl2) and aluminium chloride (AlCl3). A flat board or a thin membrane coated alginate gel adsorbent can be prepared by coating alginate gels onto a supporter such as paper, wood plate and textile fabrics. The alginate gel adsorbent for water purification can be applied to a water purifier as well as a process of wastewater treatment. The alginate gel coated onto a supporter is prepared by immersing a supporter in 0.05-5 wt % alginate solution so that the supporter may uniformly adsorb the alginate solution, immersing the supporter in a polyvalent cationic solution thereby forming alginate gel on the surface of the supporter, and drying the supporter formed with alginate gel thereon.

대표청구항 ▼

What is claimed is: 1. A method of treating water for removal of heavy metals, which comprises contacting heavy metal contaminated water with an activated carbon/alginate gel adsorbent prepared by a process comprising adding dropwisely a mixed solution of 0. 1-10 wt % alginate and 0.1-10 wt % acti

What is claimed is: 1. A method of treating water for removal of heavy metals, which comprises contacting heavy metal contaminated water with an activated carbon/alginate gel adsorbent prepared by a process comprising adding dropwisely a mixed solution of 0. 1-10 wt % alginate and 0.1-10 wt % activated carbon powder to a polyvalent cationic solution to form an activated carbon/alginate gel adsorbent, thereby cross-linking alginic acid with polyvalent cations, drying the activated carbon/alginate gel adsorbent, and applying a coating to the activated carbon/alginate gel adsorbent to prevent the effluence of activated carbon dust and increase adsorption capability of heavy metal ions, said coating application comprising immersing the dried activated carbon/alginate gel adsorbent in an alginate solution of 0.05-5 wt % alginate, and immersing the activated carbon/alginate gel adsorbent in a polyvalent cationic solution. 2. The method of treating water for removal of heavy metals of claim 1 wherein said alginate is an alginic acid salt. 3. The method of treating water for removal of heavy metals of claim 1 wherein said polyvalent cationic solution is selected from the group consisting of calcium chloride (CaCl2), strontium chloride (SrCl2), barium chloride (BaCl2) and aluminum chloride (AlCl3). 4. The method of treating water for removal of heavy metals of claim 1 wherein said alginate contains a powder selected from the group consisting of starch, wooden powder and mud powder. 5. The method of treating water for removal of heavy metals of claim 1 wherein the heavy metal contaminated water contains organochemical materials and wherein said mixed solution contains an adsorbent for adsorbing organochemical materials. 6. A method of treating water for purification in a water purifier, which comprises passing heavy metal contaminated water through a water purifier containing an activated carbon/alginate gel adsorbent prepared by a process comprising adding dropwisely a mixed solution of 0. 1-10 wt % alginate and 0.1-10 wt % activated carbon powder to a polyvalent cationic solution to form an activated carbon/alginate gel adsorbent, thereby cross-linking alginic acid with polyvalent cations, drying the activated carbon/alginate gel adsorbent and applying a coating to the dried activated carbon/alginate gel adsorbent to prevent the effluence of activated carbon dust and increase adsorption capability of heavy metal ions, said coating application comprising immersing the dried activated carbon/alginate gel adsorbent in an alginate solution of 0.05-5 wt % alginate, and immersing the activated carbon/alginate gel adsorbent in a polyvalent cationic solution. 7. The method of treating water for purification in a water purifier of claim 6 wherein said alginate is an alginic acid salt. 8. The method of treating water for purification in a water purifier of claim 6 wherein said polyvalent cationic solution is selected from the group consisting of calcium chloride (CaCl2), strontium chloride (SrCl2), barium chloride (BaCl2) and aluminum chloride (AlCl3). 9. The method of treating water for purification in a water purifier of claim 6 wherein said alginate contains a powder selected from the group consisting of starch, wooden powder and mud powder. 10. The method of treating water for purification in a water purifier of claim 6 wherein the contaminated water contains organochemical materials and wherein said mixed solution contains an adsorbent for adsorbing organochemical materials.